Fireproof pot clay, and preparation method thereof

A refractory and mud material technology, applied in the field of refractory pot mud and its preparation, can solve problems such as poor plasticity of refractory pot mud, and achieve the effect of matching bright colors and high heat resistance index

Inactive Publication Date: 2019-01-11
HUNAN EKA CERAMICS
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, refractory pot mud is a kind of heat-resistant soil with a white body after firing. It can be used as refractory pot pots and porcelain for microwave ovens without bursting. However, refractory pot mud on the existing market has poor plasticity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of refractory pot mud, the components contained in the mud used in it and the mass parts of each component are as follows:

[0020] 10 parts cordierite,

[0021] 15 parts of phyllophyllite,

[0022] 7.5 parts of black stone powder,

[0023] 35 parts of black slime,

[0024] 2.5 parts raw talcum powder,

[0025] Spodumene 5 parts,

[0026] 0.4 parts of fairy water.

[0027] The preparation method of the refractory pot mud, the steps of the method include:

[0028] S1: Prepare materials according to each component and the mass parts of each component;

[0029] S2: According to the mass ratio of ball: water: material = 1.5:0.25:1, wet ball mill for 15 hours, then pass through a 120 mesh screen, and then adjust to a slurry with a concentration of 57-60 Baume;

[0030] S3: After the mud is sunken and rotted, it is cast into shape and fired at a kiln temperature of 1160-1200°C to obtain a finished product.

Embodiment 2

[0032] A kind of refractory pot mud, the components contained in the mud used in it and the mass parts of each component are as follows:

[0033] 15 parts cordierite,

[0034] 20 parts of phyllophyll,

[0035] 10 parts black stone powder,

[0036] 50 parts of black slime,

[0037] 3.5 parts of raw talcum powder,

[0038] 7 parts of spodumene,

[0039] 0.6 parts of fairy water.

[0040] The preparation method of the refractory pot mud, the steps of the method include:

[0041] S1: Prepare materials according to each component and the mass parts of each component;

[0042] S2: According to the mass ratio of ball: water: material = 1.5:0.25:1, wet ball mill for 18 hours, then pass through a 120 mesh screen, and then adjust to a slurry with a concentration of 57-60 Baume;

[0043] S3: After the mud is sunken and rotted, it is cast into shape and fired at a kiln temperature of 1160-1200°C to obtain a finished product.

Embodiment 3

[0045] A kind of refractory pot mud, the components contained in the mud used in it and the mass parts of each component are as follows:

[0046] 12 parts cordierite,

[0047] 16 parts of phyllophyll,

[0048] 8 parts black stone powder,

[0049] 45 parts of black slime,

[0050] 3 parts raw talcum powder,

[0051] 6 parts of spodumene,

[0052] 0.5 parts of fairy water.

[0053] The preparation method of the refractory pot mud, the steps of the method include:

[0054] S1: Prepare materials according to each component and the mass parts of each component;

[0055] S2: According to the mass ratio of ball: water: material = 1.5:0.25:1, wet ball mill for 16 hours, then pass through a 120 mesh screen, and then adjust to a slurry with a concentration of 57-60 Baume;

[0056] S3: After the mud is sunken and rotted, it is cast into shape and fired at a kiln temperature of 1160-1200°C to obtain a finished product.

[0057] The fairy water in the above three examples is Americ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fireproof pot clay, and a preparation method thereof. The fireproof pot clay comprises, by mass, 10 to 15 parts of iolite, 15 to 20 parts of petalite, 7.5 to 10 parts of black stone powder, 35 to 50 parts of black slime, 2.5 to 3.5 parts of raw talcum powder, 5 to 7 parts of spodumene, and 0.4 to 0.6 part of ACUMER 9300. The fireproof pot clay is subjected to high temperature sintering, obtained blank is white, color is bright, the heatproof index is higher than that of common fireproof pot clay, 300 to 400 DEG C quenching-rapid heating test requirements are satisfied, and no cracking is caused.

Description

technical field [0001] The invention relates to a refractory pot mud and a preparation method thereof. Background technique [0002] At present, refractory pot mud is a kind of heat-resistant soil with a white green body after firing, which can be used as refractory pot pot and porcelain for microwave ovens without bursting, but the plasticity of refractory pot mud on the existing market is not good. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the defects of the prior art and provide a kind of refractory clay pot, which is fired at high temperature, the green body is white, and the matching color is bright. 400°C rapid cooling and rapid heating performance test, no bursting. [0004] In order to solve the problems of the technologies described above, the technical solution of the present invention is: a kind of refractory pot mud, the mass parts of the component that its used mud material contains and each ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
CPCC04B35/66C04B2235/3463C04B2235/3472C04B2235/3481C04B2235/349
Inventor 谢泉英
Owner HUNAN EKA CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap