Underbody cover for vehicle and manufacturing method thereof

A manufacturing method and body technology, applied in vehicle parts, chemical instruments and methods, applications, etc., can solve problems such as heavy weight, inability to effectively block impact sound, etc., and achieve high mechanical strength, excellent sound insulation performance, and lightness. Effect

Active Publication Date: 2021-07-09
LG HAUSYS LTD +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since this reinforced fiber composite material is composed of a high-density material with no porosity, it has the disadvantage of being relatively heavy and unable to effectively block the impact sound generated on the ground such as a sandy road or a stone road.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Underbody cover for vehicle and manufacturing method thereof
  • Underbody cover for vehicle and manufacturing method thereof
  • Underbody cover for vehicle and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0143] As the binary polymer fiber, the following fibers were prepared: the polyester core and the low-melting point polyester sheath had a weight ratio of 50:50, a length of 5 mm in order to ensure water dispersibility, and 4 denier (about 20μm cross-sectional diameter) thickness. Glass fibers having a cross-sectional diameter of 13 μm and coated in a manner suitable for water-based dispersion were cut to a length of 13 mm to prepare glass fibers. After blending 40 parts by weight of the above-mentioned glass fiber and 60 parts by weight of the above-mentioned binary polymer fiber, it was stirred in an aqueous solution adjusted to pH 2 with hydrochloric acid for 1 hour. In this case, the total fiber content of glass fibers and binary polymer fibers was adjusted to 2 g per 1 L of water. On the aqueous slurry that has been subjected to the stirring process in the manner described above, a wet papermaking process was performed in a headbox by vacuum suction to form a web. Afte...

Embodiment 2

[0145] In order to improve the binding force between the polyester resin, the glass fiber with special silane coating treatment on the surface was used instead of the glass fiber used in Example 1. After the composite material sheet is produced in the same way, then, the composite material preformed plate is formed in the same method as in Example 1, and then the above-mentioned composite material is preheated in an IR oven at a temperature of 200° C. for 2 minutes. The material preformed sheet expands and is transferred to the press process at room temperature, and pressure is applied to complete the vehicle underbody cover with an average thickness of 2.0 mm.

Embodiment 3

[0147] With 10 parts by weight of the glass fibers used in Example 2 with a special silane-coated surface and 90 parts by weight of binary polymer fibers, except for this point, in the same manner as in Example 2 Method After the composite material sheet is manufactured, the composite material preformed plate is formed in the same method as in Example 2, and then the above composite material is preheated again in an IR oven at a temperature of 200° C. for 2 minutes. The molded sheet expands and is transferred to a press process at room temperature, and pressure is applied to complete the vehicle undercover with an average thickness of 2.0 mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
lengthaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The present invention provides an undercover for a vehicle, comprising: a central layer; and a cover layer disposed on both sides of the central layer, the central layer comprising: first fibrous particles; second fibrous particles; and an adhesive material used When the above-mentioned first fibrous particles and the above-mentioned second fibrous particles are adhered, the above-mentioned first fibrous particles and the above-mentioned second fibrous particles are adhered by the above-mentioned adhesive material to form an irregular network structure including pores, and the above-mentioned first fibrous particles A fibrous particle is an inorganic fiber or an organic fiber, the second fibrous particle contains a first thermoplastic resin, the adhesive material contains a second thermoplastic resin, and the melting point of the first thermoplastic resin is higher than the melting point of the second thermoplastic resin.

Description

technical field [0001] The present invention relates to an undercover for a vehicle and a manufacturing method thereof. Background technique [0002] The undercover for vehicles has the effect of protecting the vehicle body from external impacts, reducing noise, and improving fuel economy by allowing air to flow smoothly while the vehicle is running. Therefore, it is used not only for commercial vehicles but also for passenger cars due to exhibiting excellent effects in characteristics that are currently prioritized for vehicles such as high fuel economy or quietness. Initially, the vehicle underbody cover was made of steel for the main purpose of protecting the vehicle body, but due to the disadvantages of corrosion and heavy weight, it was gradually replaced by thermoplastic injection molding. However, since thermoplastics exhibit very low physical properties compared to the strength required for undercovers for general vehicles, composite materials in which thermoplastic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B62D25/20B60R13/08B29C43/18
CPCB60R13/0861B29C43/18B29L2031/3005B62D25/20B60R13/08B32B5/06B32B3/26B32B5/022B32B7/12B32B5/26B32B27/08B32B27/12B32B15/14B32B15/08B32B15/04B32B15/20B32B27/36B32B27/32B32B27/302B32B27/365B32B27/34B32B27/304B32B27/40B32B27/308B32B27/322B32B2262/101B32B2262/0269B32B2262/106B32B2262/10B32B2262/103B32B2262/14B32B2260/023B32B2260/046B32B2262/0284B32B2307/72B32B2307/718B32B2307/732B32B2307/546B32B2307/54B32B2307/558B32B2307/306B32B2307/728B32B2307/73B32B2307/3065B32B2605/08
Inventor 安承贤韩庆锡郑胜文
Owner LG HAUSYS LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com