Lithium ion battery and method of manufacturing

A lithium-ion battery, battery technology, applied in secondary battery manufacturing, electrolyte storage battery manufacturing, secondary battery, etc.

Active Publication Date: 2018-08-28
DREAMWEAVER INT
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, in the rechargeable battery industry, emphasis is placed on battery fabrication methods that are effective in providing sufficient voltage soak and current to provide sufficient electron transport and electrolyte deposition; currently, no such methods have been developed. method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium ion battery and method of manufacturing
  • Lithium ion battery and method of manufacturing
  • Lithium ion battery and method of manufacturing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0081] Dreamweaver Silver diaphragms were fabricated according to the method described in US Patent No. 8,936,878 (incorporated herein by reference). The example used in these trials was Dreamweaver Silver 25, which consisted of: EFTec A-010-04 nanofibrillated polyacrylonitrile fibers, EFTec L-010-04 nanofibrillated cellulose fibers, and polyethylene terephthalate Alcohol ester fiber, which has a length of 5 mm and a linear density of 0.3 denier per filament. The properties of this separator are shown in Table 2 below.

[0082] Table 2

[0083] Basement Membrane Properties

Units of measurement

Dreamweaver Silver TM 25

Thickness (12.6psi)

μm

27

Thickness (25psi)

μm

26

Gurley (JIS)

Second

80

porosity

％

56％

Aperture

μm

1.1

TD Shrinkage @160C

％

0

MD Shrinkage @160C

％

2

TD length

Kgf / cm 2

175

MD length

Kgf / cm 2

330

Young's modulu...

experiment example

[0090] Experimental example: battery manufacturer A

[0091] Production LiFePO4 electrodes were obtained from two manufacturers and tested in single-layer pouch cells sandwiched between two sheets of Plexiglas for uniform stress. Electrical properties other than self-discharge are very consistent across batteries and are otherwise reported more completely.

[0092] A single-layer contact cell (pouch cell) is made in a dimension of 50mm x 50mm. Electrodes (matched anode and cathode pairs) were commercially available from Chinese battery manufacturers. Fill the cell with a Li-ion battery electrolyte comprising 1 mole of LiPF in a 4:3:3 volumetric mixture of ethylene carbonate, dimethyl carbonate, and diethyl carbonate 6 . The battery was sealed into shape, and the procedure in Table 3 and Test parameters for testing. Use the following procedure to complete the test on a Neware battery tester.

[0093] The battery fabrication method included separator drying, cell assembl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

A method for producing a lithium ion battery is disclosed. The method comprises the steps of assembling a cell including an interior space comprising an anode, a cathode, and a separator; filling theinterior space of the cell with an electrolyte; connecting the anode and the cathode to a charging device; charging the cell at a rate less than or equal to C / 6 until the cell reaches a voltage capacity; and charging the cell at a voltage for greater than six hours. The invention further encompasses a method in which the voltage capacity is greater than or equal to 3.4 volts. The invention furtherencompasses a method in which the voltage is greater than 3.4 volts. The resultant batteries may comprise an efficient and properly formed solid electrolyte interface layer.

Description

technical field [0001] The present invention relates to a method of making a lithium-ion battery comprising an insulating (non-conducting) microporous polymer battery separator composed of a single layer of embedded microfibers and nanofibers. The overall fabrication method is efficient and produces a suitable solid electrolyte interface (SEI) layer on the anode of the battery. Methods of making the separator, methods of utilizing the separator in batteries, and methods of making a solid electrolyte interface layer are all encompassed by the present invention. Background technique [0002] Batteries have been used for electrical energy storage in remote locations and for portable applications for many years. Through the controllable movement of ions between the electrodes (anode and cathode), a power circuit is created, providing power that can be used until the excess ions in one electrode are depleted and no further power generation is possible. In recent years, recharge...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M2/16H01M10/04H01M10/0525H01M50/417H01M50/42H01M50/429H01M50/449H01M50/489
CPCH01M10/049H01M10/0525H01M10/446H01M50/449H01M50/44H01M50/42H01M50/429H01M50/417H01M50/489Y02E60/10Y02P70/50H01M10/058H01M50/411
Inventor 布莱恩·G·莫兰
Owner DREAMWEAVER INT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com