Non-toxic antiseptic and mildewproof water-based coating and preparation and application method thereof

A water-based coating, anti-corrosion and mildew-proof technology, applied in the preparation of non-toxic anti-corrosion and anti-mildew water-based coatings, the application of non-toxic anti-corrosion and anti-mildew water-based coatings, in the field of non-toxic anti-corrosion and anti-mildew water-based coatings, it can solve the problems affecting the health of users. It is easy to produce a large amount of harmful substances, complex formulations of water-based coatings and other problems, to achieve the effects of reducing viscosity, adjusting volatilization speed, and reducing production costs

CN109096840AInactive Publication Date: 2018-12-28清远市承明新材料科技有限公司
1 Cites 1 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Publication Date
2018-12-28
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
Patent Text Reader

Abstract

The invention discloses a non-toxic antiseptic and mildewproof water-based coating and a preparation and application method thereof. The non-toxic antiseptic and mildewproof water-based coating includes, by weight parts, 100-130 parts of water-based resin, 2 parts of anti-mold agent, 5-10 parts of preservative, 2 parts of organosilicone flatting agent, 2-8 parts of surfactant, 30-40 parts of waterand 20-30 parts of pigment, wherein the pigment comprises, by weight parts, 20-30 parts of lead chrome yellow, 10-15 parts of iron yellow, 18-25 parts of lead silicate chromate, 10-15 parts of (strontium-calcium) chrome yellow, 8-10 parts of transparent yellow, 2-10 parts of benzidine yellow, 1-8 parts of Hansha yellow and 5-7 parts of lemon yellow. The preparation method includes step S1 of weighing the raw materials in proportion, step S2 of obtaining a first mixture by mixing, step S3 of obtaining a second mixture by mixing, and step S4 of adding a surfactant at a ratio to obtain a finished product. The non-toxic antiseptic and mildewproof water-based coating is applied to architectural interior wall decorative coatings and exterior wall waterproof coatings. Application fields are widewhile a production process is simple, the production cost is greatly reduced, no toxic substance is generated in the product production and using process, and the non-toxic antiseptic and mildewproofwater-based coating can also play the role of anticorrosion and mildew prevention.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to the field of water-based coatings, in particular to a non-toxic, anti-corrosion and mildew-proof water-based coating.

[0002] The invention relates to the field of water-based paint, in particular to a preparation method of a non-toxic, anti-corrosion and mildew-proof water-based paint.

[0003] The invention relates to the field of water-based paint, in particular to an application method of a non-toxic, anti-corrosion and mildew-proof water-based paint. Background technique

[0004] Water-based coatings usually refer to coatings that use water as a solvent or as a dispersion medium. Water-based coatings have emerged in recent years, and their environmental protection is much higher than that of paint.

[0005] In the Chinese invention patent application publication specification CN107353733A, a non-toxic and environmentally friendly water-based paint and its preparation method are disclosed, including the following componen...

Examples

Embodiment 1

[0025] The invention provides a technical solution: a non-toxic, anti-corrosion and mildew-proof water-based coating, comprising the following components by weight: 100-130 parts of water-based resin, 2 parts of anti-mold agent, 5-10 parts of preservative, and 2 parts of silicone leveling agent 2-8 parts of surfactant, 30-40 parts of water, 20-30 parts of pigment.

[0026] The pigments include the following components by weight: 20-30 parts of lead chrome yellow, 10-15 parts of iron yellow, 18-25 parts of lead silicochromate, 10-15 parts of strontium calcium yellow, 8-10 parts of transparent yellow, 2 parts of benzidine yellow -10 parts, Hansa yellow 1-8 parts, lemon yellow 5-7 parts.

[0027] A preparation method of a non-toxic, anti-corrosion and mildew-proof water-based paint, comprising the following steps:

[0028] S1: Weigh the ratio, weigh all the required raw materials, and store them for use. The ratio is as follows: 100-130 parts of water-based resin, 2 parts of ant...

Embodiment 2

[0034] The invention provides a technical solution: a non-toxic, anti-corrosion and mildew-proof water-based coating, comprising the following components by weight: 100-130 parts of water-based resin, 2 parts of anti-mold agent, 5-10 parts of preservative, and 2 parts of silicone leveling agent 2-8 parts of surfactant, 30-40 parts of water, 20-30 parts of pigment.

[0035] The pigments include the following components by weight: 20-30 parts of lead chrome yellow, 10-15 parts of iron yellow, 18-25 parts of lead silicochromate, 10-15 parts of strontium calcium yellow, 8-10 parts of transparent yellow, 2 parts of benzidine yellow -10 parts, Hansa yellow 1-8 parts, lemon yellow 5-7 parts.

[0036] A preparation method of a non-toxic, anti-corrosion and mildew-proof water-based paint, comprising the following steps:

[0037] S1: Weigh the ratio, weigh all the required raw materials, and store them for use. The ratio is as follows: 100-130 parts of water-based resin, 2 parts of ant...