A kind of preparation method of plate tile adhesive

A tile adhesive and plate-like technology, which is applied in the field of preparation of plate-like tile adhesives, can solve the problems of inconvenient use of tile adhesives and the like, and achieves a simple, fast, easy-to-operate laying process and saves a stirring step. Effect

Active Publication Date: 2020-12-01
FOSHAN DONGPENG CERAMIC +2
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The purpose of the present invention is to propose a preparation method of a plate-shaped tile adhesive, which solves the problem of inconvenient use of the tile adhesive in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of plate tile adhesive
  • A kind of preparation method of plate tile adhesive
  • A kind of preparation method of plate tile adhesive

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] A method for preparing a plate-like ceramic tile adhesive, comprising the steps of material preparation, mixing, pressing and drying, specifically as follows.

[0036] Material preparation: plastic solid waste is ball-milled and granulated with water to make plastic granules, and the moisture content of the plastic granules is 7-10%. The plastic particles with this moisture content are mixed with the binder and then pressed, which has a good molding effect and can ensure the stability of the binder, which is convenient for the storage of the adhesive for plate-shaped tiles and does not affect the adhesive effect of the binder.

[0037] Mixing: mix the plastic granules and the binder uniformly to obtain the mixture, and the weight ratio of the plastic granules to the binder is (0.5-1):2. The binder is powder, which can be fully mixed with plastic particles.

[0038] The plastic solid waste enables the plate-shaped tile adhesive to maintain a certain shape and have suffi...

Embodiment 1

[0058] A preparation method of a plate-shaped ceramic tile adhesive, comprising the following steps:

[0059] Material preparation: ball mill the plastic solid waste, add water and granulate to make plastic granules, and the moisture content of the plastic granules is 7%;

[0060] Mixing: Mix the plastic granules and the binder evenly to obtain the mixture. The weight ratio of the plastic granules to the binder is 1:2; the plastic granules and the binder are mixed with a dry powder mortar mixer for 30 minutes. The particle size of the plastic particles is 120 mesh.

[0061] Pressing: pressing the mixture into a plate-shaped green body; the pressing pressure is 30MPa.

[0062] Drying: The green body is dried to obtain a tile adhesive in the form of a plate.

[0063] The obtained tile adhesive has a compressive strength ≥ 1.2 MPa. The tile adhesive obtained had a thickness of 1 mm.

[0064] The plastic solid waste includes one or more of kaolin tailings, calcined shale and c...

Embodiment 2

[0068] A preparation method of a plate-shaped ceramic tile adhesive, comprising the following steps:

[0069] Material preparation: ball mill the plastic solid waste, add water and granulate to make plastic granules, the moisture content of the plastic granules is 8%;

[0070] Mixing: Mix the plastic granules and the binder evenly to obtain the mixture. The weight ratio of the plastic granules to the binder is 0.76:2; the plastic granules and the binder are mixed with a dry powder mortar mixer for 40 minutes. The particle size of the plastic particles is 100 mesh.

[0071] Pressing: pressing the mixture into a plate-shaped green body; the pressing pressure is 25MPa.

[0072] Drying: The green body is dried to obtain a tile adhesive in the form of a plate.

[0073] The obtained tile adhesive has a compressive strength ≥ 1.2 MPa. The thickness of the tile adhesive obtained was 2 mm.

[0074] The plastic solid waste includes one or more of kaolin tailings, calcined shale and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
thicknessaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a plate-shaped ceramic tile bonding agent. The method comprises the following steps of material preparation: performing ball milling on plastic solid waste; adding water; performing granulation so as to obtain plastic particles with the water content being 7 to 10 percent; mixing: uniformly mixing the plastic particles with bonding materials according to the weight ratio of (0.5 to 1):2 to obtain a mixture; pressing: pressing the mixture into the plate-shaped blank bodies; drying: drying the blank bodies to obtain the plate-shaped ceramic tile bonding agent. The plate-shaped ceramic tile bonding agent prepared by the steps has the advantages that the steps of the method are simple; the operation is easy. The ceramic tile bonding agent is madeinto the plate shape, and is used as required; the step of stirring before the use of the powdery ceramic tile bonding agent in the prior art is omitted; the fly dust caused by stirring is avoided; in addition, the time saving and labor saving effects are achieved during the ceramic tile laying. The plastic solid waste can be subjected to mixing pressing with the bonding material after the granulation; the stability of the bonding material is ensured; the storage of the ceramic tile bonding agent is convenient.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a method for preparing a plate-shaped ceramic tile adhesive. Background technique [0002] Existing ceramic tile adhesives are powdery, and must be mixed with water to form a paste before use. The current methods of laying tiles using powdered tile adhesives are: [0003] 1. First clean the back of the pre-selected tiles, and check the paste base surface; [0004] 2. According to the ratio agreed in advance, first pour the required clear water into the mixing container, and then slowly pour the tile adhesive powder into the mixing container; [0005] 3. Then use an electric mixer to stir until the paste-like mucilage is uniform and free of particles and precipitation. Let it stand for a few minutes and then stir slightly, then it can be used for tiling tiles; [0006] 4. Use a scraper to evenly scrape the glue on the base surface and the back of the tiles before til...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2111/00637C04B14/06C04B14/28C04B24/38C04B24/383C04B24/26
Inventor 钟保民徐瑜
Owner FOSHAN DONGPENG CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com