High-pressure-resistance abrasion-resistance dustproof capsule and preparation method thereof

A preparation process and high-pressure-resistant technology, applied in the field of high-pressure-resistant, anti-wear and dust-proof capsules and their preparation technology, can solve the problems of poor wear resistance, poor volume expansion deformation, poor heat-resistant air performance, etc., and achieve suitable hardness. , Low cross-linking density, and the effect of improving wear resistance

Active Publication Date: 2017-04-26
南阳天一密封股份有限公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the patented capsule has poor heat-resistant air performance, poor wear resistance, and poor volume expansion and deformation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-pressure-resistance abrasion-resistance dustproof capsule and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A high-pressure, wear-resistant and dust-proof capsule is made of the following raw materials in parts by weight: 85 parts of hydrogenated nitrile rubber, 15 parts of chlorinated butyl rubber, 5 parts of natural rubber, 5 parts of zinc oxide, 1 part of magnesium oxide, 1 part of stearic acid, 0.5 parts of paraffin, 30 parts of N330 carbon black, 10 parts of N770 carbon black, 10 parts of white carbon black, 3 parts of solid coumarone resin, 1 part of binder A, 2 parts of binder RS, 1 part of accelerator NOBS, 1 part of accelerator TMTD, 1 part of accelerator CZ, 1 part of sulfur, 1 part of vulcanizing agent DCP (dicumyl peroxide), 1 part of co-vulcanizing agent HVA2 (m-phenylene bismaleimide) 1 part, plasticizer TP759 5 parts, internal release agent 18D 1 part and anti-aging agent 3 parts.

[0027] Described anti-aging agent is anti-aging agent 4010NA.

[0028] The preparation process of the above-mentioned high-pressure-resistant, wear-resistant and dust-proof capsule...

Embodiment 2

[0037] A high-pressure resistant, wear-resistant and dust-proof capsule is made of the following raw materials in parts by weight: 86 parts of hydrogenated nitrile rubber, 16 parts of chlorinated butyl rubber, 6 parts of natural rubber, 6 parts of zinc oxide, 2 parts of magnesium oxide, 1.5 parts of stearic acid, 0.6 parts of paraffin, 32 parts of N330 carbon black, 8 parts of N770 carbon black, 11 parts of white carbon black, 4 parts of solid coumarone resin, 1.5 parts of binder A, 3 parts of binder RS, Accelerator NOBS 2 parts, accelerator TMTD 2 parts, accelerator CZ 3 parts, sulfur 2 parts, vulcanizing agent DCP (dicumyl peroxide) 2 parts, co-vulcanizing agent HVA2 (m-phenylene bismaleimide ) 2 parts, 6 parts of TP759, 1 part of internal release agent 18D and 4 parts of anti-aging agent.

[0038] The anti-aging agent is anti-aging agent MB.

[0039] The preparation process of the above-mentioned high-pressure-resistant, wear-resistant and dust-proof capsule includes the f...

Embodiment 3

[0048] A high-pressure, wear-resistant and dust-proof capsule is made of the following raw materials in parts by weight: 87 parts of hydrogenated nitrile rubber, 17 parts of chlorinated butyl rubber, 7 parts of natural rubber, 7 parts of zinc oxide, 1 part of magnesium oxide, 2 parts of stearic acid, 0.7 parts of paraffin, 35 parts of N330 carbon black, 5 parts of N770 carbon black, 12 parts of white carbon black, 5 parts of solid coumarone resin, 2 parts of binder A, 2.5 parts of binder RS, 3 parts of accelerator NOBS, 2.5 parts of accelerator TMTD, 2 parts of accelerator CZ, 3 parts of sulfur, 3 parts of vulcanizing agent DCP, 2 parts of co-curing agent HVA2, 7 parts of TP759, 1.5 parts of internal release agent 18D and 4.5 parts of anti-aging agent share.

[0049] The anti-aging agent is a mixture of anti-aging agent 4010NA, anti-aging agent MB and anti-aging agent 445, and the weight ratio of the three is 1:1:1.

[0050] The preparation process of the above-mentioned high...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-pressure-resistance abrasion-resistance dustproof capsule and a preparation process thereof. The dustproof capsule is prepared from the following raw materials in parts by weight: 85-90 parts of hydrogenated butadiene-acrylonitrile rubber, 15-20 parts of chlorinated butyl rubber, 5-10 parts of natural rubber, 5-10 parts of zinc oxide, 1-2 parts of magnesium oxide, 1-2 parts of stearic acid, 0.5-1 part of paraffin, 30-40 parts of N330 carbon black, 5-15 parts of N770 carbon black, 10-15 parts of white carbon black, 3-5 parts of solid coumarone resin, 1-2 parts of adhesive A, 2-3 parts of adhesive RS, 1-3 parts of accelerant NOBS, 1-3 parts of accelerant TMTD, 1-3 parts of accelerant CZ, 1-3 parts of sulfur, 1-3 parts of a vulcanizing agent, 1-2 parts of a co-curing agent HVA, 5-10 parts of TP759, 1-2 parts of an internal releasing agent and 3-5 parts of an antiaging agent. The dustproof capsule has the advantages of high pressure resistance and abrasion resistance.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a high-pressure-resistant, wear-resistant and dust-proof capsule and a preparation process thereof. Background technique [0002] In the process of steelmaking in steel mills, a large amount of useless dust is generated. Under the reality of increasingly serious environmental protection requirements, dust treatment is particularly important. The rubber capsule is inflated and pumped in the pipeline to make it expand and close to control the dust recovery. Due to the softness and expandability of the rubber capsule, it fits and tightens well with the pipeline, so that it expands and seals tightly. It will cause dust leakage. When it is tightened, the pipeline will be unblocked and the dust can pass through quickly. [0003] Chinese patent CN105837963A discloses a butyl rubber composite material used in vulcanization bladders, which is composed of butyl rubbe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L15/00C08L23/28C08L7/00C08L91/06C08K13/02C08K3/04C08K3/36C08K5/14C08K5/3415B29B7/74B29C35/02
CPCB29B7/002B29B7/7461B29C35/02C08K2201/014C08L15/005C08L2201/08C08L2205/035C08L2312/00C08L23/283C08L7/00C08L91/06C08K13/02C08K3/04C08K3/36C08K5/14C08K5/3415
Inventor 樊红星赵红祥刘元英杨松涛陈宇翔朱建周张冰潭
Owner 南阳天一密封股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com