Preparation method and application of toughening operation gauze with ultrahigh water-absorbing quality
A technology of water absorption and operation, which is applied in the direction of spinning solution preparation, absorption pad, wet spinning method, etc., can solve the problems of weak absorption, psychological burden of patients, and occurrence of static electricity, and achieve improved use performance, good water absorption performance, and toughness high effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] (1) Mix polyacrylonitrile, sodium alginate, hydroxyethyl cellulose powder and deionized water according to the mass ratio of 2:1:5:23, and after ultrasonic dispersion treatment, fully stir to form a mixed spinning solution , the frequency of ultrasonic dispersion is 20kHz, the ultrasonic power is 200W, and the ultrasonic treatment time is 30 minutes, then the mixed spinning solution is centrifuged and left to stand overnight, and the precipitate in the mixed spinning solution is removed by filtration, and set aside;
[0023] (2) Carry out vacuum defoaming of the spinning solution, the vacuum degree of vacuum defoaming is -0.08MPa, and the defoaming time is 40 minutes, then add it to the wet spinning machine, measure it through the metering pump, and press it out from the spinneret Precipitate and form fiber filaments in coagulation bath, described coagulation bath is the mixed alcohol solution of dimethylacetamide, sodium sulfate, wherein the mol ratio of dimethylacetami...
Embodiment 2
[0029] (1) Mix polyacrylonitrile, sodium alginate, hydroxyethyl cellulose powder and deionized water according to the mass ratio of 2:1:5:23, and after ultrasonic dispersion treatment, fully stir to form a mixed spinning solution , the frequency of ultrasonic dispersion is 22.5kHz, the ultrasonic power is 250W, and the ultrasonic treatment time is 35 minutes, then the mixed spinning solution is centrifuged and left to stand overnight, and the precipitate in the mixed spinning solution is removed by filtration, and set aside;
[0030] (2) Carry out vacuum defoaming of the spinning solution, the vacuum degree of vacuum defoaming is -0.09MPa, and the defoaming time is 50 minutes, then add it to the wet spinning machine, measure it through the metering pump, and press it out from the spinneret Precipitate and form fiber filaments in coagulation bath, described coagulation bath is the mixed alcohol solution of dimethylacetamide, sodium sulfate, wherein the mol ratio of dimethylaceta...
Embodiment 3
[0036](1) Mix polyacrylonitrile, sodium alginate, hydroxyethyl cellulose powder and deionized water according to the mass ratio of 2:1:5:23, and after ultrasonic dispersion treatment, fully stir to form a mixed spinning solution , the frequency of ultrasonic dispersion is 25kHz, the ultrasonic power is 300W, and the ultrasonic treatment time is 40 minutes, then the mixed spinning solution is centrifuged and left to stand overnight, and the precipitate in the mixed spinning solution is removed by filtration, and set aside;
[0037] (2) Carry out vacuum defoaming of the spinning solution, the vacuum degree of vacuum defoaming is -0.1MPa, and the defoaming time is 60 minutes, then add it to the wet spinning machine, measure it through the metering pump, and press it out from the spinneret Precipitate and form fiber filaments in coagulation bath, described coagulation bath is the mixed alcohol solution of dimethylacetamide, sodium sulfate, wherein the mol ratio of dimethylacetamide...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap