Brown master batch and preparation process thereof

A masterbatch, brown technology, applied in the field of brown masterbatch and its preparation, can solve problems such as color inconsistency, achieve high light resistance, obvious advantages, and solve the effect of metamerism

Active Publication Date: 2019-04-05
上海晋升塑料科技有限公司
View PDF13 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a brown masterbatch, which can solve the problem that the color of the product in the automobile industry is inconsistent with the color of the standard sample under different light sources. For this reason, the present invention also provides a brown masterbatch Granule preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Brown master batch and preparation process thereof
  • Brown master batch and preparation process thereof
  • Brown master batch and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A brown masterbatch, including the following components:

[0022]

[0023] Its preparation method is as follows:

[0024] Step 1, mix the carrier resin, plastic additives, dispersant, titanium dioxide, iron oxide red, bismuth vanadate yellow, titanium yellow, and carbon black in a high-speed mixer after proportioning;

[0025] Step 2, melt and extrude the raw materials obtained in step 1 in the extruder, after cooling, enter the pelletizer to granulate to obtain granular bodies; the extruder is a twin-screw extruder, and the twin-screw extruder The temperature is 180°C, and the speed is 400r / min;

[0026] Step 3, cooling and drying the granules obtained in Step 2 to obtain brown masterbatch.

[0027] The brown masterbatch of embodiment 1 is added in the plastic, and the prepared plastic is compared with the standard sample:

[0028] Standard sample: BMW Group, the color number is the standard color of Mocha.

[0029] Sample 1: Plastics added with the brown master...

Embodiment 2

[0033] A brown masterbatch, including the following components:

[0034]

[0035] Its preparation method is as follows:

[0036] Step 1, mix the carrier resin, plastic additives, dispersant, titanium dioxide, iron oxide red, bismuth vanadate yellow, titanium yellow, and carbon black in a high-speed mixer after proportioning;

[0037] Step 2, melt and extrude the raw materials obtained in step 1 in the extruder, after cooling, enter the pelletizer to granulate to obtain granular bodies; the extruder is a twin-screw extruder, and the twin-screw extruder The temperature is 180°C, and the speed is 400r / min;

[0038] Step 3, cooling and drying the granules obtained in Step 2 to obtain brown masterbatch.

[0039] The brown masterbatch of embodiment 2 is added in the plastic, and the plastic that makes compares with standard sample:

[0040] Standard sample: BMW Group, the color number is the standard color of Mocha.

[0041] Sample 2: Plastics added with the brown masterbatch...

Embodiment 3

[0045] A brown masterbatch, including the following components:

[0046]

[0047] Its preparation method is as follows:

[0048] Step 1, mix the carrier resin, plastic additives, dispersant, titanium dioxide, iron oxide red, bismuth vanadate yellow, titanium yellow, and carbon black in a high-speed mixer after proportioning;

[0049] Step 2, melt and extrude the raw materials obtained in step 1 in the extruder, after cooling, enter the pelletizer to granulate to obtain granular bodies; the extruder is a twin-screw extruder, and the twin-screw extruder The temperature is 180°C, and the speed is 400r / min;

[0050] Step 3, cooling and drying the granules obtained in Step 2 to obtain brown masterbatch.

[0051] The brown masterbatch of embodiment 3 is added in the plastic, and the plastic prepared is compared with the standard sample:

[0052] Standard sample: BMW Group, the color number is the standard color of Mocha.

[0053] Sample 3: Plastics added with the brown master...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses brown master batch, which comprises the following components in parts by weight: 26.8-30.4 parts of carrier resins, 0.8-1.2 parts of plastic additives, 9.8-10.2 parts of dispersants, 6.0-6.4 parts of titanium dioxide, 8.8-9.2 parts of iron oxide red, 5.8-6.2 parts of bismuth vanadate yellow, 35.9-37.1 parts of titanium yellow and 2.5-2.9 parts of carbon black. The brown master batch is safe and environment-friendly, the color of the product prepared by adding the brown master batch to the plastic is completely consistent with that of the target sample under different light source conditions, and thus the problem of metamerism between the product and the target sample is effectively solved; 99% of the color developing substances in the brown master batch adopt inorganic toner, compared with organic toner, the inorganic toner has higher light resistance, light resistance and corrosion resistance, and has obvious advantages in the automobile industry.

Description

technical field [0001] The invention relates to the technical field of plastic processing and color matching, in particular to a brown masterbatch and a preparation process thereof. Background technique [0002] Cars will encounter different lighting environments during use. Therefore, in the process of making plastic parts for cars, it is necessary to ensure that the color of the product is consistent with the color of the standard sample under different light conditions. There are three internal regulations in the automotive industry. Common light sources, namely D65, A and F11, the overall level of color matching in the existing plastic dyeing industry is insufficient, and it is basically impossible to ensure color uniformity under different light sources, resulting in the result that the color of the product is inconsistent with the color of the standard sample under different light sources problem, namely metamerism. For example, the overall color under natural light (...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L75/04C08L23/06C08K13/06C08K3/22C08K3/04C08K9/10C08K3/24C08J3/22
CPCC08J3/226C08J2475/04C08K3/04C08K3/24C08K2201/011C08K9/10C08K13/06C08K2003/2241
Inventor 顾鸿章郑有家
Owner 上海晋升塑料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More