Flame-retardant smoke-suppression pipe material

A water pipe and smoke suppressant technology, applied in the field of water pipe materials, can solve problems such as the reduction of mechanical properties of water pipe materials, achieve good flame retardancy and smoke suppression performance, meet the pursuit of quality and safety performance

Inactive Publication Date: 2018-05-08
DENG QUAN PLASTIC TECH HUNAN CO LTD
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] This application provides a flame-retardant and smoke-suppressing water pipe material to solve the problem of adding existing flame-retardant and smoke-suppressing agents in the preparation of water pipes. Although it meets people's needs for flame-retardant and smoke-suppressing safety, it causes the mechanical properties of the water pipe material to decrease The problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A flame-retardant and smoke-suppressing water pipe material, which is composed of the following substances in parts by mass: 80 parts of polyvinyl chloride, 0.5 parts of lubricant, 5 parts of stabilizer, and 5 parts of flame-retardant and smoke-suppressing agent.

[0035] Flame retardant and smoke suppressant including palygorskite: 0.5 parts, Mg(OH) modified by silane coupling agent 2 : 1 part, nano-montmorillonite modified by silane coupling agent: 2 parts, nano-SiO modified by titanate coupling agent 2 : 1.5 servings.

[0036] Silane coupling agent accounts for Mg(OH) 2 The mass fraction of the silane coupling agent is 2.5%, the mass fraction of the nano-montmorillonite is 2.5%, and the titanate coupling agent accounts for the nano-SiO 2 The mass fraction is 2%.

[0037] Optionally, the stabilizer includes nanometer hydrotalcite and alkyl phosphite, the ratio of which is 3:1.

[0038] Optionally, the length of nano-montmorillonite is 50-150 nm, and nano-SiO 2 Th...

Embodiment 2

[0042] A flame-retardant and smoke-suppressing water pipe material, which is composed of the following substances in parts by mass: 85 parts of polyvinyl chloride, 0.9 parts of lubricant, 8 parts of stabilizer, and 10 parts of flame-retardant and smoke-suppressing agent.

[0043] Flame retardant and smoke suppressant include palygorskite: 1.5 parts, Mg(OH) modified by silane coupling agent 2 : 2 parts, nano-montmorillonite modified by silane coupling agent: 3 parts, nano-SiO modified by titanate coupling agent 2 : 2.5 servings.

[0044] Silane coupling agent accounts for Mg(OH) 2 The mass fraction of the silane coupling agent is 2.5%, the mass fraction of the nano-montmorillonite is 2.5%, and the titanate coupling agent accounts for the nano-SiO 2 The mass fraction is 2%.

[0045] Optionally, the stabilizer includes nano hydrotalcite and alkyl phosphite in a ratio of 3:1.

[0046] Optionally, the length of the nano-montmorillonite is 50-150 nm, and the nano-SiO 2 The diam...

Embodiment 3

[0050] A flame-retardant and smoke-suppressing water pipe material, which is composed of the following substances in parts by mass: 90 parts of polyvinyl chloride, 1.3 parts of lubricant, 11 parts of stabilizer, and 15 parts of flame-retardant and smoke-suppressing agent.

[0051] Flame retardant and smoke suppressant including palygorskite: 3 parts, Mg(OH) modified by silane coupling agent 2 : 3.5 parts, nano-montmorillonite modified by silane coupling agent: 4 parts, nano-SiO modified by titanate coupling agent 2 : 3.5 servings.

[0052] Silane coupling agent accounts for Mg(OH) 2 The mass fraction of the silane coupling agent is 2.5%, the mass fraction of the nano-montmorillonite is 2.5%, and the titanate coupling agent accounts for the nano-SiO 2 The mass fraction is 2%.

[0053] Optionally, the stabilizer includes nanometer hydrotalcite and alkyl phosphite, the ratio of which is 3:1.

[0054] Optionally, the length of nano-montmorillonite is 50-150 nm, and nano-SiO 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The application provides a flame-retardant smoke-suppression pipe material. The pipe material is prepared from, by mass, 80-100 parts of polyvinyl chloride, 0.5-2 parts of lubricant, 5-15 parts of stabilizer and 5-25 parts of flame retardant and smoke suppressant. The flame retardant and smoke suppressant includes 0.5-4 parts of palygorskite, 1-5 parts of a silane coupling agent modified Mg(OH)2,2-5.5 parts of a silane coupling agent modified nano montmorillonite and 1.5-5.5 parts of a titanate coupling agent modified Nano-SiO2; wherein the silane coupling agent accounts for 2.5% by mass of Mg (OH)2, the silane coupling agent accounts for 2.5% by mass of nano montmorillonite and the titanate coupling agent accounts for 2% by mass of nano-SiO2. Compared with existing flame retardants and anti smoke additives, the flame-retardant material is modified by organic modifier, the effect of flame retardants and smoke suppressants on mechanical properties of water pipe materials is reduced, atthe same time, synergistic flame retardancy among flame-retardant materials, makes the water pipe material have good flame retardancy and smoke suppression performance. Provided is a water pipe material with good flame retardant and smoke suppressing performance without reducing the mechanical properties of the pipe material.

Description

technical field [0001] The invention relates to the technical field of water pipe materials, in particular to a flame-retardant and smoke-suppressing water pipe material. Background technique [0002] Polyvinyl chloride (PVC) is the most widely used general-purpose plastic in the world. Due to the advantages of light weight, smooth surface, small resistance, large drainage, convenient installation, and low price, PVC drainage pipes are widely used in indoor drainage construction of residential buildings and public buildings. [0003] Although PVC is a self-extinguishing material, when a fire occurs, PVC will produce a large amount of black smoke and toxic gases, such as carbon monoxide, benzene aromatic compounds, etc., which will cause harm to the human body and even cause death by suffocation. Therefore, people have higher and higher requirements for the flame retardant and smoke suppression performance of PVC water pipes used in buildings. The usual method is to add flam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08K13/06C08K9/06C08K9/04C08K7/26C08K3/36C08K3/34C08K3/22
Inventor 邓权
Owner DENG QUAN PLASTIC TECH HUNAN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products