A silicon carbide nanowire reinforced c/c-sic-zrb 2 Preparation method of ceramic matrix composite material

A silicon carbide nanowire, c-sic-zrb2 technology, applied in the field of materials, achieves good preservation, improved mechanical properties, and simple preparation process

Active Publication Date: 2020-02-14
NORTHWESTERN POLYTECHNICAL UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In order to avoid the deficiencies of the prior art, the present invention proposes a silicon carbide nanowire reinforced C / C-SiC-ZrB 2 A method for preparing ceramic matrix composites, solving the problems of uniform distribution of silicon carbide nanowires inside the composite and improving the mechanics of the composite

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A silicon carbide nanowire reinforced c/c-sic-zrb <sub>2</sub> Preparation method of ceramic matrix composite material
  • A silicon carbide nanowire reinforced c/c-sic-zrb <sub>2</sub> Preparation method of ceramic matrix composite material
  • A silicon carbide nanowire reinforced c/c-sic-zrb <sub>2</sub> Preparation method of ceramic matrix composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Step 1: Put the carbon fiber preform into anhydrous ethanol for ultrasonic cleaning for 20 minutes, and dry the cleaned carbon fiber preform for 10 hours at a temperature of 100°C for use;

[0033]Step 2: Preparation of porous C / C preform, placing the carbon fiber preform in an isothermal chemical vapor deposition furnace, using natural gas as a precursor, and depositing pyrolytic carbon to protect the carbon fiber preform at 1100 ° C, the natural gas flow rate is 80ml / min, The deposition time is 5h; after the deposition is completed, it is cooled in the furnace to obtain a porous C / C preform;

[0034] Step 3: Stir the absolute ethanol and ethyl orthosilicate solution evenly, then add a small amount of distilled water, ferrocene and hydrochloric acid, and stir again to make a silica sol; the absolute ethanol, ethyl orthosilicate, The molar ratio of distilled water, ferrocene and hydrochloric acid is 3:1:5:0.01:0.2;

[0035] Step 4: Immerse the porous C / C preform in the...

Embodiment 2

[0040] Step 1: Put the carbon fiber preform into anhydrous ethanol for ultrasonic cleaning for 20 minutes, and dry the cleaned carbon fiber preform for 10 hours at a temperature of 100°C for use;

[0041] Step 2: Preparation of porous C / C preform, placing the carbon fiber preform in an isothermal chemical vapor deposition furnace, using natural gas as a precursor, and depositing pyrolytic carbon to protect the carbon fiber preform at 1100 ° C, the natural gas flow rate is 80ml / min, The deposition time is 5h; after the deposition is completed, it is cooled in the furnace to obtain a porous C / C preform;

[0042] Step 3: Stir the absolute ethanol and ethyl orthosilicate solution evenly, then add a small amount of distilled water, ferrocene and hydrochloric acid, and stir again to make a silica sol; the absolute ethanol, ethyl orthosilicate, The molar ratio of distilled water, ferrocene and hydrochloric acid is 3:1:5:0.01:0.2;

[0043] Step 4: Immerse the porous C / C preform in th...

Embodiment 3

[0048] Step 1: Put the carbon fiber preform into anhydrous ethanol for ultrasonic cleaning for 20 minutes, and dry the cleaned carbon fiber preform for 10 hours at a temperature of 100°C for use;

[0049] Step 2: Preparation of porous C / C preform, placing the carbon fiber preform in an isothermal chemical vapor deposition furnace, using natural gas as a precursor, and depositing pyrolytic carbon to protect the carbon fiber preform at 1100 ° C, the natural gas flow rate is 80ml / min, The deposition time is 5h; after the deposition is completed, it is cooled in the furnace to obtain a porous C / C preform;

[0050] Step 3: Stir the absolute ethanol and ethyl orthosilicate solution evenly, then add a small amount of distilled water, ferrocene and hydrochloric acid, and stir again to make a silica sol; the absolute ethanol, ethyl orthosilicate, The molar ratio of distilled water, ferrocene and hydrochloric acid is 3:1:5:0.01:0.2;

[0051] Step 4: Immerse the porous C / C preform in th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
bending strengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a silicon carbide nanowire enhanced C / C-SiC-ZrB2 ceramic-based composite material. A pretreated carbon fiber prefabricating body is thermally treated to obtain a silicon carbide nanowire. The silicon carbide nanowire prepared by a sol-gel carbon-thermal reaction method is evenly distributed at the inner part of a porous carbon / carbon composite material. Subsequently, pyrolytic carbon deposited in an isothermal chemical vapor deposition furnace is coated at the surface of the silicon carbide nanowire, thus the dropping, growing and rupture of the silicon carbide nanowire in the following reaction and infiltration processes are effectively avoided. A ceramic-based composite material carbon fiber, a silicon carbide nanowire and a pyrolytic carbon middle layer after reaction and infiltration are not eroded by a high-temperature metal bath and are well preserved; thus the physical performance of the composite material can be improved. Compared with the C / C-SiC-ZrB2 ceramic-based composite material without adding the silicon carbide nanowire, the bending strength and the fracture toughness property of the silicon carbide nanowire enhanced C / C-SiC-ZrB2 ceramic-based composite material are improved by 26.9-41.3% and 45.2-59.1% respectively.

Description

technical field [0001] The invention belongs to the field of materials, and relates to a silicon carbide nanowire reinforced C / C-SiC-ZrB 2 Preparation method of ceramic matrix composite material. Background technique [0002] With the development of new engines and the development of new concept aerospace vehicles, traditional ceramic matrix composite materials have been unable to achieve the required performance indicators. It is urgent to develop new composite materials with higher temperature resistance and longer life to meet the development of aerospace industry. demand. Continuous Carbon Fiber Reinforced C / C-SiC-ZrB 2 In addition to a series of excellent properties such as high temperature resistance, high specific strength, high specific modulus, and low thermal expansion coefficient, composite materials also have the characteristics of high ceramic matrix density, ablation resistance, thermal shock resistance, and good thermochemical stability. A new type of ultra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/80C04B35/83C04B35/622
CPCC04B35/622C04B35/806C04B35/83C04B2235/3813C04B2235/3826C04B2235/5248C04B2235/614C04B2235/9676
Inventor 付前刚刘跃李贺军李克智林红娇王贝贝
Owner NORTHWESTERN POLYTECHNICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap