Glass bottle capable of resisting 1300 DEG C and being not deformed during high temperature flame polishing, and preparation method thereof

A technology of glass bottle and fire throwing, which is applied in the field of glass bottle and its preparation, which can solve the problems of affecting quality, unacceptable high temperature, poor surface treatment effect, etc., and achieve the effect of avoiding unprocessable and good effect

Active Publication Date: 2019-05-07
浙江晶华玻璃有限公司
View PDF14 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a glass bottle that can withstand high temperature of 1300 degrees Celsius without being deformed by fire throwing and its preparation method, so as to solve the problem that the original glass bottle proposed in the above background technology cannot accept higher temperature during heat treatment, resulting in The surface treatment effect is poor, which affects its quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass bottle capable of resisting 1300 DEG C and being not deformed during high temperature flame polishing, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0021] see figure 1 , the present invention provides a technical solution: a glass bottle that can withstand high temperature fire throwing at 1300 degrees Celsius without deformation, and the composition of the glass bottle that can withstand high temperature fire throwing at 1300 degrees Celsius without deformation includes: Al 2 o 3 , SiO 2 , BaO, Fe 2 o 3 , La 2 o 3 , MnO, Sb 2 o 3 、TiO 2 , ZnO, B 2 o 3 、As 2 o 3 , CaO, K 2 O, MgO, Na 2 O, S...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of glass bottle processing, and discloses a glass bottle capable of resisting 1300 DEG C and being not deformed during high temperature flame polishing, wherein the glass bottle comprises: Al2O3, SiO2, BaO, Fe2O3, La2O3, MnO, Sb2O3, TiO2, ZnO, B2O3, As2O3, CaO, K2O, MgO, Na2O, SrO, Y2O3 and ZrO2. According to the present invention, when the temperaturereaches about 700-800 DEG C, the surface of the glass bottle is subjected to treatment and flame polishing, such that the heat treatment effect is good due to the soft exterior and the hard interior at this time, and the condition of incapability of being processed due to easy softening of the original glass bottle can be avoided.

Description

technical field [0001] The invention relates to the technical field of glass bottle processing, in particular to a glass bottle that can withstand high temperature fire throwing at 1300 degrees Celsius without deformation and a preparation method thereof. Background technique [0002] There have been glass bottles in our country since ancient times. In the past, academic circles believed that glassware was very rare in ancient times, so only a few ruling classes could own and use them. However, recent studies have concluded that the production and manufacture of ancient glassware is not difficult, but it is not easy to preserve, so it is rare to see it in later generations. Glass bottle is a traditional beverage packaging container in our country, and glass is also a kind of packaging material with a long history. With many kinds of packaging materials pouring into the market, glass containers still occupy an important position in beverage packaging, which is inseparable fr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C6/04C03C1/00C03B25/04C03C23/00
Inventor 徐祥
Owner 浙江晶华玻璃有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com