A new type of brush for cleaning glass oil stains

An oil cleaning and brush technology, applied in the field of new glass oil cleaning brushes, can solve the problems of glass scratches, wear resistance not as good as 610, oil stains on the glass surface cannot be absorbed and diluted, etc., and achieves long practical life and increased toughness. Effect

Active Publication Date: 2019-12-27
江门市意奇高工贸有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The oil stains on the glass have always been the most troublesome place for cleaning. At present, newspapers are often used to wipe them, which is time-consuming and laborious. The existing concentrated brush materials cannot clean oil stains on the glass;
[0003] The elasticity of PBT wire is better than that of nylon brush wire, but its wear resistance is not as good as 610. The performance of PBT is softer. It is most suitable for cleaning and decontaminating fine parts, such as car surface cleaning, but it cannot absorb and dilute oil stains on the glass surface;
[0004] Nylon or flocking brush, the brush wire has good wear resistance, high temperature resistance, acid and alkali resistance, good elasticity, and is suitable for household dust removal and cleaning brush parts, such as vacuum cleaner roller brushes, brush rollers, brush platforms, etc. etc. Long-term friction on the glass surface may easily cause scratches on the glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A new type of brush for cleaning glass oil stains
  • A new type of brush for cleaning glass oil stains
  • A new type of brush for cleaning glass oil stains

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0034] Specific embodiment 1: as figure 1 and figure 2 , a new type of glass oil cleaning brush, the brush 1 is a three-layer structure, nested with each other, the inner layer is a corrosion-resistant high-toughness rubber strip 11, the middle layer is a soluble soft wax 12, and the outer layer is a sponge 13;

[0035] A certain amount of mixed cleaning solution of citric acid and water is absorbed in the sponge, and the ratio is 1:350;

[0036] The top of the hairbrush of the three-layer structure is bound with a rubber band, inserted on the cleaning tool 2, and 30-40 hairbrushes are inserted on the cleaning tool.

[0037] The overall diameter of the brush is 0.7-1cm, and the length is 10-12cm. Each time it absorbs the mixed cleaning solution of citric acid and water, the use area is 0.8-1 square meter.

specific Embodiment 2

[0038] Specific embodiment 2: a new type of brush for cleaning glass oil stains, the brush is a three-layer structure, nested with each other, the inner layer is a corrosion-resistant high-toughness rubber strip, the middle layer is a soluble soft wax, and the outer layer is a sponge;

[0039] A certain amount of mixed cleaning solution of citric acid and water is absorbed in the sponge, and the ratio is 1:300;

[0040] The top of the hairbrush of the three-layer structure is bound with a rubber band, inserted on the cleaning tool, and 30-40 hairbrushes are inserted on the cleaning tool.

[0041] The overall diameter of the brush is 0.7-1cm, and the length is 10-12cm. Each time it absorbs the mixed cleaning solution of citric acid and water, the use area is 0.8-1 square meter.

specific Embodiment 3

[0042] Specific embodiment 3: a kind of novel glass grease cleaning hairbrush, its hairbrush is a three-layer structure, nested with each other, the inner layer is a corrosion-resistant high-toughness rubber strip, the middle layer is a soluble soft wax, and the outer layer is a sponge;

[0043] Corrosion-resistant high-toughness rubber strips specifically include 70 parts of butyl rubber, 10 parts of ethylene vinyl acetate copolymer, 8 parts of chitosan, 5 parts of hydroxypropyl methylcellulose, 6 parts of antioxidant, 12 parts of toughening agent, 95 parts of polyphenylene sulfide raw powder, 1 part of dispersed coupling agent, 30 parts of toughened polyvinyl chloride resin, 2 parts of acrylate polymer.

[0044] The preparation method of the corrosion-resistant high-toughness rubber strip is as follows:

[0045] Extrude ethylene vinyl acetate copolymer, chitosan, and hydroxypropyl methylcellulose through a twin-screw extruder. The screw length-to-diameter ratio of the twin-s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel glass oil stain cleaning hairbrush. The hairbrush is of a three-layer structure, wherein the three layers are mutually nested; the inner layer is a corrosion-resistinghigh-tenacity rubber strip; the middle layer is soluble soft wax; and the outer layer is a sponge. The hairbrush has the beneficial effects that the inner layer, which is the corrosion-resisting high-tenacity rubber strip, can be bent forth and back due to the addition of toughened polyvinyl chloride, so that service life in practical use is prolonged; through acrylate polymer double bonds, self-polymerization and co-polymerization are promoted, agglomeration is accelerated, and tenacity is enhanced; the middle layer, which is soluble soft wax, takes micro-crystalline wax as a main body, and the middle layer is defined in cooperation with the micro-crystalline wax and vegetable oil; the outer layer is covered by wax which is prepared from an oil gel, and the wax can get thinned as being dissolved together with oil stains which are adsorbed, so that the oil stains can be effectively cleaned; the oil stains are adsorbed by virtue of the sponge of the outer layer; and the oil stains can penetrate to the surface of the wax via the sponge, get dissolved together with the wax and remain on the sponge, so that secondary pollution to glass is prevented.

Description

Technical field: [0001] The invention relates to cleaning supplies, in particular to a novel brush for cleaning glass oil stains. Background technique: [0002] The oil stains on the glass have always been the most troublesome place for cleaning. At present, newspapers are often used to wipe them, which is time-consuming and laborious. The existing concentrated brush materials cannot clean oil stains on the glass; [0003] The elasticity of PBT wire is better than that of nylon brush wire, but its wear resistance is not as good as 610. The performance of PBT is softer, and it is most suitable for cleaning and decontaminating fine parts, such as car surface cleaning, but it cannot absorb and dilute oil stains on the glass surface; [0004] Nylon or planting brush, the brush wire has good wear resistance, high temperature resistance, acid and alkali resistance, good elasticity, and is suitable for household dust removal and cleaning brush parts, such as vacuum cleaner roller b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A46D1/00C08L23/22C08L23/08C08L5/08C08L81/02C08L27/06C08L33/04
CPCA46D1/0207C08L23/22C08L2205/02C08L2205/035C08L23/0853C08L5/08C08L1/284C08L81/02C08L27/06C08L33/04
Inventor 王小艳
Owner 江门市意奇高工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products