Anti-pilling cellulose fiber knitted fabric and production method thereof

A cellulose fiber and knitted fabric technology, applied in knitting, weft knitting, fabric surface trimming, etc., can solve the problem of easy pilling of cellulose fibers, and achieve large elastic extensibility, soft and comfortable hand feel, and small elastic recovery force. Effect

Inactive Publication Date: 2017-11-03
RUGAO CHANGJIANG SCI & TECHCAL IND CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In recent years, as people continue to pursue more comfortable wearing, more and more cellulose fibers are used in knitted fabrics. Cellulose fibers are softer and more hygroscopic than cotton fibers, but cellulose fibers have the disadvantage of easy pilling.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A kind of anti-pilling cellulose fiber knitted fabric, using the blended yarn of cellulose fiber and cotton fiber and spandex screw as raw material, the weight content of cellulose fiber is 45%, the fineness is 0.56dtex, the weight of cotton fiber The content is 25%, the fineness is 1.62dtex, the fineness of blended yarn is 14.1dtex, and the fineness of spandex bare silk is 21dtex.

[0014] A kind of production method of the knitted fabric of anti-pilling cellulose fiber, the production is completed through the steps of spinning, weaving and presetting, and the specific steps are as follows:

[0015] (1) Spun yarn: The drawing process is introduced in the spun yarn processing stage, and the cellulose fiber strips and cotton fiber strips are mixed and drafted to obtain a blended yarn of cellulose fibers and cotton fibers;

[0016] (2) Weaving: The blended yarn of cellulose fiber and cotton fiber is used as ground yarn and spandex screw, and weaving is carried out by weav...

Embodiment 2

[0023] A kind of anti-pilling cellulose fiber knitted fabric, using the blended yarn of cellulose fiber and cotton fiber and spandex screw as raw material, the weight content of cellulose fiber is 75%, the fineness is 0.86dtex, the weight of cotton fiber The content is 55%, the fineness is 1.62dtex, the fineness of blended yarn is 27.4dtex, and the fineness of spandex bare silk is 28dtex.

[0024] A kind of production method of the knitted fabric of anti-pilling cellulose fiber, the production is completed through the steps of spinning, weaving and presetting, and the specific steps are as follows:

[0025] (1) Spun yarn: The drawing process is introduced in the spun yarn processing stage, and the cellulose fiber strips and cotton fiber strips are mixed and drafted to obtain a blended yarn of cellulose fibers and cotton fibers;

[0026] (2) Weaving: The blended yarn of cellulose fiber and cotton fiber is used as ground yarn and spandex screw, and weaving is carried out by weav...

Embodiment 3

[0033] A kind of anti-pilling cellulose fiber knitted fabric, using the blended yarn of cellulose fiber and cotton fiber and spandex screw as raw material, the weight content of cellulose fiber is 60%, the fineness is 0.66dtex, the weight of cotton fiber The content is 40%, the fineness is 1.62dtex, the fineness of blended yarn is 20.5dtex, and the fineness of spandex bare silk is 25dtex.

[0034] A kind of production method of the knitted fabric of anti-pilling cellulose fiber, the production is completed through the steps of spinning, weaving and presetting, and the specific steps are as follows:

[0035] (1) Spun yarn: The drawing process is introduced in the spun yarn processing stage, and the cellulose fiber strips and cotton fiber strips are mixed and drafted to obtain a blended yarn of cellulose fibers and cotton fibers;

[0036] (2) Weaving: The blended yarn of cellulose fiber and cotton fiber is used as ground yarn and spandex screw, and weaving is carried out by weav...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-pilling cellulose fiber knitted fabric and a production method thereof. The blended yarn of cellulose fiber and cotton fiber and spandex screw are used as raw materials, and the fabric is produced through the steps of spinning, weaving and presetting. The advantage of the present invention is that: the present invention effectively solves the problem of anti-pilling of the blended fabric mainly composed of cellulose fibers, and realizes that the fabric has high elastic extensibility and small elastic recovery force, and the underwear is soft and comfortable after being made into underwear.

Description

technical field [0001] The invention relates to the technical field of spinning, in particular to an anti-pilling cellulose fiber knitted fabric and a production method thereof. Background technique [0002] Pilling on the surface of textile fabrics generally occurs on natural fibers and chemical fiber fabrics, while chemical fibers are more obvious and prominent. Fabric pilling affects the appearance of clothing and reduces wearability. With the improvement of living standards, people are more concerned about the appearance of fabrics. Therefore, the anti-pilling finishing of fabrics to improve the wearing comfort and quality of fabrics has increasingly attracted the attention of dyeing and finishing workers at home and abroad. [0003] In recent years, as people continue to pursue more comfortable wearing, more and more cellulose fibers are used in knitted fabrics. Cellulose fibers are softer than cotton fibers and have better hygroscopicity, but cellulose fibers have the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/00D04B1/14D06C7/02
CPCD04B1/00D04B1/14D06C7/02D10B2201/02D10B2331/10D10B2401/061D10B2501/02
Inventor 朱杰
Owner RUGAO CHANGJIANG SCI & TECHCAL IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com