Environment-friendly heavy metal repairing agent, application thereof and slow-releasing heavy metal repairing fertilizer
A technology of heavy metal and repairing agent, applied in application, potash fertilizer, organic fertilizer and other directions, can solve the problems of many raw materials, high production cost and low economic benefit, and achieve the effects of simple preparation process, low production cost and good adsorption effect.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0045] The preparation method of the slow-release heavy metal repair fertilizer of the embodiment of the present invention includes the following steps:
[0046] Step 2-1: Prepare the main material particles
[0047] At least one of organic fertilizer, potash fertilizer and boron fertilizer is used as raw materials to prepare granules. When carrying out this step, it can be carried out according to the conventional steps for preparing fertilizer granules, or directly purchased on the market.
[0048] Step 2-2: Preparation of auxiliary materials
[0049] Take the humic acid and the binder of the embodiment of the present invention, wherein the humic acid accounts for 30-35% of the total weight of the auxiliary material, and the binder accounts for 15-20% of the total weight of the auxiliary material. The humic acid and the binder are mixed in a mixer according to the aforementioned weight percentage to prepare a slurry for use.
[0050] Step 2-3: Film formation
[0051] In the embodimen...
Example
[0056] Example 1-1
[0057] After pretreatment, the oyster shells are roasted protectively under the conditions of a roasting temperature of 600℃ and a roasting time of 12 minutes. When feeding, the flow rate of the oyster shells is controlled to 0.2m 3 / min, the rotation speed of the roasting equipment is 25r / min. After roasting, the water content in the oyster shell is 10% (weight percent). The oyster shells were subjected to the first cooling treatment and the second cooling treatment respectively, wherein the natural cooling time of the first cooling treatment was 10 min, and the condition of the second cooling treatment was cooling at a temperature drop rate of 15° C. / min for 15 min. Then, the oyster shells are crushed, and oyster shell powders of different particle sizes are selected by winnowing. Then, oyster shell powders of different sizes are prepared into a heavy metal repair agent, which includes a first-grade powder, a second-grade powder, a third-grade powder and a...
Example
[0058] Example 1-2
[0059] After pretreatment, the oyster shells are roasted protectively at a roasting temperature of 650°C and a roasting time of 10 minutes. When feeding, the flow rate of the oyster shells is controlled to 0.3m 3 / min, the rotating speed of the roasting equipment is 30r / min. After roasting, the water content in the oyster shell is 9.5% (weight percent). The oyster shells were subjected to the first cooling treatment and the second cooling treatment respectively, wherein the natural cooling time of the first cooling treatment was 14 min, and the condition of the second cooling treatment was cooling at a temperature drop rate of 17° C. / min for 11 min. Then, the oyster shells are crushed, and oyster shell powders of different particle sizes are selected by winnowing. Then, oyster shell powders of different sizes are prepared into a heavy metal repair agent, which includes first-level powder, second-level powder, third-level powder and fourth-level powder. The ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap