Casting method for steel-copper composite cylinder body

A casting method and composite cylinder technology, applied in cylinders, liquid chemical plating, coating, etc., can solve problems such as oxidation and substandard composite performance, and achieve improved corrosion resistance, no peeling and bubbling, and good composite performance Effect

Inactive Publication Date: 2017-08-29
安徽恒利增材制造科技有限公司
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a casting method for a steel-copper composite cylinder, to solve the problems of oxidation, substandard composite performance, composite casting tooling design and copper material ratio in the composite process of the steel-copper composite cylinder, and to realize the qualified production of the casting method Steel-copper composite cylinder blank

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Casting method for steel-copper composite cylinder body
  • Casting method for steel-copper composite cylinder body

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The present invention will be described in further detail below in conjunction with the accompanying drawings and embodiments, but the present invention is not limited to these embodiments.

[0034] Depend on Figure 1-2 , a casting method of a steel-copper composite cylinder, comprising the following steps:

[0035] Step 1. Establish a three-dimensional model, calculate the mass of the cast copper metal to be 19.86kg, carry out casting process design and simulation, optimize the casting process, and determine that the initial temperature of the steel base is 1250°C, and the initial casting temperature of the copper metal is 1250°C. The holding time is 9-12min, the casting time is 15s, and the casting speed is 1.5kg / s;

[0036] Step 2: Use cylindrical steel billet as the steel base, and perform heat treatment and annealing process on the steel base: slowly heat to 900°C-1050°C, heat for 15h-20h and then cool to room temperature;

[0037] Step 3: Carry out turning, mil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
heightaaaaaaaaaa
Login to view more

Abstract

The invention discloses a casting method for a steel-copper composite cylinder body. The casting method comprises the steps of performing three-dimensional modeling, designing a casting technology and performing technology simulation and optimization, performing base steel heat treatment, performing machining, tool machining and welding, performing base steel surface treatment, performing pre-heating treatment before base steel production, smelting copper alloy, dipping the copper alloy, melting anhydrous borax, putting base steel into a borax solution, pouring the copper alloy into the base steel, putting the base steel into a water tank and cooling and solidifying the base steel to room temperature to obtain the steel-copper composite cylinder body. According to the casting method, the problems of the composite casting technology and the composite material composition of the steel-copper cylinder body can be solved; and the composite strength of the thermometal cylinder body can be high, the yield can be high, the cost can be low, the size of the cylinder body can not be limited, the forming process can be controlled easily, and the quality can be stable.

Description

technical field [0001] The invention is applied to the field of metal casting, and in particular relates to a casting method of a steel-copper composite cylinder body. Background technique [0002] In the field of casting, the casting technology of steel-copper-metal composite is not mature and stable all the time. For a long time, welding or powder sintering methods have been used for production, but both methods have many limitations. If the welding compound is not strong, the metal will often fall off and the service life will be short; the size of the powder sintering molding cannot be too large, and the cost is very high. Through the understanding of advanced countries, the steel-copper composite cylinder block produced by casting method is the most reliable. There is a great demand for domestic steel-copper composite cylinders, but most of them still rely on imports, and most of the imported composite cylinders are produced by casting. The steel-copper composite cyl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22D19/16C22C9/08C23C18/50C23C22/42B22D27/20
CPCB22D19/0009B22D19/0081B22D19/16B22D27/20C22C9/08C23C18/1692C23C18/50C23C22/42Y02T10/40
Inventor 徐宏宋彬夏建强张国伟
Owner 安徽恒利增材制造科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap