Preparation method of shape memory fiber membrane with adjustable fiber surface micropore structure and application of drug release of membrane

A technology of memory fiber and microporous structure, which is applied in non-active ingredient medical preparations, drug delivery, pharmaceutical science, etc., can solve problems such as uncontrollable drug loading, achieve drug loading and drug release, and simple preparation process Effect

Active Publication Date: 2018-05-01
HARBIN INST OF TECH
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problems of uncontrollable drug release process and low drug loading capacity of existing drug-loaded materials, the present i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of shape memory fiber membrane with adjustable fiber surface micropore structure and application of drug release of membrane
  • Preparation method of shape memory fiber membrane with adjustable fiber surface micropore structure and application of drug release of membrane
  • Preparation method of shape memory fiber membrane with adjustable fiber surface micropore structure and application of drug release of membrane

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0037] Specific embodiment 1: The preparation method of the shape memory fiber membrane with the microporous structure of the adjustable fiber surface of this embodiment is carried out according to the following steps;

[0038] Dissolve the biodegradable polymer in an organic solvent, stir at room temperature until the polymer is completely dissolved to obtain a polymer solution; transfer the polymer solution into the syringe of the electrostatic spinning device, and use the electrostatic spinning device to transfer the polymer solution Electrospinning forming, to obtain a shape memory fiber membrane with adjustable fiber surface microporous structure;

[0039] The biodegradable polymer is a mixture of one or more of polylactic acid, polycaprolactone, and polyurethane in any ratio.

[0040] The diameter of the fiber in the shape memory fiber membrane with the microporous structure of the adjustable fiber surface obtained by the preparation method of this embodiment is 500nm-5μm; in t...

Example Embodiment

[0041] Specific embodiment two: this embodiment is different from specific embodiment one in that the organic solvent is dichloromethane, chloroform, N,N-dimethylformamide, and N,N-dimethylacetamide. One or more mixtures in any proportion. The other steps and parameters are the same as in the first embodiment.

Example Embodiment

[0042] Specific embodiment three: this embodiment is different from specific embodiment one or two in that the mass concentration of the polymer solution is 8-15%. The other steps and parameters are the same as in the first or second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a shape memory fiber membrane with an adjustable fiber surface micropore structure and an application of drug release of the membrane, relates to a preparation method of a shape memory fiber membrane and an application of the membrane, and aims to solve the problems that the drug release process of an existing drug loading material cannot be controlled, and drug loading capacity is low. The preparation method of the shape memory fiber membrane includes the steps: dissolving polymer in an organic solvent to obtain polymer solution; transferring the polymer solution into electrostatic spinning forming. A drug release method includes the steps: preparing the drug-loading shape memory fiber membrane with the adjustable fiber surface micropore structure; performing stretching treatment and drug blocking; taking shape memory recovery measures to the drug-blocked shape memory fiber membrane to perform shape memory recovery. The fiber surface ofthe fiber membrane prepared by an electrostatic spinning process is provided with the uniform micropore structure, the drug loading capacity is high, the size and the shape of the fiber surface micropore structure can be adjusted by heating treatment or ultrasonic treatment, and drug loading and drug release are realized.

Description

technical field [0001] The invention relates to a preparation method and application of a shape memory fiber membrane. Background technique [0002] As one of the smart polymers, shape memory polymers can realize sensing, driving and control, and change their shape under external excitation conditions. The main excitation methods include heat, electricity, light, magnetism, microwave, chemical solvents, etc. . Because of this characteristic, shape memory polymers are widely used in space expandable structures, biomedical devices, information carriers, smart clothes and other fields. With the demand of practical applications, micro-sized porous structure materials have received attention, especially in biomedical fields, such as drug release, cell culture, tissue engineering, etc. Electrospinning is a common method used to prepare shape memory polymer micro-nano fibers, which is characterized in that a variety of shape memory polymers can be prepared into fiber structures, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04H1/728D01F1/08A61L31/06A61L31/16A61L31/14A61K47/34
CPCA61K47/34A61L31/041A61L31/06A61L31/148A61L31/16A61L2300/602A61L2400/16D01F1/08D04H1/728
Inventor 张风华冷劲松刘彦菊王亚立
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap