a nanotio 2 In-situ hybrid antibacterial and waterproof coating treatment agent and preparation method thereof
A waterproof coating and coating treatment technology, applied in antifouling/underwater coatings, coatings, paints containing biocides, etc., can solve the problems of small size, easy deposition, easy volatilization, etc. Damage-reducing, non-volatile effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032] A kind of nano TiO 2 The preparation method of in-situ hybridization antibacterial waterproof coating treatment agent is characterized in that comprising the following steps:
[0033] Step (1) Prepare titanate alcohol solution: take 15 parts of butyl titanate and dissolve in 100 parts of anhydrous butanol solvent, stir evenly to obtain titanate alcohol solution;
[0034] Step (2) Prepare the acid catalyst solution: take 5 parts of glacial acetic acid and 20 parts of deionized water, stir evenly, add a small amount of hydrochloric acid dropwise, and adjust the pH value of the solution to 2-3;
[0035] Step (3) Prepare the alcohol solution of isooctyltrimethoxysilane: take 50 parts of silane coupling agent and dissolve in 40 parts of anhydrous butanol solvent, stir evenly to obtain the alcohol solution of silane coupling agent;
[0036] Step (4) Nano TiO 2 Sol preparation: under nitrogen protection and stirring, slowly add the acid catalyst solution prepared in step (2)...
Embodiment 2
[0039] A kind of nano TiO 2 The preparation method of in-situ hybridization antibacterial waterproof coating treatment agent is characterized in that comprising the following steps:
[0040] Step (1) Prepare titanate alcohol solution: take 15 parts of isopropyl titanate and dissolve in 100 parts of anhydrous butanol solvent, stir evenly to obtain titanate alcohol solution;
[0041] Step (2) Prepare the acid catalyst solution: take 5 parts of glacial acetic acid and 20 parts of deionized water, stir evenly, add a small amount of hydrochloric acid dropwise, and adjust the pH value of the solution to 2-3;
[0042] Step (3) Prepare the alcohol solution of isooctyltrimethoxysilane: take 50 parts of silane coupling agent and dissolve in 40 parts of anhydrous butanol solvent, stir evenly to obtain the alcohol solution of silane coupling agent;
[0043] Step (4) Nano TiO 2 Sol preparation: under nitrogen protection and stirring, slowly add the acid catalyst solution prepared in step...
Embodiment 3
[0046] A kind of nano TiO 2 The preparation method of in-situ hybridization antibacterial waterproof coating treatment agent is characterized in that comprising the following steps:
[0047] Step (1) Prepare titanate alcohol solution: take 15 parts of butyl titanate and dissolve in 100 parts of anhydrous butanol solvent, stir evenly to obtain titanate alcohol solution;
[0048] Step (2) Prepare the acid catalyst solution: take 5 parts of glacial acetic acid and 20 parts of deionized water, stir evenly, add a small amount of hydrochloric acid dropwise, and adjust the pH value of the solution to 2-3;
[0049] Step (3) Prepare the alcohol solution of isobutyltrimethoxysilane: take 50 parts of silane coupling agent and dissolve in 40 parts of anhydrous butanol solvent, stir evenly to obtain the alcohol solution of silane coupling agent;
[0050] Step (4) Nano TiO 2 Sol preparation: under nitrogen protection and stirring, slowly add the acid catalyst solution prepared in step (2)...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com