A polyurethane and system technology, applied in the field of halogen-free flame retardants, can solve problems such as poor flame retardancy, whitening, and reduced insulation properties of materials, and achieve good compatibility.

Active Publication Date: 2019-08-13
JIANGSU LISIDE NEW MATERIAL
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the most widely used are ammonium polyphosphate (APP) with high polymerization degree and organic phosphates, ammonium polyphosphate (APP) flame retardant system with high polymerization degree, which belongs to an intumescent flame retardant system, because of its flame retardant Compared with the inorganic hydroxide system, the addition amount is much lower than that of the inorganic hydroxide system. However, APP is still incompatible with the base material due to its hydrophilic surface and certain water solubility. Therefore, the flame-retardant polyurethane material of the APP system The mechanical strength is still low, and at the same time, it is easy to migrate and precipitate, and the whitening phenomenon of precipitation occurs on the surface of the product
In addition, due to the presence of ammonium ions, APP is easy to absorb moisture, and water droplets will appear on the surface of the product after a period of time. If there are water droplets on the surface of polyurethane leather products, or after the leather is exposed to water, water spots will form on the surface of the product after drying. It affects the appearance of the product, and at the same time has a sticky feel, which reduces the touch of polyurethane leather. If there are water droplets on the surface of the TPU cable, the insulation performance of the material is reduced, and there is a major safety hazard; while some organic phosphates still have Water-soluble, although some water-soluble is small, it overcomes the problem of forming water stains or reducing cable insulation, but its flame retardant mechanism belongs to condensed phase flame retardant, which belongs to non-expandable, non-expandable flame-retardant system. For polyurethane materials, in It is easy to form drips when it is on fire, and the molten droplets will affect the flame retardant effect, and it is difficult to meet the requirements of the standard
[0007] In general, the main defects of the flame retardant system currently applied to polyurethane materials are: poor flame retardancy, easy to melt, easy to absorb moisture to form water spots or reduce insulation and migration whitening and other issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A halogen-free flame-retardant composite system for polyurethane and its application in halogen-free flame-retardant polyurethane
  • A halogen-free flame-retardant composite system for polyurethane and its application in halogen-free flame-retardant polyurethane
  • A halogen-free flame-retardant composite system for polyurethane and its application in halogen-free flame-retardant polyurethane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] The compound flame retardant system is applied to thermoplastic polyurethane TPU to prepare cable materials. According to the following steps and test methods to investigate the performance of flame retardants.

[0056] (1) Mixing of halogen-free flame retardant TPU system

[0057] Dry the TPU in advance, add TPU, compound flame retardant system and other additives that have been weighed in advance according to the proportion (if there is no special statement, the proportion in the present invention is weight percentage), start high-speed stirring, Stir for 10 minutes to complete the compounding of the halogen-free flame-retardant TPU system and discharge.

[0058] (2) Extrusion granulation of materials

[0059] Set the temperature of each zone of the twin-screw extruder at the predetermined temperature (the maximum temperature of the plasticizing section of the screw is 210°C). After the temperature stabilizes for 20 minutes, add a uniformly mixed halogen-free flame-...

Embodiment 2

[0075] The implementation process is the same as that of Example 1, except that the ratio of aluminum diethyl hypophosphite and char-forming agent is adjusted, the ratio of diethyl hypophosphite is increased, and the total amount of the flame retardant system remains unchanged. Other materials and proportioning are shown in Table 1, and the obtained material results are shown in Table 1.

Embodiment 3

[0077] The implementation process is the same as that of Example 1, except that the ratio of aluminum diethyl hypophosphite and char-forming agent is adjusted, the ratio of char-forming agent is increased, and the total amount of the flame retardant system remains unchanged. Other materials and proportioning are shown in Table 1, and the obtained material results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a halogen-free flame-retardant compounded system for polyurethane. The halogen-free flame-retardant compounded system comprises the following raw materials in percentage by weight: 50-90% of diethyl aluminum hypophosphite, and 10-50% of a charring agent, wherein the charring agent is an insoluble and infusible crosslinked polymer, and a cross-linking point structure is shown in the following formula (I). The invention develops a novel halogen-free flame-retardant compounded system for polyurethane to overcome the defects of an existing flame-retardant system applied topolyurethane materials, and the halogen-free flame-retardant compounded system has the characteristics of no molten drop, high flame retardance, migration resistance, moisture absorption resistance, good compatibility with matrix polyurethane materials and the like, and can be used for preparing a halogen-free flame-retardant polyurethane material.

Description

technical field [0001] The invention relates to the technical field of halogen-free flame retardants, in particular to a halogen-free flame-retardant composite system for polyurethane and its application in halogen-free flame-retardant polyurethane. Background technique [0002] Polyurethane is a type of polymer whose main chain contains -NHCOO- repeating structural units, abbreviated as PU in English, which is polymerized from isocyanate (monomer) and hydroxyl compound. Because it contains a strong polar carbamate group, it is insoluble in non-polar solvents, and has good oil resistance, toughness, wear resistance, aging resistance, etc., and has been widely used in many fields. Polyurethane includes two types of materials, one is thermosetting PU, which is usually used in synthetic leather, foaming and other fields; the other is thermoplastic polyurethane, referred to as TPU, which has the processing method of thermoplastic materials and has the properties of thermosetting...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L75/04C08L85/02C08K5/5313C08G79/04
CPCC08G79/04C08K5/5313C08L75/04C08L2201/02C08L2201/22C08L85/02
Inventor 李金忠雷华
Owner JIANGSU LISIDE NEW MATERIAL