A kind of anti-oil pollution heat-sealing high barrier film

An anti-oil stain and high-resistance technology, applied in the direction of non-polymer organic compound adhesives, synthetic resin layered products, packaging, etc., can solve the problems of package damage, material waste, oil residue, etc., and achieve good oleophobic effect , prevent damage, easy to clean the effect

Active Publication Date: 2020-02-14
中塑新材料科技(杭州)有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When packaging packages with high temperature oil pollution in daily life, the high barrier film cannot be well sealed according to the package, and it is often placed for a long time during the processing process. After a long period of storage, High-temperature packaging causes shrinkage and damage of materials, resulting in waste of materials. At the same time, it is impossible to ventilate the high-temperature oil-stained packaging, which will cause damage to the packaging, and the packaging film will lose its shape during the lifting process. The packaging is antibacterially protected, and after a long period of storage, the organic matter in the oil stains will adhere to the film. When the oil stains are treated, there will be a large amount of oil stains on the film, so the film has to be disposed of. fall off, causing the film to be unrecyclable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-oil pollution heat-sealing high barrier film
  • A kind of anti-oil pollution heat-sealing high barrier film
  • A kind of anti-oil pollution heat-sealing high barrier film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] An oil-resistant heat-sealed high-barrier film, its structure is: PA1 / T1 / PP / T2 / PA2 / C / PA3 / T3 / PE1 / PE2 / PE3, PE3 is the outer layer in contact with the outside world during packaging, and PA1 is the outer layer of the packaging The inner layer that is in contact with the package, PP material is the auxiliary layer, C is the gas barrier layer, T1, T2, T3 are the adhesive layer, PA1, PA2, PA3 are the oil resistance layer, PE1, PE2, PE3 are the heat sealing layer barrier layer;

[0025] The gas barrier layer is mainly composed of the following components in parts by weight: 10 parts of ethylene-vinyl alcohol copolymer, 9 parts of polyvinyl alcohol, 11 parts of isocyanurate, 16 parts of 4-tert-butylbenzoic acid, polysilicon 6 parts of azane, 16 parts of methacrylamide;

[0026] The adhesive layer is mainly composed of the following components in parts by weight: 15 parts of ethylene-vinyl acetate copolymer, 16 parts of ethylhexyl acrylate, 9 parts of Weirong fiber, 19 parts of c...

Embodiment 2

[0038] The technical scheme of the present invention: an anti-oil pollution heat-sealed high barrier film, its structure is PA1 / T1 / PP / T2 / PA2 / C / PA3 / T3 / PE1 / PE2 / PE3, PE3 is the outer surface contacting with the outside world during packaging. PA1 is the inner layer in contact with the packaging during packaging, PP material is the auxiliary layer, C is the gas barrier layer, T1, T2, T3 are adhesive layers, PA1, PA2, PA3 are oil-resistant layers, PE1, PE2, PE3 is a heat-sealed high-resistance layer;

[0039] The gas barrier layer is mainly composed of the following components in parts by weight: 15 parts of ethylene-vinyl alcohol copolymer, 10 parts of polyvinyl alcohol, 12 parts of isocyanurate, 21 parts of 4-tert-butylbenzoic acid, polysilicon 10 parts of azane, 23 parts of methacrylamide;

[0040] The adhesive layer is mainly composed of the following components in parts by weight: 20 parts of ethylene-vinyl acetate copolymer, 19 parts of ethylhexyl acrylate, 10 parts of Weiro...

Embodiment 3

[0052] An anti-oil stain heat-sealed high barrier film, its structure is PA1 / T1 / PP / T2 / PA2 / C / PA3 / T3 / PE1 / PE2 / PE3, PE3 is the outer layer that contacts with the outside during packaging, and PA1 is the outer layer when packaging. For the inner layer in contact with the package, PP material is the auxiliary layer, C is the gas barrier layer, T1, T2, T3 are the adhesive layer, PA1, PA2, PA3 are the anti-oil layer, PE1, PE2, PE3 are heat-sealed high-resistance layers layer;

[0053]The gas barrier layer is mainly composed of the following components in parts by weight: 20 parts of ethylene-vinyl alcohol copolymer, 12 parts of polyvinyl alcohol, 15 parts of isocyanurate, 28 parts of 4-tert-butylbenzoic acid, polysilicon 14 parts of azane, 32 parts of methacrylamide;

[0054] The adhesive layer is mainly composed of the following components in parts by weight: 25 parts of ethylene-vinyl acetate copolymer, 22 parts of ethylhexyl acrylate, 12 parts of Weirong fiber, 28 parts of carboxy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an oil-pollution-resistant heat-sealing high-barrier thin film. The structure of the oil-pollution-resistant heat-sealing high-barrier thin film is PA1 / T1 / PP / T2 / PA2 / C / PA3 / T3 / PE1 / PE2 / PE3. The PE3 is an outer layer in contact with the outside during packaging. The PA1 is an inner layer in contact with a packaged object during packaging. The PP material is an auxiliary layer,and the C is a gas barrier layer. The T1, T2 and T3 are adhesive layers, the PA1, PA2 and PA3 are oil-pollution-resistant layers, and the PE1, PE2 and PE3 are heat-sealing high barrier layers. The auxiliary layer, the gas barrier layer, the adhesive layers and the oil-pollution-resistant layers are separately subjected to pretreatment to obtain pre-crystalline materials, and the pre-crystalline materials are subjected to transverse and longitudinal stretching, corona, static electricity removal, curing and winding treatment by a twin-screw extruder to obtain the high-barrier thin film. In a word, according to the process structure of the oil-pollution-resistant heat-sealing high-barrier thin film, the adhered oil pollution can be cleaned away, the influence of high temperature on the high-barrier thin film is prevented, and good bending strength is achieved; and the high-barrier thin film is subjected to sealing treatment, the structure is reasonable, and the recovery is facilitated.

Description

technical field [0001] The invention belongs to the technical field of packaging materials and specifically designs an oil-pollution-resistant heat-sealing high-resistance barrier film. Background technique [0002] With the rapid development of industrialization, high-barrier plastic packaging film is one of the fastest-growing functional films at present. High-barrier film refers to protecting the contents of the package. Strong polyolefin is extruded at the same time, and it is a film with a multi-layer structure. It is also a packaging film that prevents the contents of the package from seeping out. The high barrier property of the high barrier film refers to the high barrier property of the high barrier film means that under the standard state of 23 ℃ and 65% relative humidity, the permeation rate of oxygen is less than 5ml / m2 day, and the permeation rate of water vapor is less than 2g / m2·d. [0003] The packaging material industry is a large industry integrating mult...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/08
CPCB32B7/12B32B27/08B32B27/18B32B27/34B65D65/40B65D2565/381C08J5/18C08L23/06C08L33/26C08L77/00C08L2203/16C08L2205/035C09J4/06C08L23/0861C08L29/04C08L83/16C08L27/18C08L83/08C08L27/06C08K5/19C08K5/20C08L63/00C08L79/08
Inventor 杨世京
Owner 中塑新材料科技(杭州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com