A kind of acid and alkali resistant chemically modified PET composite material and preparation method thereof

A technology of chemical modification and composite material, applied in the field of chemically modified PET composite material and its preparation, can solve the problems of difficult to achieve miscibility, poor thermodynamic compatibility, unstable performance, etc., to meet mechanical properties, improve compatibility, etc. The effect of improving the stability of acid and alkali resistance

Active Publication Date: 2020-11-10
宁波力达得为高分子科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, if the structure of the modified filler and the masterbatch is quite different, the thermodynamic compatibility is poor, and it is difficult to achieve engineering miscibility, especially as the time after the blending operation is completed, the phase separation phenomenon becomes more obvious, resulting in poor performance. instability and deterioration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of acid and alkali resistant chemically modified PET composite material and preparation method thereof
  • A kind of acid and alkali resistant chemically modified PET composite material and preparation method thereof
  • A kind of acid and alkali resistant chemically modified PET composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035]In order to further understand the content of the present invention, the present invention will be described in detail below in conjunction with specific examples. Unless otherwise specified, the reagents, methods and equipment used in the present invention are conventional reagents, methods and equipment in the technical field.

[0036] General synthesis method of modified PET resin:

[0037] The preparation of the modified PET resin is obtained by polycondensation of terephthalic acid (TPA) and a diol mixture, and the diol mixture is ethylene glycol (EG) with a molar ratio of 1:0.1-0.3:0.03-0.15, The mixture of propoxylated bisphenol A (D33) and neopentyl glycol (NPG), the proportioning of terephthalic acid and dibasic alcohol is that dibasic alcohol is in excess of 20%-30% according to the stoichiometric ratio; and in polycondensation After the reaction is finished, add a certain amount of diphenylmethane diisocyanate (MDI) for end-capping treatment, and then cool ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to view more

Abstract

The invention provides an acid-and-alkali-resistant chemically modified PET composite material. The material is characterized by comprising, by weight, 65-75 parts of modified PET resin, 6-9 parts ofstearic acid modified glass fiber, 3-5 parts of a crystallization promoter, 3-5 parts of a chain repairing agent, 1-1.5 parts of an antioxidant, 0.5-1 part of a nucleating agent and 0.3-0.8 part of lubricant. The modified PET resin is obtained through polycondensation of p-phthalic acid (TPA) and a dihydric alcohol mixture, and the dihydric alcohol mixture is a mixture of ethylene glycol (EG), propoxy bisphenol A (D33) and neopentyl glycol (NPG). The stearic acid modified glass fiber is prepared by grafting stearic acid groups on glass fiber. The chemically modified PET composite material is good in mechanical property, high in transparency and excellent in acid and alkali resistance; after the material is soaked in 5 wt% HCl and NaOH for 30 days, good mechanical property intensity can still be maintained, a preparation method is simple, the raw materials are easy to obtain, and the material is suitable for industrial production.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an acid and alkali resistant chemically modified PET composite material and a preparation method thereof. Background technique [0002] Polyethylene terephthalate (PET) has excellent comprehensive performance and low price. There are rigid groups on the main molecular chain and the molecular chain has a high degree of symmetry. Its physical and mechanical properties, heat resistance, electrical properties and composition It is a kind of mature and industrialized thermoplastic resin, which is widely used in engineering plastics, fiber textile and film industry; especially in the application of engineering plastics, compared with other traditional engineering plastics, such as Polyamide (PA), polycarbonate (PC), etc. have extremely high cost performance, so they are extremely competitive. [0003] Since the pH of the environment may change during the use of engineering p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08L71/02C08K13/06C08K9/04C08K9/06C08K7/14C08G63/672C08G63/91
CPCC08G63/672C08G63/916C08L67/02C08L71/02C08K13/06C08K9/04C08K9/06C08K7/14
Inventor 王鑫
Owner 宁波力达得为高分子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap