Method of preparing channel steel by local heating and stepwise roll pressing

A technology of local heating and channel steel, which is applied in the field of rolling and forming of steel materials, can solve the problems of large stress concentration of channel steel, large degree of plastic deformation of materials, difficulty in obtaining dovetail groove edges, etc., and achieves high production efficiency and low production cost , Dimensional accuracy is easy to guarantee the effect

Inactive Publication Date: 2017-11-28
TIANJIN LEYING TECH CO LTD
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The processing process of cold rolling or cold bending process does not require heating, but the degree of plastic deformation of the material is large, the stress concentration of the channel steel is large, and it is difficult to obtain the dovetail groove edge

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0006] In order to further illustrate the present invention, the present invention will be further described in detail below in conjunction with preferred embodiments.

[0007] A channel steel for the bottom of hollow glass, the size of the rollers in the equipment and the gap between the rollers are adjusted according to the size of the special channel steel.

[0008] In order to ensure the automatic operation of the channel steel manufacturing process, the strip steel is limited by a pair of side lying rollers when feeding. The strip 2 is leveled by two pairs of leveling rollers after passing through the side-lying roller limit rollers. After the strip is leveled, it passes through a pair of rollers (for micro-pressing. When micro-pressing, the upper roller is the driving wheel, and the lower roller is the driven wheel; there are small acute angles on both sides of the upper roller surface, so that the upper roller A small acute-angle slope is formed at the outer edge of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a channel steel forming method, which belongs to the technical field of rolling, processing and forming of iron and steel materials. The forming process of channel steel is as follows: strip steel feeding → leveling → micro pressure → local heating → dovetail edge forming → cooling → step-by-step cold bending forming → straightening → blanking. The channel steel is prepared by local heating and multi-channel step-by-step roll forming. The dimensional accuracy of the prepared professional channel steel is easy to ensure, and the appearance is free of burrs. The production efficiency of channel steel produced by the method of the invention is high, the process is simple, and the obtained special channel steel has strong bearing capacity, long service life and low production cost.

Description

technical field [0001] The invention relates to a channel steel forming method, which belongs to the technical field of rolling, processing and forming of iron and steel materials. Background technique [0002] The processing process of cold rolling or cold bending process does not require heating, but the degree of plastic deformation of the material is large, the stress concentration of the channel steel is large, and it is difficult to obtain the dovetail groove edge. Therefore, it is very meaningful to research and develop the forming process of channel steel with dovetail groove edge without hot rolling, uniform plastic deformation and low cost in the forming process. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies of the prior art and provide a method for preparing channel steel with dovetail groove edges by adopting partial heating and step-by-step roll forming. [0004] The technical solution of the present i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21D5/08B21D21/00B21B1/095
CPCB21D5/08B21B1/095B21D21/00
Inventor 王洪乐
Owner TIANJIN LEYING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com