Water-based intumescent flame-retardant paint based on modified boron nitride and preparation method thereof

A technology of fire retardant coating and boron nitride, applied in the direction of fire retardant coating, coating, etc., can solve the problem that the performance of water-based intumescent fire retardant coating is not good enough, and achieve excellent antifouling performance, good compatibility, high efficiency fire resistance and flame retardant performance Effect

Inactive Publication Date: 2019-03-01
WUHAN INSTITUTE OF TECHNOLOGY
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the above-mentioned deficiencies existing in the existing boron nitride modification method and the problems that the performance of the existing water-based intumescent fireproof coating is not good enough, and provide a new boron nitride stripping modification method and apply it to water-based intumescent fire retardant coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based intumescent flame-retardant paint based on modified boron nitride and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A water-based intumescent fireproof coating based on modified boron nitride, its composition is as follows (mass percentage): 2% of modified boron nitride, 36% of ammonium polyphosphate, 17% of pentaerythritol, 12% of melamine, water-based styrene-acrylic core-shell Emulsion 20%, hydroxyethyl cellulose 0.5%, dispersant 0.5%, defoamer 0.5%, n-octanol 0.5%, water 11%.

[0032] The preparation method of the water-based intumescent fireproof coating is as follows: prepare materials according to the above-mentioned ratio; mix and grind the weighed ammonium polyphosphate, pentaerythritol, melamine, and modified boron nitride into powder, then add water and continue to grind to make it evenly mixed , then add hydroxyethyl cellulose, defoamer and dispersant to continue grinding, and finally add water-based styrene-acrylic core-shell emulsion and n-octanol, grind thoroughly for the third time and mix well.

Embodiment 2

[0034] A water-based intumescent fireproof coating based on modified boron nitride, its composition is as follows (mass percentage): 6% of modified boron nitride, 34% of ammonium polyphosphate, 13% of pentaerythritol, 12% of melamine, water-based styrene-acrylic core-shell Emulsion 20%, hydroxyethyl cellulose 0.5%, dispersant 0.5%, defoamer 0.5%, n-octanol 0.5%, water 13%. The preparation method of the water-based intumescent fireproof coating is the same as that of Example 1.

Embodiment 3

[0036] A water-based intumescent fireproof coating based on modified boron nitride, its composition is as follows (mass percentage): 10% of modified boron nitride, 30% of ammonium polyphosphate, 12% of pentaerythritol, 11% of melamine, water-based styrene-acrylic core-shell Emulsion 20%, hydroxyethyl cellulose 0.5%, dispersant 0.5%, defoamer 0.5%, n-octanol 0.5%, water 15%. The preparation method of the water-based intumescent fireproof coating is the same as that of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to water-based intumescent flame-retardant paint based on modified boron nitride and a preparation method thereof. Firstly, by means of isopropanol liquid-phase mechanical ball milling and N,N-dimethylformamide assistant ultrasound, hexagonal boron nitride is exfoliated, and then the exfoliated boron nitride, water-based styrene-acrylic core-shell emulsion, ammonium polyphosphate, pentaerythritol, melamine, hydroxyethyl cellulose, a defoaming agent, a dispersion agent and water are prepared into the water-based intumescent flame-retardant paint according to a certain ratio. An intumescent carbon layer formed by the flame-retardant paint at high temperatures is compact and firm, the water-based intumescent flame-retardant paint based on the modified boron nitride has efficient flame-retardant performance, the preparation method thereof is simple, the film-forming performance is excellent, and water-based environment-friendliness is achieved.

Description

technical field [0001] The invention relates to the technical field of coatings and fireproof materials, in particular to a water-based intumescent fireproof coating based on modified boron nitride and a preparation method thereof. Background technique [0002] Water-based intumescent fire-resistant coatings are widely used in fire protection in various industries due to their advantages of thin coating thickness, convenient construction, good decoration, and water-based environmental protection. Common intumescent fireproof coatings will release a lot of heat during thermal expansion and foaming, which seriously endangers people's life and health. As a member of two-dimensional nanomaterials, hexagonal boron nitride is a honeycomb layered material composed of boron atoms and nitrogen atoms in sp2 hybridization. Due to the polar boron-nitrogen bond between layers, hexagonal boron nitride (hBN) has the advantages of excellent high temperature resistance, thermal stability, h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D5/18C09D7/63
CPCC08K2003/323C08K2003/385C08L2201/02C08L2201/22C09D5/185C09D7/63C09D125/14C08L1/284C08K13/06C08K9/00C08K3/38C08K3/32C08K5/053C08K5/34922
Inventor 刘治田刘诗胡清华王成张旗
Owner WUHAN INSTITUTE OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap