Waterborne asphalt anticorrosion coating

A technology of anti-corrosion coatings and asphalt, which is applied in the direction of anti-corrosion coatings, asphalt coatings, coatings, etc., can solve the problems of harsh natural conditions, high decorative effect and service life requirements, high prices, etc., achieve low prices, solve environmental pollution and waste of resources As well as the damage to the human body and the effect of overcoming poor water resistance

Active Publication Date: 2019-05-17
宁波新灵防水材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Water-based fluororesin coatings are expensive and are currently limited to use in large buildings with harsh natural conditions, high decorative effects and service life requirements, and difficult to maintain

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne asphalt anticorrosion coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] 1) Preparation of anti-corrosion emulsified asphalt:

[0039] Take each raw material according to the following parts by weight:

[0040] 60 parts of 70# asphalt;

[0041] 0.5 parts of pine soap;

[0042] 1.5 parts of emulsifier;

[0043] Sodium hydroxide 0.5 part;

[0044] 1 part of defoamer;

[0045] Thickener 0.2 parts;

[0046] 40-50 parts of water.

[0047] Prepare the anti-corrosion emulsified asphalt by weighing each raw material according to the following method: add rosin soap, emulsifier, sodium hydroxide, defoamer, thickener and water into the reactor A, stir evenly, and heat up to 50- 70°C for standby; at the same time, add 70# asphalt to reactor B and heat it to 100-120°C for standby; finally, mix the raw materials in reactors A and B and pass through a colloid mill for high-speed shearing to prepare anti-corrosion emulsified asphalt for standby;

[0048] 2) Preparation of water-based asphalt anticorrosion coating:

[0049] Weigh each raw material o...

Embodiment 2

[0061] 1) Preparation of anti-corrosion emulsified asphalt:

[0062] Take each raw material according to the following parts by weight:

[0063] 55 parts of 70# asphalt;

[0064] 0.5 parts of pine soap;

[0065] 1.5 parts of carboxylate emulsifier;

[0066] Sodium hydroxide 0.5 part;

[0067] 1 part of mineral oil defoamer;

[0068] 0.2 part of polyurethane thickener;

[0069] 40 parts of water.

[0070] Prepare the anti-corrosion emulsified asphalt by weighing each raw material according to the following method: add rosin soap, carboxylate emulsifier, sodium hydroxide, mineral oil defoamer, polyurethane thickener and water into reaction kettle A, stir Evenly, heat up to 50-70°C for later use; at the same time, add 70# asphalt to reactor B and heat to 100-120°C for later use; finally, mix the raw materials in reactor A and B and pass through a colloid mill for high-speed shearing to produce Obtain anti-corrosion emulsified asphalt for use;

[0071] 2) Preparation of wate...

Embodiment 3

[0083] 1) Preparation of anti-corrosion emulsified asphalt:

[0084] Take each raw material according to the following parts by weight:

[0085] 60 parts of 70# asphalt;

[0086] 1.5 parts of pine soap;

[0087] 1.5 parts of sulfonate emulsifier;

[0088] Sodium hydroxide 0.5 part;

[0089] 1 part of defoamer;

[0090] Thickener 0.2 parts;

[0091] 50 parts of water.

[0092] Prepare the anti-corrosion emulsified asphalt by weighing each raw material according to the following method: add rosin soap, sulfonate emulsifier, sodium hydroxide, defoamer, thickener and water into reaction kettle A, stir evenly, and heat Raise the temperature to 50-70°C for later use; at the same time, add 70# bitumen to the reactor B and heat it to 100-120°C for later use; finally, mix the raw materials in the reactor A and B and pass through a colloid mill for high-speed shearing to obtain anti-corrosion emulsification Asphalt spare;

[0093] 2) Preparation of water-based asphalt anticorros...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a water-based asphalt anticorrosive paint which is prepared from the following raw materials in parts by weight: 65-90 parts of anticorrosive emulsified asphalt, 5-12 parts of acrylic emulsion, 5-12 parts of styrene-butadiene latex, 0.1-0.5 part of de-foaming agent, 1-3 parts of coalescing agents, 0.5-1 part of flatting agent, 0.1-0.2 part of anti-rusting agent and 0.3-1 part of thickening agent. The water-based asphalt anticorrosive paint has high stability, water resistance and weather fastness and has the characteristics of high drying speed, environmental protection and high efficiency.

Description

technical field [0001] The invention relates to a water-based asphalt anticorrosion paint. Background technique [0002] Petroleum asphalt has good adhesion, anti-aging and anti-corrosion capabilities, and has been used as an anti-corrosion material for a long time. It is one of the most widely used materials in anti-corrosion engineering at home and abroad because of its advantages of easy availability of raw materials and low price for anti-corrosion engineering. The loss caused by metal corrosion is very serious, and coating anti-corrosion coating is one of the main methods to prevent metal corrosion. [0003] At present, the vast majority of anti-corrosion coatings at home and abroad are mainly solvent-based coatings, which contain a large amount of organic volatiles, most of which are flammable and explosive toxic substances, which not only pollute the environment, waste energy, but also seriously It endangers the health of construction workers and brings multiple haz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D195/00C09D133/00C09D109/08C09D7/63C09D7/47C09D7/20C09D5/08
CPCC08L2201/08C08L2205/035C09D5/08C09D195/005C08L33/00C08L9/08C08K5/103C08K5/06
Inventor 冯凯平李玲
Owner 宁波新灵防水材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap