Preparation method and application of metal boride and sulfur composite nanometer material

A technology of composite nanomaterials and metal borides, applied in nanotechnology, nanotechnology, nanotechnology, etc. for materials and surface science, can solve problems such as lithium polysulfide shuttle effect, and achieve clean and environmentally friendly preparation process, catalytic discharge process, effect of promoting transformation

Active Publication Date: 2018-03-06
HARBIN INST OF TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problem of the shuttle effect of lithium polysulfide in lithium-sulfur batteries, to provide a preparation method and application of metal boride and sulfur composite nanomaterials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of metal boride and sulfur composite nanometer material
  • Preparation method and application of metal boride and sulfur composite nanometer material
  • Preparation method and application of metal boride and sulfur composite nanometer material

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0022] Specific embodiment one: what this embodiment records is a kind of preparation method of metal boride and sulfur composite nanomaterial, described method step is as follows:

[0023] Step 1: dissolving sodium borohydride and NaOH in deionized water under inert gas protection conditions to obtain a reducing agent solution, wherein the concentrations of sodium borohydride and NaOH are both 0.5-3 M; dissolving the metal salt in deionized water, To obtain a metal salt solution with a concentration of 0.5-2M, separate the obtained reducing agent solution and metal salt solution into an ice-water bath for 15 minutes;

[0024] Step 2: Under the protection of an inert gas, slowly add the metal salt solution after the ice-water bath to an equal volume of reducing agent solution at a rate of one drop per second, and stir for 30 minutes to obtain a dry product, and then place the dry product at 350- High-temperature calcination at 500°C for 2-10 hours to obtain metal borides;

[...

specific Embodiment approach 2

[0026] Specific embodiment two: the preparation method of a metal boride and sulfur composite nanomaterial described in specific embodiment one, in step one, the metal salt is a kind of in iron salt, cobalt salt, nickel salt, molybdenum salt .

specific Embodiment approach 3

[0027] Specific embodiment three: the preparation method of a metal boride and sulfur composite nanomaterial described in specific embodiment one, in step two, the morphology of the metal boride is nanowire, nanorod, nanosphere, nanosheet , nanoparticle, nanoarray, nanoflower, nanocube, determined by its experimental temperature, adding speed and concentration; material surface defects can be regulated by calcination temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method and application of a metal boride and sulfur composite nanometer material, and belongs to the technical field of an energy material. The method comprisesthe following steps: dissolving a reducing agent and NaOH into deionized water under the protection condition of inert gas, dissolving metal salt into the deionized water and putting the obtained twosolutions into ice-water bath separately; under the protection condition of the inert gas, slowly adding the metal salt aqueous solution in the step 1 into the reducing agent solution, stirring for 30minutes and performing high-temperature calcination for 2 to 10 hours to obtain metal boride; and mixing the metal boride and elemental sulfur according to the mass ratio of 1:(1-4), and heating andcalcining at the temperature of 150 to 180 DEG C for 12 to 24 hours to obtain the metal boride and sulfur composite nanometer material. The preparation method and the application of the metal boride and sulfur composite nanometer material have the following advantages: the metal boride has high lithium polysulfide adsorption ability and can improve the stability of a lithium sulfur battery; the crystallinity degree and the defect site of the metal boride can be controlled through different calcination temperature and time, so that the whole performance of the lithium sulfur battery is controlled; and the cost is low, the process is simple and the preparation process is clean and environment-friendly.

Description

technical field [0001] The invention belongs to the technical field of energy materials, and in particular relates to a preparation method and application of metal boride and sulfur composite nanomaterials. Background technique [0002] With the development of the portable electronics industry, the demand for high specific energy batteries is more urgent, limited by the specific capacity of traditional materials such as lithium cobaltate and lithium manganese oxide, lithium ion batteries have been unable to meet the growing demand. It is imperative to seek a secondary battery with higher specific capacity. Lithium-sulfur battery has attracted the attention of researchers in recent years. It has the characteristics of high specific capacity (1675mAh / g), low cost, wide source of elemental sulfur, and non-toxicity. It is expected to become the next generation of commercialized secondary battery system. [0003] However, there are still many difficulties restricting the commerc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M4/36H01M4/38H01M4/62H01M10/0525B82Y30/00
CPCB82Y30/00H01M4/364H01M4/38H01M4/628H01M10/0525Y02E60/10
Inventor 孙克宁关斌张乃庆范立双
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com