A dinuclear monovalent gold complex containing a bispyridine group with both aggregation-induced luminescent and mechanochromic properties and its application

A technology of aggregation-induced luminescence and gold complexes, which is applied in the fields of gold organic compounds, compounds containing elements of Group 1/11 of the periodic table, luminescent materials, etc.

Active Publication Date:
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, a large number of AIE compounds have been reported, but these compounds are alm...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A dinuclear monovalent gold complex containing a bispyridine group with both aggregation-induced luminescent and mechanochromic properties and its application
  • A dinuclear monovalent gold complex containing a bispyridine group with both aggregation-induced luminescent and mechanochromic properties and its application
  • A dinuclear monovalent gold complex containing a bispyridine group with both aggregation-induced luminescent and mechanochromic properties and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1: the synthesis of complex 1

[0020] The synthetic route is as follows:

[0021]

[0022] CH in the reaction formula 2 Cl 2 - dichloromethane; Au(C 6 f 5 )(tht)-tetrahydrothiophene pentafluorophenyl gold

[0023] Concrete synthetic steps are as follows:

[0024] 1. Under nitrogen atmosphere conditions, 0.3g (1.92mmol) of 2,3′-bipyridine, Au(C 6 f 5 )(tht) 1.78g (3.94mmol) and 30ml of dichloromethane that has been exhausted are added to vacuumize and fill with N 2 In the final reaction vessel, react at room temperature for 10-12 hours. After the reaction finishes, spin out the dichloromethane solvent and separate by column chromatography (the eluent is a mixed solvent of sherwood oil and dichloromethane, and the volume ratio is 1:1). 1.61 g of the target product, complex 1, was obtained as a white solid. Yield: 94.79%. 1 H NMR (400MHz, CDCl 3 ):δ(ppm)=9.31(s,1H),8.78-8.62(m,3H),7.90-7.69(m,3H),7.41(t,J=6Hz,1H).Anal.Calcd for C 22 h 8 Au 2 f ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a dinuclear monovalent gold complex containing a bipyridine group, which has both aggregation-induced luminescence and mechanochromic properties, and its application. A dinuclear monovalent gold complex containing a bipyridine group, which has both aggregation-induced luminescence and mechanochromic properties, has the structure described in formula 1. This metal complex exhibits an aggregation-induced luminescence effect from colorless to yellow, and the photoluminescence of the solid sample can be changed from green to bright yellow after mechanical grinding, and the yellow luminescence after grinding The green luminescence can be restored after the methyl chloride solvent vapor treatment. Therefore, such gold-containing complexes are expected to be used in the fields of luminescent materials and mechanical sensors.

Description

technical field [0001] The present invention relates to a novel stimuli-responsive luminescent material and its application, in particular to a novel double-nuclear monovalent gold complex containing bispyridine groups with both aggregation-induced luminescent and mechanochromic properties and its application. Background technique [0002] Mechanochromic materials that respond to mechanical force have aroused extensive research interest of scientists due to their potential application value in the fields of mechanical sensors, anti-counterfeiting and information storage. Under the action of external mechanical force, the optical properties of smart materials with mechanochromic properties will change. So far, many pure organic compounds with mechanochromic properties have been reported. In comparison, the number of metal complexes with mechanochromic properties is very limited. In addition, traditional luminescent materials often emit strongly in solution, but under the con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C07F1/12C09K11/06C09K9/02
CPCC07F1/00C09K9/02C09K11/06C09K2211/188
Inventor 蒲守智陈钊刘刚
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products