High-performance assembling type construction reinforcing steel bar sleeve grouting material and using method thereof

A technology for building steel bars and sleeve grouting, which is applied in construction, building components, building structures, etc., can solve the problems of the quality of grouting materials not up to standard and high price, and achieve the benefits of environmental protection, price reduction, and improvement of compressive strength Effect

Inactive Publication Date: 2018-01-12
云南鼎安翔农业产业发展股份有限公司
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to propose a high-performance prefabricated building steel sleeve grouting material, which is replaced by mountain sand or river sand, in view of the situation that the price of the grout

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance assembling type construction reinforcing steel bar sleeve grouting material and using method thereof
  • High-performance assembling type construction reinforcing steel bar sleeve grouting material and using method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1: as figure 1 As shown, the mass ratio components of the high-performance prefabricated building steel sleeve grouting material of the present invention are: 80 parts of cement, 80 parts of quartz sand, 10 parts of mountain sand or river sand, 10 parts of expansion agent, 1 part of retarder, 0.5 part of water reducer, 1 part of defoamer, 15 parts of steel slag. The particle size of quartz sand, mountain sand or river sand, and steel slag powder is 400 mesh. Calcium sulfoaluminate is used as expansion agent, sodium gluconate is used as retarder, polycarboxylate water reducer is used as water reducer, and rosin thermal polymer is used as defoamer.

[0016] The method of using the high-performance prefabricated building reinforcement sleeve grouting material of the present invention is: under normal temperature and normal pressure, first take cement, quartz sand, mountain sand or river sand, and steel slag in proportion, and mix them evenly; then press the wei...

Embodiment 2

[0017] Embodiment 2: as figure 1 As shown, the mass ratio components of the high-performance prefabricated building steel sleeve grouting material of the present invention are: 90 parts of cement, 40 parts of quartz sand, 40 parts of mountain sand, 5 parts of expansion agent, 0.5 part of retarder, and water reducer 3 parts, 20 parts of steel slag. The particle size of quartz sand, mountain sand or river sand, and steel slag powder is 700 mesh. The expansion agent is MgO, the retarder is calcium lignosulfonate, the water reducer is phosphate, and the defoamer is petroleum sulfonate.

[0018] The method of using the high-performance prefabricated building steel sleeve grouting material of the present invention is: under normal temperature and normal pressure, first take cement, quartz sand, mountain sand, and steel slag in proportion, and mix them evenly; then press 13% of the mixture weight, Slowly add water and stir. During the stirring process, slowly add expansion agent, r...

Embodiment 3

[0019] Embodiment 3: as figure 1 As shown, the mass ratio components of the high-performance prefabricated building steel sleeve grouting material of the present invention are: 100 parts of cement, 100 parts of river sand, 15 parts of expansion agent, 2 parts of water reducing agent, 0.5 part of defoamer, and 80 parts of steel slag share. The particle size of quartz sand, mountain sand or river sand, and steel slag powder is 1000 mesh. The expansion agent is gypsum, the retarder is sodium gluconate, the water reducing agent is zinc salt, and the defoamer is hydroxyethyl methyl cellulose ether.

[0020] The method of using the high-performance prefabricated building reinforcement sleeve grouting material of the present invention is: under normal temperature and normal pressure, first take cement, quartz sand, mountain sand or river sand, and steel slag in proportion, and mix them evenly; then press the weight of the mixture 14%, slowly add water and stir, and slowly add expan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-performance assembling type construction reinforcing steel bar sleeve grouting material and a using method thereof, and belongs to the technical field of building materials. The grouting material consists of the following components in parts by mass: 80 to 100 parts of cement, 0 to 80 parts of quartz sand, 10 to 100 parts of mountain sand or river sand, 5 to 15 partsof an expanding agent, 0 to 1 part of a set retarder, 0.5 to 3 parts of a water reducing agent, 0 to 1 part of a defoaming agent and 15 to 80 parts of steel slag powder. When the grouting material isused, the cement, the quartz sand and steel slag are uniformly mixed in proportion first, then 2 to 3 times of water is added slowly, the materials are stirred, the expanding agent, the set retarder,the water reducing agent and the defoaming agent are added in proportion in a stirring process, and after the materials are stirred uniformly into the grouting material, the grouting material can beused. According to the grouting material, the quartz sand is partially or completely replaced by adopting the river sand or the mountain sand, the using of complex admixtures is reduced, and industrial waste steel slag is added, so that the performance of the grouting material can be maintained, and meanwhile, the cost is greatly reduced; therefore, the grouting material is suitable to be widely applied in an assembling type construction reinforcing steel bar sleeve grouting material.

Description

technical field [0001] The invention relates to a high-performance assembled building reinforcement sleeve grouting material, which belongs to the technical field of building materials. Background technique [0002] At present, with the increasing promotion of prefabricated buildings in the country, more and more grouting materials are used. Most of the existing grouting materials are mainly composed of cement, quartz sand, expansion agent, retarder, and water reducing agent. , the compressive strength of this kind of grouting material is ≥85MPa, which can meet the basic performance of the grouting material specification, but the main indicators such as vertical expansion rate and fluidity cannot meet the standard requirements, especially the fluidity, and most domestic grouting materials cannot meet the standard requirements , After 10 minutes, the solidified state appeared. In order to meet the standard strength standard, the existing technology usually uses quartz sand a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00E04C5/20C04B111/70
Inventor 陈红梅张沛钦茶文祥肖琴许云涛
Owner 云南鼎安翔农业产业发展股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap