Black zirconia ceramic, black zirconia ceramic shell and preparation method thereof

A technology of black zirconia and zirconia ceramics, which is applied in the field of black zirconia ceramic shells and its preparation, and black zirconia ceramics, which can solve the problems of insufficient penetration depth and zero transmittance of the outer surface, so as to improve the appearance texture , improve the transmittance, beautify the appearance effect

Active Publication Date: 2021-03-09
BEIJING XIAOMI MOBILE SOFTWARE CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the black zirconia ceramics currently used in electronic equipment casings have basically zero transmittance in the visible light range, resulting in insufficient visual penetration depth on the outer surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Black zirconia ceramic, black zirconia ceramic shell and preparation method thereof
  • Black zirconia ceramic, black zirconia ceramic shell and preparation method thereof
  • Black zirconia ceramic, black zirconia ceramic shell and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0041] Reference will now be made in detail to the exemplary embodiments, examples of which are illustrated in the accompanying drawings. When the following description refers to the accompanying drawings, the same numerals in different drawings refer to the same or similar elements unless otherwise indicated. The implementations described in the following exemplary examples do not represent all implementations consistent with the present disclosure. Rather, they are merely examples of apparatuses and methods consistent with aspects of the present disclosure as recited in the appended claims.

[0042] The disclosure provides a black zirconia ceramic capable of improving the transparency of the black zirconia ceramic, a black zirconia ceramic shell and a preparation method thereof. The black zirconia ceramic, the black zirconia ceramic housing and the preparation method thereof of the present disclosure will be described in detail below with reference to the accompanying drawi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The disclosure relates to a black zirconia ceramic, a black zirconia ceramic shell and a preparation method thereof. A method for preparing black zirconia ceramics, comprising: providing a black zirconia ceramic substrate; preparing and forming an ion implantation layer on the first surface of the black zirconia ceramic substrate; preparing and forming an optical coating layer on the surface of the ion implantation layer to improve black The transmittance of the zirconia ceramic substrate in the visible light range is obtained to obtain black zirconia ceramics. In the present disclosure, by preparing an ion implantation layer on the surface of the black zirconia ceramic, the surface of the black zirconia ceramic can be strengthened, and an optical coating layer can be formed on the surface of the ion implantation layer, which can change the reflection and transmission characteristics of the black zirconia ceramic surface. Weaken or eliminate the gray-yellow phase of black zirconia ceramics, beautify the appearance of black zirconia ceramics, improve the transmittance of black zirconia ceramics in the visible light range, and improve the appearance and texture of black zirconia ceramics.

Description

technical field [0001] The disclosure relates to the technical field of shell processing, in particular to a black zirconia ceramic, a black zirconia ceramic shell and a preparation method thereof. Background technique [0002] Zirconia ceramics are a new type of ceramic material with many excellent properties such as wear resistance, corrosion resistance, high strength, high toughness, and good thermal stability. Compared with metals and plastics, zirconia ceramics have the characteristics of high Mohs hardness, high dielectric constant, no signal shielding and good biocompatibility, and have broad application prospects in smartphones and wearable devices, which makes zirconia Zirconium ceramics start from fingerprint identification cover and mobile phone back cover, and will gradually cut into the mobile terminal industry chain, becoming the third largest mobile phone back panel material after plastic and metal. [0003] Zirconia powder itself is a white powder, and the c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/80C04B41/87C04B41/89
CPCC04B41/0054C04B41/009C04B41/5035C04B41/5041C04B41/5042C04B41/5051C04B41/5066C04B41/52C04B41/80C04B41/87C04B41/89C04B35/48C04B41/4529C04B41/46C04B41/522
Inventor 刘兵孙坤肖志强
Owner BEIJING XIAOMI MOBILE SOFTWARE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap