A kind of preparation method of cotton-polyester double-sided gingham knitted fabric

A technology of knitted fabrics and gingham, applied in the field of textiles, can solve the problems of polyester with hard hand feeling, short service life, poor snag resistance, etc., and achieve soft hand feel, snag resistance up to standard, tear resistance and bursting powerful high effect

Active Publication Date: 2019-12-06
361 DEGREES CHINA
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Pure cotton woven fabrics are widely used because of their softness and comfort, but their tear strength and burst strength are relatively low, resulting in short service life and high loss rate. In the prior art, polyester is often used to replace them to solve the problem. The above problems, but polyester feels hard and has poor snag resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of cotton-polyester double-sided gingham knitted fabric
  • A kind of preparation method of cotton-polyester double-sided gingham knitted fabric
  • A kind of preparation method of cotton-polyester double-sided gingham knitted fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A kind of preparation method of cotton-polyester double-sided gingham knitted fabric, the raw material of this cotton-polyester double-sided gingham knitted fabric comprises compact spinning JC26S / 1 and polyester filament DTY 150D / 144F, comprising the following steps:

[0038] 1) Weaving: Send the above raw materials into the ordinary double-sided weft knitting large circular machine for weaving to obtain the gray cloth. The dial adopts ABABABAB, and the needle cylinder adopts AAABBBBB needle row. The triangular arrangement of the upper machine is as shown in the table and figure 1 Shown:

[0039]

[0040]

[0041] Among them, ∧ or ∨ means circle, ∩ or ∪ means tuck circle, - means floating line,

[0042] Specific threading method: Number of yarn feeding paths (1)~(6), (9), (12), (15), (18), (21), (24), (27), (30), ( 33) and (36) wear compact spinning JC26S / 1, wherein the thread length of yarn feeding channels (1)~(6) is 49.0cm / 100 needles, and the yarn feeding ch...

Embodiment 2

[0057] A kind of preparation method of cotton-polyester double-sided gingham knitted fabric, the raw material of this cotton-polyester double-sided gingham knitted fabric comprises compact spinning JC26S / 1 and polyester filament DTY 150D / 144F, comprising the following steps:

[0058] 1) Weaving: Send the above raw materials into the ordinary double-sided weft knitting large circular machine for weaving to obtain the gray cloth. The dial adopts ABABABAB, and the needle cylinder adopts AAABBBBB needle row. The triangular arrangement of the upper machine is as shown in the table and figure 1 Shown:

[0059]

[0060]

[0061] Among them, ∧ or ∨ means circle, ∩ or ∪ means tuck circle, - means floating line,

[0062] Specific threading method: Number of yarn feeding paths (1)~(6), (9), (12), (15), (18), (21), (24), (27), (30), ( 33) and (36) wear compact spinning JC26S / 1, wherein the thread length of yarn feeding channels (1) to (6) is 48.5cm / 100 needles, and the yarn feeding...

Embodiment 3

[0078] A kind of preparation method of cotton-polyester double-sided gingham knitted fabric, the raw material of this cotton-polyester double-sided gingham knitted fabric comprises compact spinning JC26S / 1 and polyester filament DTY 150D / 144F, comprising the following steps:

[0079] 1) Weaving: Send the above raw materials into the ordinary double-sided weft knitting large circular machine for weaving to obtain the gray cloth. The dial adopts ABABABAB, and the needle cylinder adopts AAABBBBB needle row. The triangular arrangement of the upper machine is as shown in the table and figure 1 Shown:

[0080]

[0081] Among them, ∧ or ∨ means circle, ∩ or ∪ means tuck circle, - means floating line,

[0082] Specific threading method: Number of yarn feeding paths (1)~(6), (9), (12), (15), (18), (21), (24), (27), (30), ( 33) and (36) wear compact spinning JC26S / 1, wherein the thread length of the yarn feeding paths (1) to (6) is 50.0cm / 100 needles, and the yarn feeding paths (9),...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a cotton polyester double-sided woven roving knitted fabric. The cotton polyester double-sided woven roving knitted fabric comprises compact-spun JC26S / 1 and polyester filaments DTY 150D / 144F. By means of special fabric design, a yarn threading mode and feeding parameter setting, small check structures are formed on fabric surfaces of fabrics produced through different combination of different polyester filaments, then dyeing and finishing are carried out, and the novel knitted fabric of a special structure is produced. The fabric obtained through the method is high in tearing resistance and bursting strength and soft in hand feeling, and the anti-snagging performance meets the standard.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a preparation method of a cotton-polyester double-sided checkered cloth knitted fabric. Background technique [0002] Pure cotton woven fabrics are widely used because of their softness and comfort, but their tear strength and burst strength are relatively low, resulting in short service life and high loss rate. In the prior art, polyester is often used to replace them to solve the problem. The above problems, but polyester feels hard and has poor snag resistance. Contents of the invention [0003] The purpose of the present invention is to overcome the defects of the prior art, and provide a method for preparing cotton-polyester double-sided gingham knitted fabric. [0004] Technical scheme of the present invention is as follows: [0005] A kind of preparation method of cotton-polyester double-sided gingham knitted fabric, the raw material of this cotton-polyest...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D04B1/16D04B1/14D04B1/10D06P1/16D06P1/44D06P5/10D06P3/54
CPCD04B1/102D04B1/14D04B1/16D06P1/16D06P1/445D06P3/54D06P5/10D10B2201/02D10B2331/04D10B2401/061D10B2401/063
Inventor 田友如李洋刘胜利
Owner 361 DEGREES CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap