An ink and external oil technology, applied in inks, household appliances, applications, etc., can solve the problems of short preservation life of handwriting, slow drying speed, poor gloss, etc., to achieve good solubility, improve drying speed, and prevent colony erosion.
Inactive Publication Date: 2017-03-22
CHONGQING IND POLYTECHNIC COLLEGE
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, the existing ink has poor gloss, insufficient brightness, and slow drying speed. After writing, it needs to be air-
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0017] Example 1: 30 parts of activated carbon black, 25 parts of colloidal calcium carbonate, 3 parts of tetrafluoroisoindolinone, 30 parts of connecting material, 3 parts of linolenic acid oil, 2-6-di-tert-butyl-4-methyl 3 parts of phenol, 1 part of tributyl phosphate, 3 parts of gum arabic, 4 parts of No. 101 outer oil, 2 parts of UV-531.
Embodiment 2
[0018] Example 2: 37 parts of activated carbon black, 30 parts of colloidal calcium carbonate, 1 part of tetrafluoroisoindolinone, 35 parts of connecting material, 4 parts of linolenic acid oil, 2-6-di-tert-butyl-4-methyl 2 parts of phenol, 2 parts of tributyl phosphate, 4 parts of gum arabic, 1 part of No. 101 outer oil, 3 parts of UV-531.
Embodiment 3
[0019] Example 3: 45 parts of activated carbon black, 20 parts of colloidal calcium carbonate, 2 parts of tetrafluoroisoindolinone, 40 parts of connecting material, 1 part of linolenic acid oil, 2-6-di-tert-butyl-4-methyl 2.5 parts of phenol, 3 parts of tributyl phosphate, 2 parts of gum arabic, 2 parts of No. 101 outer oil, 4 parts of UV-531.
[0020] Concretely, the connecting material of the present invention is made up of following examples weight parts raw material:
[0021] Example 1: 30 parts of rosin modified p-tertiaryl phenol resin, 12 parts of catalpa oil, 14 parts of tung oil, 5 parts of long oil alkyd resin, 27 parts of ink oil (distillation range 270-290°C), 10 parts of linseed oil 2 parts, polyethylene wax 2 parts, nitrocellulose 2 parts, cobalt naphthenate 0.5 parts.
[0022] Example 2: 33 parts of rosin modified p-tertiaryl phenol resin, 15 parts of catalpa oil, 10 parts of tung oil, 6 parts of long oil alkyd resin, 30 parts of ink oil (distillation range 270...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
Printing ink for pens is composed of the following raw materials (by weight): 30-45 parts of activated carbon black, 20-30 parts of calcene, 1-3 parts of tetrafluoro isoindolinone, 30-40 parts of a binder, 1-4 parts of linolenic acid oil, 2-3 parts of 2-6-ditert-butyl-4-methylphenol, 1-3 parts of tributyl phosphate, 2-4 parts of Arabic gum, 1-4 parts of No. 101 gasoline and 2-4 parts of UV-531. The binder is composed of the following raw materials (by weight): 30-35 parts of rosin-modified p-tert-butylphenol resin, 10-15 parts of stillingia oil, 10-14 parts of tung oil, 5-8 parts of long oil alkyd resin, 25-30 parts of oil for printing ink (distillation range 270-290 DEG C), 6-10 parts of linseed oil, 2-5 parts of polyethylene wax, 1-3 parts of nitrocellulose and 0.2-0.5 part of cobalt naphtenate. In the prepared printing ink for pens, the resin in the binder is completely soluble in the oil for printing ink, and resin has good dissolvability in a solvent.
Description
technical field [0001] The invention belongs to the field of ink, in particular to a pen ink. Background technique [0002] Pen ink is the most common kind of ink in daily life, and it is usually filled in the refills of ballpoint pens and carbon pens. At present, the existing ink has poor gloss, insufficient brightness, and slow drying speed. After writing, it needs to be air-dried for a certain period of time. The preservation life of the writing is short, and the writing will fade after a long time. Contents of the invention [0003] The invention provides a pen ink to solve the defects in the prior art. [0004] The present invention is achieved through the following technical solutions: [0005] A pen ink is composed of the following raw materials in parts by weight: 30-45 parts of activated carbon black, 20-30 parts of colloidal calcium carbonate, 1-3 parts of tetrafluoroisoindolinone, 30-40 parts of binder, linolenic acid 1-4 parts of oil, 2-3 parts of 2-6-di-ter...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more