Experimental method for studying the reaction of fine ore in motion

A test method and powder ore technology, applied in the field of metallurgy, can solve the problems of small temperature difference constant temperature zone, large influence, large temperature difference, etc., to ensure the accuracy and prevent the effect of reaction

Active Publication Date: 2017-06-30
NORTHEASTERN UNIV
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the first two methods cannot avoid the bonding phenomenon of fine ore particles at high temperature, while the tubular dripping furnace method avoids the mutual bonding of molten fine ore particles by flying a small amount of fine ore through the constant temperature zone.
But the application of tube dripping brings another problem at the same time: how to get a constant temperature zone with small temperature difference
The former tube-type dripping furnace has a relatively low temperature and a large temperature difference between the parts above the constant temperature zone and below the constant temperature zone in the furnace, so it has a greater impact on the research results of the isothermal method; although the latter one uses water-cooled feeding tubes and water-cooled +Air-cooled feed pipe prevents fine ore from reacting in the uneven temperature area at both ends of the furnace, but the water-cooled equipment takes away a lot of heat in the furnace, especially due to the high cooling intensity of water-cooled+air-cooled feed pipe, close to The temperature at the upper end of the water-cooled + air-cooled feed pipe is much lower than when the water-cooled + air-cooled feed pipe is not used. Therefore, there is still a very large temperature difference in the constant temperature area in this set of equipment, which has great influence on the accuracy of the experimental results. big impact

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Experimental method for studying the reaction of fine ore in motion
  • Experimental method for studying the reaction of fine ore in motion
  • Experimental method for studying the reaction of fine ore in motion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0141] Taking the 130cm long tubular shaft furnace as an example, the operating temperature of the tubular shaft furnace is 1400°C. The present invention adopts a water-cooled feeding pipe and a feeding pipe protected by an inert gas. The length of the constant temperature zone is set at 50cm. The highest temperature in the zone is 1388°C, the lowest temperature in the constant temperature zone is 1350°C, the temperature in this constant temperature zone is 1369°C, and the error of the temperature in the constant temperature zone is ±19°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to an experimental method for studying the reaction of fine ore in motion. The method comprises the following steps of: S1. adjusting the position of a discharge port of a feed pipe and a collecting port of a collecting pipe in a reactor pipe to obtain the temperature distribution of a number of quasi-constant temperature zones, then according to the experimental requirements, selecting constant temperature zones and the position of the discharge port of the feed pipe and the feed-collecting port of the feed-collecting pipe that the constant temperature zones correspond to; S2. According to the needs, adjusting the position of the discharge port of the feed pipe and / or the feed-collecting port of the feed-collecting pipe in the reactor pipe,so as to set the temperature, length and / or temperature error of the constant temperature zones; and S3. ensuring the fine ore is reacted in the constant temperature zones. The experimental method for studying the reaction of fine ore in motion has the advantages of implementing all reactions of fine ore in the constant temperature zones, and making the temperature difference of the constant temperature zones smaller through adjustment and selection.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, in particular to an experimental method for studying the reaction of fine ore in motion. Background technique [0002] Due to the natural fragility of most iron ores, a large amount of fine ore is often produced during the mining, crushing and screening of iron ore. Therefore, fine ore accounts for a large proportion of the iron ore in the world. Big. In addition, for some low-grade iron ores, in the smelting process, they will also be first made into fine ore. For example, some low-grade iron ores found in China, North America and Russia need to be crushed into fine powder first, and then go through the beneficiation process to obtain concentrate particles with acceptable grade levels. The obtained concentrate particles generally have a size of less than 0.15 mm. [0003] In the traditional ironmaking process, powdered ore needs to be sintered or pelletized to be processed into large-sized...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N15/00
CPCG01N15/00
Inventor 曲迎霞邹宗树邢力勇张立
Owner NORTHEASTERN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products