Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Glass gradient spraying technology, gradient ramp glass cover plate and electronic product

A gradient color and glass technology, applied in the direction of coating, etc., can solve the problems of poor color and gradient transition, poor gradient color appearance, orange lines or wrinkled surfaces, etc., to achieve smooth color gradient transition and glass gradient spraying process Stable and efficient results

Active Publication Date: 2018-11-23
LENS TECH CHANGSHA
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, every process in spraying will affect the spraying effect, resulting in uneven spraying, uneven surface after spraying, orange lines or wrinkles, poor gradient color appearance, poor color and gradient transition, and visual steps sense

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass gradient spraying technology, gradient ramp glass cover plate and electronic product
  • Glass gradient spraying technology, gradient ramp glass cover plate and electronic product
  • Glass gradient spraying technology, gradient ramp glass cover plate and electronic product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0109] A glass gradient spraying process, comprising the following steps:

[0110] Use nano translucent ink to spray the entire surface of each glass according to 7 parallel spraying paths, and then reduce the spraying area three times, and each glass reduces 2 spraying paths each time, so that each glass forms an ink layer with a gradient thickness After the spraying is completed, the ink is baked and back-baked in a tunnel oven to obtain a gradient glass;

[0111] Among them, the viscosity of nano translucent ink is 11Pa.s;

[0112] The distance between adjacent spraying paths is 14mm; the spray width range during spraying is 2cm, and the spraying height is 8cm;

[0113] The spraying speed during spraying is 600mm / s, the ink supply pressure is 200Pa, the atomization pressure is 300Pa, and the spray pressure is 350Pa;

[0114] The baking temperature is 80°C, and the baking time is 8 minutes; the back-baking temperature is 80°C, and the back-baking time is 30 minutes; the ba...

Embodiment 2

[0117] A glass gradient spraying process, comprising the following steps:

[0118] Use nano translucent ink to spray the entire surface of each glass according to 7 parallel spraying paths, and then reduce the spraying area three times. Each glass reduces 2 spraying paths each time, so that each glass forms a spraying thickness gradient, and the spraying is completed. Finally, the ink is baked and back-baked using a tunnel oven to obtain gradient glass;

[0119] Among them, the viscosity of nano translucent ink is 10Pa.s;

[0120] The distance between adjacent spraying paths is 15mm; the spray width range during spraying is 2.5cm, and the spraying height is 8.5cm;

[0121] The spraying speed during spraying is 500mm / s, the ink supply pressure is 180Pa, the atomization pressure is 300Pa, and the spray pressure is 320Pa;

[0122] The baking temperature is 75°C, and the baking time is 10 minutes; the back-baking temperature is 75°C, and the back-baking time is 35 minutes; the b...

Embodiment 3

[0125] A glass gradient spraying process, comprising the following steps:

[0126] Use nano-translucent ink to spray the entire surface according to 10 parallel spraying paths for each glass, and then reduce the spraying area three times. Each glass reduces 3 spraying paths each time, so that each glass forms a spraying thickness gradient, and the spraying is completed. Finally, the ink is baked and back-baked using a tunnel oven to obtain gradient glass;

[0127] Among them, the viscosity of nano translucent ink is 12Pa.s;

[0128] The distance between adjacent spraying paths is 16mm; the spray width range during spraying is 3cm, and the spraying height is 8cm;

[0129] When spraying, the spraying speed is 700mm / s, the ink supply pressure is 220Pa, the atomization pressure is 320Pa, and the spray pressure is 380Pa;

[0130] The baking temperature is 85°C, and the baking time is 6 minutes; the back-baking temperature is 85°C, and the back-baking time is 25 minutes; the bakin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a glass gradient spraying technology, a gradient ramp glass cover plate and an electronic product, and relates to the technical field of ink spraying. The glass gradient spraying technology comprises the following steps: firstly, using semitransparent ink to carry out whole-surface spraying according to a plurality of parallel spraying paths; then, gradually reducing a spraying area to form an ink layer with a changed thickness gradient, wherein the viscosity of the semitransparent ink is 8-18Pa.s, an interval between adjacent spraying paths is 14-18mm, a spraying swathrange during spraying is 2-3cm, spraying height is 7-10cm, and 1-3 spraying paths are reduced for each piece of glass each time when the spraying area is gradually reduced. According to the glass gradient spraying technology, a spraying process condition is optimized, the surface of the ink after spraying is smooth and flat and is free from orange stripes or wrinkled surfaces, a color gradient effect is good, transitivity and continuity are good, and no ladder feeling is in the presence.

Description

technical field [0001] The invention relates to the technical field of ink spraying, in particular to a glass gradient spraying process, a gradient glass cover plate and electronic products. Background technique [0002] At present, gradient colors have been widely used in daily life. With the development of the times, the public's perception and preferences of colors are also changing. Gradient colors are gradually being applied to various fields, including UI interfaces, brand logos, posters, illustrations, and fonts. [0003] With the development of smart phones, customers not only have higher and higher requirements for mobile phone functions, but also higher and higher requirements for the appearance of mobile phones. Gradient color slowly transitions from one color to another, which is a kind of infinite change Mysterious and romantic colors are increasingly used for smartphone back covers and watch cases, and are loved by consumers. [0004] The current gradient eff...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C17/00
CPCC03C17/002C03C17/006C03C2218/112
Inventor 周群飞管俊涛
Owner LENS TECH CHANGSHA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com