Novel osteanagenesis promotion material and preparing method thereof

A new type of nanosheet technology, applied in the fields of biomedical materials technology and biomedical engineering, can solve the problems of limited promotion of bone regeneration, unfavorable bone formation, and reduced operability

Active Publication Date: 2019-05-17
PEKING UNION MEDICAL COLLEGE HOSPITAL CHINESE ACAD OF MEDICAL SCI +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although artificially synthesized hydroxyapatite can well simulate the inorganic structure of natural bone, the degradation time of hydroxyapatite in the body is too long, which can last for several years, which is not conducive to bone formation.
In addition, the degradation rate of tricalcium phosphate in the body is too fast to effectively promote bone regeneration in the long term
After making tricalcium phosphate and hydroxyapatite as a composite, although the biodegradation rate of the composite has been improved to a certain extent, it is difficult to control the degradation rate of the material in vivo relatively accurately by existing methods
Biomaterials such as silk protein and chitosan can promote bone regeneration to a certain extent, but the degree of promoting bone regeneration is limited, and cannot meet the speed requirements of bone repair in the body. In addition, organic materials cannot be visualized under X-rays. It makes it difficult to observe whether the material in the osteonecrosis area is fully filled and in place by X-ray after operation
Magnesium-based materials, represented by high-purity magnesium, degrade too quickly in the body, and a certain amount of hydrogen gas is generated during the degradation of magnesium metal, which causes emphysema in the local and subcutaneous implants. Although the research on magnesium alloys has been in full swing in recent years , but whether it is calcium-based materials or magnesium-based materials, few researchers have studied their performance in promoting bone regeneration in osteonecrosis areas, and none of the above materials that promote bone regeneration can promote bone quality outside the material implantation site. The effect of increased density
Although studies in recent years have shown that magnesium ions within a certain concentration range have a clear bone regeneration effect, the current research on magnesium-based materials is non-injectable, which reduces their operability to a certain extent. , which is not conducive to the vigorous promotion of this material in clinical applications in the future

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel osteanagenesis promotion material and preparing method thereof
  • Novel osteanagenesis promotion material and preparing method thereof
  • Novel osteanagenesis promotion material and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] Embodiment 1 Bone regeneration material 1 preparation

[0053] Mg(NO 3 ) 2 ·6H 2O(Sigma-Aldrich 63084-500G-F), Al(NO 3 ) 3 9H 2 O (Sigma-Aldrich 229415-100G), Yb (NO 3 ) 3 ·5H 2 O (Sigma-Aldrich209147-10G) was weighed according to the molar ratio of 1mmol:1.5mmol:0.4mmol, and dissolved in deionized water. Under the protection of nitrogen, the above three were completely dissolved by mechanical stirring to form a stable and uniform solution of 10mL. Prepare 10mL of 1mM NaOH solution, fully dissolve it for later use; prepare 3% NaNO 3 , and make 10mL mixed solution with formamide according to the ratio of 3:7. The above Mg(NO 3 ) 2 ·6H 2 O, Al(NO 3 ) 3 9H 2 O,Yb(NO 3 ) 3 ·5H 2 O solution and NaOH solution were added dropwise to NaNO 3 In the formamide mixed solution, keep the pH at 9-10, and perform mechanical stirring for 10-15 minutes in an oil bath at 80° C. to 90° C. After the reaction was completed and the solution was cooled, the solution was tak...

Embodiment 2

[0054] Example 2 Preparation of bone regeneration material 2

[0055] Mg(NO 3 ) 2 ·6H 2 O, Al(NO 3 ) 3 9H 2 O,Yb(NO 3 ) 3 ·5H 2 O was weighed according to the molar ratio of 4mmol:0.4mmol:0.5mmol, and dissolved in deionized water. Under the protection of nitrogen, the above three were completely dissolved by mechanical stirring to form a stable and uniform solution of 10mL. Prepare 10mL of 1-1.5mM NaOH solution, fully dissolve it for later use; prepare 3%-5% NaNO 3 , and make 10mL mixed solution with formamide according to the ratio of 3:7. The above Mg(NO 3 ) 2 ·6H 2 O, Al(NO 3 ) 3 9H 2 O,Yb(NO 3 ) 3 ·5H 2 O solution and NaOH solution were added dropwise to NaNO 3 In the formamide mixed solution, keep the pH at 9-10, and perform mechanical stirring for 10-15 minutes in an oil bath at 80° C. to 90° C. After the reaction was completed and the solution was cooled, the solution was taken out and centrifuged, washed three times with a mixture of deionized water...

Embodiment 3

[0056] Embodiment 3 Bone regeneration material 3 preparation

[0057] Mg(NO 3 ) 2 ·6H 2 O, Al(NO 3 ) 3 9H 2 O,Yb(NO 3 ) 3 ·5H 2 O was weighed according to the molar ratio of 2mmol:0.8mmol:0.2mmol, and dissolved in deionized water. Under the protection of nitrogen, the above three were completely dissolved by mechanical stirring to form a stable and uniform solution of 10mL. Prepare 10mL of 1-1.5mM NaOH solution, fully dissolve it for later use; prepare 3%-5% NaNO 3 , and make 10mL mixed solution with formamide according to the ratio of 3:7. The above Mg(NO 3 ) 2 ·6H 2 O, Al(NO 3 ) 3 9H 2 O,Yb(NO 3 ) 3 ·5H 2 O solution and NaOH solution were added dropwise to NaNO 3 In the formamide mixed solution, keep the pH at 9-10, and perform mechanical stirring for 10-15 minutes in an oil bath at 80° C. to 90° C. After the reaction was completed and the solution was cooled, the solution was taken out and centrifuged, washed three times with a mixture of deionized water...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel LDH nanosheet material, an AL / LDH material, a preparing method of the two materials, and application of the materials in preparing an osteanagenesis material for treating femoral head necrosis, bone defects and / or osteoporosis. The prepared LDH components are Mg-Al-Yb single-layer hydroxide, and through the mutual effect of hydrophilic groups, alendronate sodium isloaded on the surface of LDH. LDH and AL / LDH are used for accelerating osteanagenesis of an osteonecrosis area, and AL / LDH can promote the increase of the density of the bone of the necrosis area while accelerating the osteanagenesis of the implanted part of the material. Currently, a main method for clinically treating femoral head necrosis in the early period involves that core decompression iscombined with bone transplantation, and AL / LDH and LDH can be used as the bone transplantation material after core decompression; moreover, for patients with the whole body suffering from osteoporosis, AL / LDH is utilized as the material for filling the osteonecrosis area, and increase of the bone density of the whole body is promoted.

Description

technical field [0001] The invention relates to the fields of biomedical material technology and biomedical engineering, in particular to a novel material for promoting bone regeneration and a preparation method thereof. Background technique [0002] With the extension of human life and the change of travel mode, the incidence of critical bone defects (bone defects that the body cannot repair spontaneously) is increasing. The causes of critical bone defects include but are not limited to tumors, femoral head necrosis In the United States, there are as many as 600,000 patients with critical bone defects due to tumors and trauma every year. In addition, about 20,000 to 30,000 people are diagnosed with femoral head necrosis every year, and the incidence rate of non-traumatic femoral head necrosis is 1.91 / 100,000*years. If patients with femoral head necrosis do not receive effective intervention in the early stage, the femoral head will develop in sequence according to the cour...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/50A61L27/04A61L27/54A61L27/02
Inventor 梁瑞政王英杰翁习生卫敏边焱焱
Owner PEKING UNION MEDICAL COLLEGE HOSPITAL CHINESE ACAD OF MEDICAL SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com