A kind of preparation method of terbium oxide with d50:2-3μm

A technology of terbium oxide and terbium chloride, applied in the preparation/treatment of rare earth metal compounds, lanthanide oxides/hydroxides, rare earth metal oxides/hydroxides, etc., can solve the problem of uneven particle size distribution of terbium oxide Uniformity, difficult particle control and other issues, to achieve good chemical properties and electronic properties, meet environmental protection requirements, and low energy consumption

Active Publication Date: 2020-12-01
CHANGZHOU GEOQUIN NANO NEW MATERIALS
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the technical defects of uneven terbium oxide particle size distribution and difficult particle control in the existing terbium oxide preparation technology, and provide a method for preparing terbium oxide with a D50:2-3 μm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] This specific embodiment adopts the following technical scheme to prepare terbium oxide powder: first weigh the refined oxalic acid (also known as oxalic acid dihydrate, molecular formula is C) with two crystal waters. 2 h 2 o 4 .2(H 2 0), molecular weight is 126.06, hereinafter the same) 12.8kg, puts into the oxalic acid solution that preparation concentration is 0.2mol / L in the retort, and retort selects ceramic reaction interlayer tank for use; Add the Polyethylene Glycol 20000 of 0.4kg, stir 0.5 hour Finally, drip concentration is 214L of terbium chloride aqueous solution of 0.2mol / L, add dropwise at a speed of 5L / min, leave standstill after the dropwise addition finishes and stir for 15min, add ice water circulation aging in the interlayer of ceramic reaction interlayer tank After 1 hour, the material mixture is obtained, and the temperature of the material in the reaction kettle is controlled to 0-5° C. by ice water circulation during the aging process. Then di...

Embodiment 2

[0018] This specific embodiment adopts the following technical scheme to prepare terbium oxide powder: first weigh 24kg of refined oxalic acid with two crystal waters, put it into a reaction tank to prepare an oxalic acid solution with a concentration of 0.4mol / L, and the reaction tank is a ceramic reaction interlayer tank Add the Polyethylene Glycol 20000 of 1.05kg, after stirring for 0.5 hours, dropwise concentration is 200L of terbium chloride solution of 0.4mol / L, add dropwise at a speed of 5L / min, leave standstill after the dropwise addition finishes and stir for 15min, After adding ice water to the interlayer of the ceramic reaction interlayer tank and aging for 4 hours, the material mixture is obtained. During the aging process, the temperature of the material in the reaction kettle is controlled to 0-5° C. by ice water circulation. Then discharge the material mixture into the suction filter barrel, drain the liquid in the material mixture, and then add pure water for wa...

Embodiment 3

[0020] This specific embodiment adopts the following technical scheme to prepare terbium oxide powder: first weigh 48kg of refined oxalic acid with two crystal waters, put it into a reaction tank to prepare an oxalic acid solution with a concentration of 0.3mol / L, and the reaction tank is equipped with a disk Tube ceramic reaction kettle; add 1.6kg of polyethylene glycol 1000, stir for 0.5 hours, then add dropwise 357L of terbium chloride aqueous solution with a concentration of 0.3mol / L, add dropwise at a speed of 4L / min, and stir after the dropwise addition After standing still for 25 minutes, ice water was added to the coil of the ceramic reactor and aged for 5 hours to obtain a material mixture. During the aging process, the temperature of the material in the reactor was controlled to 0-5°C by ice water circulation. Then discharge the material mixture into the suction filter barrel, drain the liquid in the material mixture, and then add pure water for washing. The temperatu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of terbium oxide with D50 being 2-3 microns. The preparation method concretely comprises the following steps of firstly, preparing an oxalic acid solution,adding polyethylene glycol 20000 with a set mass ratio, performing stirring until uniform dispersion, then slowly dropwise adding a terbium chloride solution with the concentration being 0.20.4mol / Lwhile performing stirring, performing ageing for 4-5 hours at 0-5 DEG C, then performing suction filtration and washing with the washing temperature being larger than 95 DEG C, performing dry filtering after washing to obtain precipitates, and searing the precipitates for 3-5 houses at 850-900 DEG C to prepare the terbium oxide with D50 being 2-3 microns. The prepared terbium oxide with a specificparticle size range can further improve some defects of some lithium iron phosphate materials and thus effectively improves the specific capacity, the cycling stability, the discharge rate and the like of a battery; and the terbium oxide with the particle size expresses better chemical performance and electronic performance in doping and improvement of lithium battery cathode materials.

Description

technical field [0001] The invention belongs to the technical field of rare earth compound ultrafine powder preparation, and in particular relates to a preparation method of terbium oxide with D50: 2-3 μm. Background technique [0002] As a functional material, terbium oxide is used to make metal terbium, magneto-optical glass, fluorescent powder, magneto-optic storage materials, chemical additives, etc., and can also be used to prepare functional ceramics. However, due to the scarcity and preciousness of terbium oxide, its application fields are limited. With the development of some industries, many excellent properties of terbium oxide have emerged. For example, in the lithium battery industry, the positive electrode material determines the performance of lithium batteries. At present, a new type of lithium iron phosphate material has attracted more and more attention, and the addition of terbium oxide has improved some defects of some lithium iron phosphate materials. Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01F17/224C01F17/10
CPCC01P2004/62C01P2006/80C01F17/206
Inventor 王鹭
Owner CHANGZHOU GEOQUIN NANO NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com