A production process for processing waste leather into suede leather with a silky feel
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A production process and leather technology, which is applied in the field of suede leather production, can solve the problems of insufficient fineness of two-layer sheepskin leather, the inability to use surface materials, and low economic benefits of leather materials, etc., and achieve good waterproof effect, Safe to use, good emulsifying effect
Active Publication Date: 2019-11-26
DONGGUAN TIANYI LEATHER TECH CO LTD
View PDF7 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] Due to the insufficient fineness and poor glossiness of the existing discarded two-layer sheepskin leather, it can only be used to make the inner lining of the leather material, and cannot be used as the surface layer material of the product. The application range is limited, and the obtained leather material The economic benefit is not high
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0058] A production process for processing waste leather into suede leather with a silky feel, comprising the following steps:
[0059] (1) Material selection: use the second-layer sheepskin leather that is discarded after being peeled and discarded as the skin embryo;
[0060] (2) Lamination: Lay a layer of fabric on the bottom of the leather;
[0061] (3) Spraying: Spray a layer of silk-like feel agent on the surface of the leather;
[0062] (4) Film application: A layer of nano-film is pasted on the surface of the leather embryo by transfer printing to obtain suede leather.
[0063] In the step (2), the cloth is cotton cloth.
[0064] In the step (3), the hand feeling agent is composed of the following raw materials in weight percentage:
[0065] Oxidized polyethylene wax 10%
[0066] Emulsifier 5%
[0067] Modified polysiloxane 0.5%
[0068] 60 ℃ demineralized water balance.
[0069] In the step (4), the nano-membrane is a PET film loaded with nanoparticles with a p...
Embodiment 2
[0083] The difference between this embodiment and above-mentioned embodiment 1 is:
[0084] In the step (2), the cloth is linen.
[0085] In the step (3), the hand feeling agent is composed of the following raw materials in weight percentage:
[0086] Oxidized polyethylene wax 20%
[0087] Emulsifier 10%
[0088] Modified Polysiloxane 1.0%
[0089] 70 ℃ demineralized water balance.
[0090] In the step (4), the nano-membrane is a PET film loaded with nanoparticles with a particle size of 50 nm.
[0091] The nano particles are nano magnesium dioxide, nano titanium dioxide, nano silicon dioxide or nano copper dioxide.
[0092] Described PET film is made of the raw material of following weight part:
[0093] PET resin 100 parts
[0094] 20 parts glass fiber
[0095] Filler 10 parts
[0096] Elasticity modifier 8 parts
[0097] Impact modifier 6 parts
[0098] Flame retardant 6 parts
[0099] 3 parts of coupling agent
[0100] Nucleating agent 2 parts
[0101] Lubric...
Embodiment 3
[0104] The difference between this embodiment and above-mentioned embodiment 1 is:
[0105] In the step (2), the cloth is silk or woolen wool.
[0106] In the step (3), the hand feeling agent is composed of the following raw materials in weight percentage:
[0107] Oxidized polyethylene wax 30%
[0108] Emulsifier 15%
[0109] Modified Polysiloxane 1.5%
[0110] 80 ℃ demineralized water balance.
[0111] In the step (4), the nano-membrane is a PET film loaded with nanoparticles with a particle size of 100 nm.
[0112] The nano particles are nano copper dioxide, nano tin dioxide, nano zinc dioxide, nano diatomite, nano bentonite or nano bauxite.
[0113] Described PET film is made of the raw material of following weight part:
[0114] PET resin 120 parts
[0115] 30 parts glass fiber
[0116] Filler 15 parts
[0117] Elastic modifier 10 parts
[0118] Impact modifier 8 parts
[0119] Flame retardant 8 parts
[0120] 5 parts of coupling agent
[0121] Nucleating age...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
diameter
aaaaa
aaaaa
length
aaaaa
aaaaa
Login to View More
Abstract
The invention relates to the technical field of leather processing, in particular to a production technology for processing a suede leather material with a silk-like hand feeling by using a waste leather material. The production technology comprises the steps of (1) selecting a material, specifically, adopting a split waste two-layer sheepskin leather material as a leather blank; (2) laminating, specifically, laminating a layer of cloth on the bottom surface of the leather material; (3) spraying, specifically, spraying a layer of a hand feeling agent with the silk-like hand feeling on the surface of the leather material; and (4) attaching a film, specifically, attaching a layer of a nano-film on the surface of the leather blank through a transfer printing mode and obtaining the suede leather material. The production technology for processing the suede leather material with the silk-like hand feeling by using the waste leather material has the advantages that the steps are simple, operation and control are convenient, the quality is stable, the production efficiency is high, the raw material is cheap and easy to obtain, the utilization rate of the leather material is high, the production cost is low, and large-scale industrial production can be realized; and the quality of the produced finished leather material is close to that of a top layer leather material, the additional value of the finished leather material is greatly improved, the application range is wide, and the economic benefit is high.
Description
technical field [0001] The invention relates to the technical field of leather processing, in particular to a production process for processing waste leather into suede leather with a silky feel. Background technique [0002] Leather is widely used on the surface of daily necessities, such as tables and chairs, sofas, shoe materials, clothing, etc., to add texture, beauty or durability to daily necessities. Leather can be broadly classified into artificial leather and natural leather. Natural leather refers to taking animal fur and drying, cleaning, softening, dyeing, trimming, cutting and other production processes to form a smooth surface and tough texture. [0003] Due to the insufficient fineness and poor glossiness of the existing discarded two-layer sheepskin leather, it can only be used to make the inner lining of the leather material, and cannot be used as the surface layer material of the product. The application range is limited, and the obtained leather material ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More