Light-weight delicate-fragrant environment-friendly wood-plastic composite material

A kind of wood-plastic composite material and Youxiang technology, which is applied in the field of wood-plastic material production, can solve the problems of small space for users to choose, single variety of plastic-wood materials, and unsatisfactory performance, and achieve the effect of no cracking and deformation and good strength

Inactive Publication Date: 2017-02-01
安徽浩峯塑业有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

The inventive wooden plastic composition described in this patented technology allows for continuous release of tiny perfume from it that lasts up until now or even longer without losing its effectiveness over time due to damage caused during use. It also provides strong properties such as durability against moisture exposing, corrosivity, weather conditions, etc., while being resistant to mold growth on walls like ceramic tiles.

Problems solved by technology

This patents discuss how common types of building materials like concrete can have issues related to its quality and usability when exposed to certain environments over time due to factors like moisture damage from rainwater, degradation caused through sunlight exposures during winter months, rustiness caused by salt sprayers on roads, snow accumulation causing slipper marks on roadways, dirt buildup on car tire surfaces, and poor indoor air circulations around buildings. These challengings require improvements in these areas while maintaining good appearance characteristics throughout long periods of usage under harsh conditions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A light-weight and fragrant environmental-friendly wood-plastic composite material, including the following components by weight: polyethylene 40kg, straw 35kg, polyethylene 5kg, polyphenylene ether 3.5kg, benzoin 2kg, mica powder 4kg, zinc borate 2kg, 5.5kg of asbestos, 5kg of walnut shell powder, 8kg of bamboo powder, 6kg of ginkgo leaf, 6kg of alder wood powder, 0.1kg of agarwood powder, 4kg of 3-hydroxybenzoic acid, 1 lauryl sulfate ㎏, plant saponin 4kg, terpineol 0.1kg, white latex 1kg.

[0018] Its preparation method comprises the following steps:

[0019] (1) Add polyethylene 40kg, straw 35kg, polyethylene 5kg, polyphenylene ether 3.5kg, benzoin 2kg, mica powder 4kg, zinc borate 2kg, asbestos 5.5kg, walnut shell powder 5kg, bamboo Powder 8kg, Ginkgo biloba leaf 6kg, Alder wood powder 6kg, Agarwood powder 0.1kg, 3-hydroxybenzoic acid 4kg, lauryl sulfate 1kg, plant saponin 4kg, terpineol 0.1kg 1. Add 1kg of white latex to the high-speed mixer and mix well;

[00...

Embodiment 2

[0023] A light-weight and fragrant environmental-friendly wood-plastic composite material, including the following components by weight: polyethylene 65kg, straw 45kg, polyethylene 8kg, polyphenylene ether 4.5kg, benzoin 3kg, mica powder 6kg, zinc borate 2.5kg, 7.5kg of asbestos, 7kg of walnut shell powder, 10kg of bamboo powder, 8kg of ginkgo leaf, 8kg of arboria vulgaris powder, 0.2kg of agarwood powder, 6kg of 3-hydroxybenzoic acid, 2 lauryl sulfate ㎏, plant saponin 6kg, terpineol 0.2kg, white latex 3kg.

[0024] Its preparation method comprises the following steps:

[0025] (1) Add polyethylene 65kg, straw 45kg, polyethylene 8kg, polyphenylene ether 4.5kg, benzoin 3kg, mica powder 6kg, zinc borate 2.5kg, asbestos 7.5kg, walnut shell powder 7kg, bamboo 10kg of powder, 8kg of ginkgo leaves, 8kg of alder wood powder, 0.2kg of agarwood powder, 6kg of 3-hydroxybenzoic acid, 2kg of lauryl alcohol sulfate, 6kg of plant saponin, 0.2kg of terpineol Add 3 kg of white latex to a hi...

Embodiment 3

[0029] A light-weight and fragrant environmental-friendly wood-plastic composite material, including the following components by weight: polyethylene 50kg, straw 40kg, polyethylene 6kg, polyphenylene ether 4kg, benzoin 3kg, mica powder 5kg, zinc borate 2kg, 6kg of asbestos, 6kg of walnut shell powder, 9kg of bamboo powder, 6kg of ginkgo leaf, 6kg of arboria vulgaris powder, 0.1kg of agarwood powder, 6kg of 3-hydroxybenzoic acid, 1 lauryl sulfate ㎏, plant saponin 6kg, terpineol 0.2kg, white latex 1kg.

[0030] Its preparation method comprises the following steps:

[0031] (1) Add polyethylene 50kg, straw 40kg, polyethylene 6kg, polyphenylene ether 4kg, benzoin 3kg, mica powder 5kg, zinc borate 2kg, asbestos 6kg, walnut shell powder 6kg, bamboo Powder 9kg, Ginkgo biloba leaf 6kg, Alder wood powder 6kg, Agarwood powder 0.1kg, 3-hydroxybenzoic acid 6kg, lauryl sulfate 1kg, plant saponin 6kg, terpineol 0.2kg 1. Add 1kg of white latex to the high-speed mixer and mix well;

[0032...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a light-weight delicate-fragrant environment-friendly wood-plastic composite material, which includes, by weight, 40-65 parts of polyethylene, 35-45 parts of straw, 5-8 parts of polyethylene, 3.5-4.5 parts of polyphenyl ether, 2-3 parts of benzoin, 4-6 parts of mica powder, 2.0-2.5 parts of zinc borate, 5.5-7.5 parts of asbestos, 5-7 parts of walnut shell powder, 8-10 parts of bamboo powder, 6-8 parts of folium ginkgo, 6-8 parts of powder of aralia echinocaulis, 0.1-0.2 parts of agalloch powder, 4-6 parts of 3-hydroxybenzoic acid, 1-2 parts of lauryl sulfate, 4-6 parts of plant saponin, 0.1-0.2 parts of terpilenol and 1-3 parts of white latex. The wood plastic composite material can release a delicate fragrance continuously, has high strength and has water-proof, anti-corrosion and mildew-proof performances, can be used both indoor and outdoor, has the anti-aging effect and is free of cracking and deformation.

Description

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Owner 安徽浩峯塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com