A kind of preparation method of modified alumina carrier

A technology of alumina support and modification, which is applied in the direction of catalyst support, chemical instruments and methods, metal/metal oxide/metal hydroxide catalysts, etc., can solve the problems such as the influence of support mechanical strength, and achieve the improvement of pore structure and mechanical strength. Strength, the effect of increasing the grain size

Active Publication Date: 2019-10-15
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the addition of physical pore-enlarging agents will affect the mechanical strength of the carrier, in addition, the interaction between the active component and the carrier needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of modified alumina carrier
  • A kind of preparation method of modified alumina carrier
  • A kind of preparation method of modified alumina carrier

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032]Weigh 10 grams of montmorillonite and bake at 950 °C for 5 hours. Mix the roasted montmorillonite with 200 g of pseudo-boehmite dry rubber powder (produced by Shandong Aluminum Co., Ltd.) and 6 grams of celadon powder, and pour into the mixture An appropriate amount of aqueous solution containing 5 grams of acetic acid was added to the material, extruded into a strip, dried at 120° C. for 5 hours, and then calcined at 300° C. for 5 hours. Put the roasted pseudo-boehmite in the polytetrafluoroethylene lining of the autoclave, add 400 grams of sodium hydroxide solution with a concentration of 4 mol / L at the same time, and heat the sealed autoclave at 90 ° C for 4 hours. The final material was filtered, washed with deionized water, dried at 110°C for 6 hours, and calcined at 600°C for 8 hours to obtain an alumina carrier.

[0033] Weigh 100 grams of the above-mentioned γ-phase cylindrical strip-shaped alumina carrier and put it into the spray rolling pot, and in the rotatin...

Embodiment 2

[0035] With embodiment 1, the add-on of diatomaceous earth is 30 grams. The low-temperature calcination temperature is 250° C., and the calcination time is 10 hours. The alkaline solution is a potassium hydroxide solution with a concentration of 3 mol / L, and the consumption of the solution is 1500 grams. The heat treatment temperature of the mixture was 100° C., and the treatment time was 3 hours. The alumina carrier is in the shape of clover strips. For the first spray and impregnation, use 30ml of an aqueous solution of sorbitol with a mass concentration of 30%, and for the second spray and impregnation, use 50ml of an aqueous solution of sorbitol with a mass concentration of 10%. In the first spraying and impregnation, 20ml of sorbitol aqueous solution with a mass concentration of 5% was used. The carbonization temperature was 200°C and the carbonization time was 8 hours to obtain carbon-containing alumina carrier S2. The properties of the carrier are shown in Table 1.

Embodiment 3

[0037] The montmorillonite was changed into kaolin the same as in Example 1, the roasting temperature was 1000° C., and the addition of kaolin was 20 grams. The low-temperature calcination temperature is 350° C., and the calcination time is 7 hours. The alkali solution is that the concentration is 5mol / L, and the solution consumption is 1200 grams. The heat treatment temperature of the mixture was 70° C., and the treatment time was 4 hours. Adopt four times of spray impregnation, use 20ml mass concentration to be the aqueous solution of mannitol of 50% when spraying and impregnating for the first time, use 40ml mass concentration to be the aqueous solution of sorbitol of 30% when spraying and impregnating for the second time, the third time Use 20ml of an aqueous solution of sorbitol with a mass concentration of 20% for spray impregnation, and use 20ml of an aqueous solution of sorbitol with a mass concentration of 10% for the fourth spray and impregnation. During the carbon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a modified alumina carrier, which includes the following contents: (1) kneading high-temperature-treated clay and pseudo-boehmite into shape, drying and low-temperature roasting of the molded product; (2) using alkali The material obtained in the solution soaking step (1) is sealed and heat treated, and then washed, dried and roasted to prepare an alumina carrier; (3) prepare at least two polyol and / or monosaccharide aqueous solutions with different concentrations, from high to low. Spray-impregnate the alumina carrier on the alumina carrier in a low order; (4) Perform hydrothermal carbonization and drying treatment on the alumina carrier impregnated in step (3) in a sealed container to prepare a modified alumina carrier. The alumina carrier prepared by this method has a suitable pore structure. At the same time, the surface of the alumina carrier pore channel is modified with carbon, and the carbon content is unevenly distributed in the radial direction of the carrier. The carrier is suitable for preparing heavy and residual oil hydrogenation and demetallization. Catalysts and other fields.

Description

technical field [0001] The invention relates to a method for preparing an alumina carrier, in particular to a method for preparing a carbon-modified alumina carrier. Background technique [0002] At present, in the production process of heavy oil hydrodemetallization, because the raw oil contains a certain amount of impurities such as vanadium, sulfur, arsenic, nickel, etc., it is easy to form deposits, thereby blocking the pores of the catalyst, resulting in a rapid decline in catalyst activity, and even Inactivation affects industrial applications. Catalysts with larger pore volume and larger pore diameter have strong metal and carbon storage capacity, which can slow down the deactivation of the catalyst and prolong the operation period of the catalyst. The pore structure of the catalyst is determined by the carrier that constitutes the catalyst. Therefore, the preparation of a carrier with a larger pore volume and larger pore diameter is an important step in the preparat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J21/18B01J32/00B01J23/883
CPCB01J21/18B01J23/883B01J37/0207B01J37/084B01J37/10B01J35/635B01J35/647B01J35/615
Inventor 佟佳吕振辉
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com