Machining technology of hair clipper blade

A processing technology and hair clipper technology, which is applied in the field of processing technology of hair clipper blades, can solve problems such as scratches on the outer surface of the blade, affecting blade sales and user experience, and achieve the effect of improving the use effect

Inactive Publication Date: 2018-10-12
海宁市兴达刀剪有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, during the production and processing of fixed blades on the market, there are relatively few processing procedures for the outer surface of the blade. Although the outer surface of the blade is polished smooth and bright through grinding and polishing, it is inevitable that the blade will be damaged during transportation or daily use. Rubbing with other items will easily cause scratches on the outer surface of the blade, which will affect the sales and use experience of the blade

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The invention provides a processing technology of a hair clipper blade, the method comprising the following steps:

[0024] A. Stamping: Use a punch to stamp the steel to form a blank for the blade; in this embodiment, the punch in step A uses a pressure of 90 tons for stamping.

[0025] B. Heat treatment: heat-treat the stamped billet through a mesh belt heat treatment furnace; in this embodiment, the mesh belt heat treatment furnace is used to quench the billet in step B, and then temper at high temperature; It is divided into five areas, and the quenching temperature is kept at 1050°C in the 1st-4th area of ​​quenching, and the temperature is maintained at 1060°C in the fifth area of ​​quenching; the high temperature tempering is carried out in three areas, and the temperature of each area is kept at 555°C.

[0026] C. Grinding the inclined surface: grinding the inclined surface of the embryo through a grinder after heat treatment;

[0027] D, chamfering: the edge ...

Embodiment 2

[0034] The invention provides a processing technology of a hair clipper blade, the method comprising the following steps:

[0035] A. Stamping: Use a punching machine to stamp the steel to form a blade blank;

[0036] B. Heat treatment: heat-treat the stamped blank through a mesh belt heat treatment furnace; in this embodiment, the punch press in step A uses a pressure of 110 tons for stamping; in this embodiment, a mesh belt type is used in step B The heat treatment furnace quenches the billet first, and then tempers at high temperature; the quenching is divided into five areas and carried out in sections, and the quenching temperature is kept at 1070 ° C in the first to fourth areas of quenching, and the temperature is maintained at 1070 ° C in the fifth area of ​​quenching ℃; high temperature tempering is carried out in three areas, and the temperature in each area is kept at 565 °C.

[0037] C. Grinding the inclined surface: grinding the inclined surface of the embryo thr...

Embodiment 3

[0045] The invention provides a processing technology of a hair clipper blade, the method comprising the following steps:

[0046] A. Stamping: Use a punch to stamp the steel to form a blade blank; in this embodiment, the punch in step A uses a pressure of 130 tons for stamping.

[0047] B. Heat treatment: heat-treat the stamped billet through a mesh belt heat treatment furnace; in this embodiment, the mesh belt heat treatment furnace is used to quench the billet in step B, and then temper at high temperature; It is divided into five areas, and the quenching temperature is kept at 1060°C in the 1st-4th area of ​​quenching, and the temperature is maintained at 1065°C in the fifth area of ​​quenching; the high temperature tempering is carried out in three areas, and the temperature of each area is Keep at 560°C; the mesh belt heat treatment furnace used in this example is a common mesh belt heat treatment furnace currently available on the market.

[0048] C. Grinding the incli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Roughnessaaaaaaaaaa
Login to View More

Abstract

The invention provides a machining technology of a hair clipper blade. The outer surface of the blade produced through the machining technology has the semigloss effect. The method comprises the stepsof A, punching, wherein a punching machine is used for punching steel, and a blade blank is formed; B, heat treatment, wherein the blank subjected to punching is subjected to heat treatment through amesh belt type heat treatment furnace; C, slope grinding, wherein the slope of the blank subjected to heat treatment is ground through a grinding machine; D, chamfering, wherein the edge of the ground blank is chamfered through an eddy type optical grinding machine via a triangular polishing block; E, outer surface grinding, wherein the outer surface of the chamfered blank is subjected to grinding through a hexagonal type rotation roller via cylindrical abrasive materials; F, smoothing, wherein the outer surface of the blank with the ground outer surface is subjected to grinding through the hexagonal type rotation roller via ceramic ball abrasive materials; and G, mirror surface polishing, wherein the front face and the reverse face of the blank subjected to smoothing are subjected to polishing through a plane polishing machine.

Description

technical field [0001] The invention belongs to the technical field of blade processing, and relates to a processing technology of a hair clipper blade. Background technique [0002] A hair clipper is a tool commonly used by barbers. The blade of a hair clipper is usually composed of a fixed fixed blade and a movable blade stacked on the fixed blade, and the movable blade can move back and forth to match The fixed blades are staggered to cut the hair. [0003] At present, during the production and processing of fixed blades on the market, there are relatively few processing procedures for the outer surface of the blade. Although the outer surface of the blade is polished smooth and bright through grinding and polishing, it is inevitable that the blade will be damaged during transportation or daily use. Rubbing with other items will easily cause scratches on the outer surface of the blade, which will affect the sales and use experience of the blade. Contents of the inventi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23P15/28B23P15/00
CPCB23P15/00B23P15/28
Inventor 张月兴李夏冰
Owner 海宁市兴达刀剪有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com