A kind of anticorrosion antifreeze-thaw mortar and preparation method thereof

A technology of anti-freeze-thaw and mortar, which is applied in the field of anti-corrosion freeze-thaw anti-freeze mortar and its preparation, and can solve the problems of freeze-thaw erosion, long ultraviolet irradiation time, destruction, etc.

Active Publication Date: 2020-06-05
内蒙古绰勒水利水电有限责任公司 +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the prior art, in the application of water conservancy projects, the concrete dam body needs to pass water for a long time, and severe freeze-thaw erosion occurs; there is a certain acid-base corrosion situation; there are acid mist, salt mist and other corrosive gases in the air from time to time. The fog causes persistent damage to the dam body; in addition, the ultraviolet radiation lasts for a long time, and the damage caused by wind, sand, rain and snow accumulates over time
The maintenance of water conservancy projects where various diseases gather together cannot be solved at all with traditional anti-corrosion mortar materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anticorrosion antifreeze-thaw mortar and preparation method thereof
  • A kind of anticorrosion antifreeze-thaw mortar and preparation method thereof
  • A kind of anticorrosion antifreeze-thaw mortar and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-4

[0083] The emulsion formula is: in terms of mass percentage, 20wt% of cationic neoprene latex, 20wt% of vinyl acetate-ethylene copolymer emulsion, and the rest is drinking water;

[0084] The powder formula is as follows in Table 9, and the specific preparation process is as follows: the powder and the emulsion are mixed and stirred at 300rpm at a mass ratio of 4:1 for 5 minutes to obtain a mortar product, wherein the particle size of the coarse sand is 1.5mm, and the mesh particle size of the fine sand is 20-100 Mesh, the length of the hollow fiber is 6mm.

[0085] Table 9 mortar powder formula (kg)

[0086] group cement fine sand coarse sand Superplasticizer expansion agent Defoamer HPMC DFM PP fiber hollow fiber Hydrophobic agent rubber powder Example 1 350 400 250 1 3 1 3 2 3 2 2 30 Example 2 300 500 100 2 8 2 2 1.4 1 1.5 1 50 Example 3 400 450 300 1.6 6 1.5 1 1.5 1.5 1 1.5 40 Example ...

Embodiment 5

[0088] The specific formula and preparation process are the same as in Example 4, except that among the PP fibers, the length of the PP fibers below 6 mm is 1 kg, and the length of the remaining PP fibers is 12 mm.

Embodiment 6

[0090] The specific formula and preparation process are the same as in Example 4, except that the particle size of the coarse sand is 1.2mm, the mesh particle size of the fine sand is 40-60 mesh, and the length of the hollow fiber is 5mm. Among the PP fibers, the length of the PP fibers below 5mm is 1.5kg, and the length of the remaining PP fibers is 13mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides an anti-corrosion and anti-freeze-thaw mortar, which is mainly composed of powder and emulsion with a mass ratio of (4-6): 1. The powder includes: in parts by mass, 300-400 parts of cement and 400-500 parts of coarse sand , 100-300 parts of fine sand, 1-2 parts of water reducer, 3-8 parts of expansion agent, 1-2 parts of defoamer, 1-3 parts of HPMC, 1-2 parts of starch ether, 1-2 parts of water repellent , 1-3 parts of polypropylene fiber, 1-2 parts of hollow fiber, 30-50 parts of rubber powder; the emulsion includes: by mass percentage, cationic neoprene emulsion 20-30%, vinyl acetate-ethylene copolymer emulsion 20-30 %, and the rest is drinking water. The preparation method comprises: after separately preparing the powder and the emulsion, stirring and mixing uniformly in a certain proportion. The anti-corrosion and anti-freeze-thaw mortar of the present invention has dual performances of anti-corrosion and anti-freeze and thaw, and is worthy of wide popularization and application.

Description

technical field [0001] The invention relates to the field of construction, in particular to an anti-corrosion anti-freeze-thaw mortar for construction and a preparation method thereof. Background technique [0002] Cement, powdery hydraulic inorganic gelling material. After adding water and stirring, it becomes a slurry, which can be hardened in the air or better hardened in water, and can firmly bind sand, stone and other materials together. In the early years the mixture of lime and volcanic ash is very similar to lime pozzolanic cement, use it to glue concrete which made of crushed stone. After hardening, the cement not only has high strength, but also can resist the erosion of fresh water or salt water. For a long time, as an important cementing material, it is widely used in civil engineering, water conservancy, national defense and other projects. [0003] However, due to the low compressive ratio, low compressive ratio of ordinary concrete, poor impermeability, crac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B24/26C04B111/20
CPCC04B24/2623C04B24/2682C04B28/00C04B2111/20C04B2201/10C04B2201/50C04B14/06C04B2103/302C04B2103/0068C04B2103/50C04B24/383C04B24/38C04B2103/65C04B16/0633C04B20/0048C04B22/002
Inventor 苏杰李国凡赵永胜李海康钱波张富春刘轶新
Owner 内蒙古绰勒水利水电有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products