A kind of grain-oriented silicon steel and its preparation method

A technology of grain-oriented silicon steel and steel coil, applied in the field of grain-oriented silicon steel and its preparation, can solve the problem of lack of mass production, and achieve the effect of ensuring electromagnetic performance and improving suppression ability

Active Publication Date: 2018-12-28
MAANSHAN IRON & STEEL CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the essential difference between the physical and metallurgical characteristics of the thin slab process and the traditional grain-oriented silicon steel production process, the country does not yet have the capacity for mass production, and a large number of researches are still in the technical research stage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of grain-oriented silicon steel and its preparation method
  • A kind of grain-oriented silicon steel and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The preparation process steps of grain-oriented silicon steel are as follows:

[0038] 1) Continuous casting of molten iron pretreatment, converter steelmaking, and vacuum treatment into 230mm billets;

[0039] 2) Heating the billet to 1250°C for 280 minutes in the furnace, of which the effective holding time at 1250°C is 85 minutes;

[0040] 3) The cast slab is subjected to rough rolling for 3 passes, the thickness of the intermediate slab is 35mm, the starting temperature of the finishing rolling is controlled at 1080°C, the finishing rolling temperature is 950°C, the coiling temperature is 560°C, and the thickness after finishing rolling is 2.3mm;

[0041] 4) After the hot-rolled raw material is pickled, it is cold-rolled for the first time, with a thickness of 0.66mm;

[0042] 5) Decarburization annealing is performed on the primary cold-rolled coil, the decarburization annealing temperature is 830°C, the dew point is 35°C, the decarburization soaking time is 6min,...

Embodiment 2

[0049] The preparation process steps of grain-oriented silicon steel are as follows:

[0050] 1) The steel with the above chemical composition is continuously cast into a 250mm billet after molten iron pretreatment, converter steelmaking, and vacuum treatment;

[0051] 2) Heating the billet to 1280°C for 370 minutes in the furnace, of which the effective holding time at 1280°C is 110 minutes;

[0052] 3) The cast slab is subjected to 5 passes of rough rolling, the thickness of the intermediate slab is 45mm, the start rolling temperature of finish rolling is controlled at 1110°C, the finish rolling temperature is 980°C, the coiling temperature is 550°C, and the thickness after finish rolling is 2.3mm;

[0053] 4) After the hot-rolled raw material is pickled, it is cold-rolled for the first time, with a thickness of 0.70mm;

[0054] 5) Decarburization annealing is performed on the primary cold-rolled coil, the decarburization annealing temperature is 820°C, the dew point is 40°...

Embodiment 3

[0061] The preparation process steps of grain-oriented silicon steel are as follows:

[0062] 1) The steel with the above chemical composition is continuously cast into a 230mm billet after molten iron pretreatment, converter steelmaking, and vacuum treatment;

[0063] 2) Heating the billet to 1300°C for 410 minutes in the furnace, of which the effective holding time at 1300°C is 125 minutes;

[0064] 3) The cast slab is subjected to rough rolling for 3 passes, the thickness of the intermediate slab is 35mm, the starting temperature of the finish rolling is controlled at 1150°C, the finish rolling temperature is 980°C, the coiling temperature is 550°C, and the thickness after finish rolling is 2.0mm;

[0065] 4) After the hot-rolled raw material is pickled, it is cold-rolled for the first time, with a thickness of 0.63mm;

[0066] 5) Decarburization annealing is performed on the primary cold-rolled coil, the decarburization annealing temperature is 830°C, the dew point is 40°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to oriented silicon steel and a preparing method thereof. The oriented silicon steel comprises, by weight, 0.030%-0.070% of C, 2.8%-3.5% of Si, 0.15%-0.30% of Mn, 0.35%-0.80% of Cu, 0.0040%-0.015% of S, 0.015%-0.025% of Als, 0.070%-0.015% of N, smaller than or equal to 0.020% of P, 0.002%-0.02% of Ti, and the balance Fe and inevitable impurities, wherein C / Ti is smaller than or equal to 10, and Cu / S is larger than or equal to 50. The preparing method comprises the steps of converter smelting, vacuum treatment, continuous casting, soaking pit heating, hot continuous rolling, first-time cold rolling, decarburization annealing, second-time cold rolling, MgO parting agent coating, high-temperature annealing and rewinding, the iron loss P1.7 of the oriented silicon steel is smaller than 1.18 W / kg, and the magnetic inductance B8 of the oriented silicon steel is larger than or equal to 1.86 T.

Description

technical field [0001] The invention belongs to the technical field of iron and steel manufacturing, and in particular relates to an oriented silicon steel and a preparation method thereof. Background technique [0002] In the production process of grain-oriented silicon steel, in order to produce a secondary recrystallization structure with accurate orientation, it is necessary to obtain fine and dispersed inhibitor particles before the final high temperature annealing. In order to obtain dispersed second-phase particles, it must be Using a very high heating temperature and a long heating time, the coarse second phase particles are fully dissolved, and then precipitated during the cold rolling process. High-temperature heating will bring huge risks to heating equipment, and will also cause a series of problems such as increased energy consumption, loss of yield, and reduced output. Therefore, in recent years, the use of second heating and enhanced inhibitor development cap...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/16C22C38/06C22C38/14C21D8/02
CPCC21D8/0226C21D8/0236C21D8/0257C22C38/001C22C38/02C22C38/04C22C38/06C22C38/14C22C38/16
Inventor 裴英豪王立涛施立发裴陈新夏雪兰张振海
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap