Hierarchical porous EU-1 molecular sieve and preparation method thereof

An EU-1, molecular sieve technology, applied in molecular sieve catalysts, molecular sieves and base exchange compounds, chemical instruments and methods, etc., can solve the problems of fast catalytic reaction deactivation, low molecular diffusion efficiency, and poor hydrothermal stability. , to reduce the rate of dissolved silicon, retain the volume of micropores, and increase the volume of mesopores

Active Publication Date: 2018-12-25
CHINA CATALYST HLDG CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the problem of low molecular diffusion efficiency of reactants and poor hydrothermal stability on EU-1 molecular sieve, resulting in fast deactivation of catalytic reaction, and to provide a preparation method of multi-stage porous EU-1 molecular sieve material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hierarchical porous EU-1 molecular sieve and preparation method thereof
  • Hierarchical porous EU-1 molecular sieve and preparation method thereof
  • Hierarchical porous EU-1 molecular sieve and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The EU-1 molecular sieve in Comparative Example 1 was used as the original powder, and the original powder was placed in a mixed alkaline solution formed by 0.08mol / L NaOH and piperidine, and treated with alkali at room temperature for 10 minutes, and the solid-liquid mass ratio was 1:20. SiO in piperidine and EU-1 molecular sieve raw powder 2 The molar ratio is 0.02:1. Then add 0.2mol / L acetic acid to the system to adjust the pH to neutral, filter out the solid, wash the solid with deionized water until it is neutral, and then dry it at 120°C for 12 hours; place the dried solid in 0.5mol / L lemon The acid solution was refluxed at 120°C for 10 hours, and the solid-to-liquid mass ratio was 1:10; then the solid product was filtered out, and the solid product was deionized and washed to neutrality, and then dried at 120°C for 12 hours to obtain the hierarchically porous EU- 1 molecular sieve. figure 2 Explain that the obtained product is an EUO topological structure phas...

Embodiment 2-8

[0035] The preparation method of Examples 2-8 is basically the same as that of Example 1, the type of inorganic lye used, the type of piperidine compounds, the treatment time of molecular sieves in lye, the type of acid, the acid concentration, the mass ratio of solid to acid solution, and the reflux Each parameter such as temperature and time is different, as shown in table 1 and table 2; Nitrogen physical adsorption result shows, the sample that embodiment 1-8 obtains all contains mesopore structure, mesopore diameter distribution, average pore diameter and mesopore The pore volume is shown in Table 3:

[0036] Table 1

[0037]

[0038] Table 2

[0039]

[0040] *: product solid yield% = multi-level porous EU-1 molecular sieve product mass / initial EU-1 molecular sieve mass × 100%

[0041] table 3

[0042]

[0043]

[0044] It can be seen from Table 3 that the molecular sieves synthesized in the examples of the present invention have mesoporous structures of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
crystallinityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a hierarchical porous EU-1 molecular sieve and a preparation method thereof. The preparation method includes: putting EU-1 molecular sieve raw powder of 20-200 in silicon oxide / aluminum oxide molar ratio into an inorganic base and piperidine organic base compound mixed basic solution, treating at room temperature for 10-60min according to a solid / liquid mass ratio of 1:(10-50), adding acid to adjust pH value to neutral, filtering, washing, drying, subjecting a sample and an acid solution of 0.01-0.5mol in concentration according to a mass ratio of 1:(10-50) to backflowtreatment at 80-120 DEG C for 0.5-1.2h, filtering, washing, and drying to obtain the hierarchical porous EU-1 molecular sieve. The hierarchical porous EU-1 molecular sieve has good reaction moleculardispersion performance and has great application prospect when serving as a catalyst carrier.

Description

technical field [0001] The invention relates to a multi-stage porous EU-1 molecular sieve and a preparation method thereof, is a post-treatment method of the EU-1 molecular sieve, and belongs to the field of inorganic material synthesis. Background technique [0002] In the crystal structure of the EUO topological structure molecular sieve, there is a one-dimensional ten-membered ring 0.54nm×0.41nm channel in the [100] direction, and there are 0.81nm deep twelve-membered ring 0.68nm×0.58nm side pockets on both sides of the ten-membered ring channel. . EU-1, ZSM-50 and TPZ-3 molecular sieves all have EUO topology, among which EU-1 molecular sieve is a molecular sieve that has been widely studied in recent years. The bifunctional catalyst prepared by the acidic component of the structure catalyst shows good activity and selectivity in the catalytic reaction of C8 aromatics hydroisomerization and benzene isopropylation, and is known as a new generation of xylene isomerization ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B39/48B01J29/70
CPCB01J29/7023B01J2229/14C01B39/48C01P2002/72C01P2004/03C01P2006/12C01P2006/14C01P2006/16
Inventor 王志光李进
Owner CHINA CATALYST HLDG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap