Deplating liquid for glass surface membrane and use method and application of deplating liquid
A glass surface and stripping solution technology, applied in the field of materials, can solve problems such as glass corrosion and poor removal effect, and achieve the effects of low corrosion, good stripping effect and strong practicability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Examples
Embodiment 1
[0049] A kind of deplating solution of silicon oxide / silicon nitride film on glass surface is made up of following components by weight: potassium hydroxide 15%, diglycolamine 4%, anhydrous sodium metasilicate 6%, Disodium edetate 3%, alkyl glycoside APG 2%, the balance is water.
[0050]Fully immerse the touch screen glass coated with silicon oxide / silicon nitride in the above deplating solution, soak for 45 minutes at about 90°C, take it out, rinse it with water, and check that the film layer can be completely removed. There is slight corrosion on the glass surface, which needs to be polished in the next process.
Embodiment 2
[0052] A kind of deplating solution of silicon oxide / silicon nitride film on the surface of glass, consisting of the following components by weight: 10% sodium hydroxide, 8% triisopropanolamine, 3% sodium citrate, 5% borax %, tetrasodium edetate 2%, isooctyl ether phosphate 5%, and the balance is water.
[0053] Fully immerse the touch screen glass coated with silicon oxide / silicon nitride in the above deplating solution, soak for 60 minutes at 85°C, take it out, rinse it with water, and check that the film can be removed. The surface of the glass is slightly corroded, and it can be circulated according to the normal process after polishing.
Embodiment 3
[0055] A kind of deplating solution of silicon oxide / silicon nitride film on glass surface is made up of following components by weight: potassium hydroxide 5%, triethanolamine 8%, sodium silicate 3%, sodium tartrate 5%, Alkyl glucoside 2%, sodium dodecylbenzene sulfonate 2%, the balance is water.
[0056] Completely immerse the touch screen glass coated with silicon oxide / silicon nitride in the above stripping solution, soak for 30 minutes at 95°C, take it out, rinse it with water, and check that the film can be removed. The surface of the glass is slightly corroded, and it can be circulated according to the normal process after polishing.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap