A kind of rapid repair material for magnesium phosphate cement and preparation method thereof

A magnesium phosphate cement and repair material technology, applied in the field of cement-based quick repair materials, can solve the problems of short time from mixing magnesium phosphate cement to final setting, difficulty in meeting construction operation and process requirements, and achieve excellent retarding effect and development Small inhibitory effect and low external environmental requirements

Active Publication Date: 2021-09-28
SOUTHEAST UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The hydration mechanism of magnesium phosphate cement is essentially an acid-base neutralization reaction, and its main active phase, magnesium oxide and phosphate, reacts very violently when it meets water. When it is short, the time from mixing to final setting of magnesium phosphate cement is extremely short, which is difficult to meet the construction operation and process requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of rapid repair material for magnesium phosphate cement and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of rapid repair material, by weight parts, comprises the following components:

[0028] 25 parts of magnesium oxide, 17 parts of potassium dihydrogen phosphate, 0.63 parts of ethylenediaminetetraacetic acid dipotassium salt dihydrate, and 6.3 parts of water.

[0029] Preparation:

[0030] (1) Take magnesium oxide and potassium dihydrogen phosphate, and use a cement slurry mixer to stir at a slow speed for 1min to stir and mix it evenly to obtain a uniform powder;

[0031] (2) Dissolve ethylenediaminetetraacetic acid dipotassium salt dihydrate in water, and slowly add it to the above mixture, stir slowly for 1min, then stir rapidly for 2min and put it into a 40mm×40mm×40mm mold, to be tested After the block is hardened, it can be removed from the mold to obtain a quick repair material.

Embodiment 2

[0033] A kind of rapid repair material, by weight parts, comprises the following components:

[0034] 25 parts of magnesium oxide, 17 parts of potassium dihydrogen phosphate, 0.84 parts of ethylenediaminetetraacetic acid dipotassium salt dihydrate, and 6.3 parts of water.

[0035] Preparation:

[0036] (1) Take magnesium oxide and potassium dihydrogen phosphate, and use a cement slurry mixer to stir at a slow speed for 1min to stir and mix it evenly to obtain a uniform powder;

[0037] (2) Dissolve ethylenediaminetetraacetic acid dipotassium salt dihydrate in water, and slowly add it to the above mixture, stir slowly for 1min, then stir rapidly for 2min and put it into a 40mm×40mm×40mm mold, to be tested After the block is hardened, it can be removed from the mold to obtain a quick repair material.

Embodiment 3

[0039] A kind of rapid repair material, by weight parts, comprises the following components:

[0040] 25 parts of magnesium oxide, 17 parts of potassium dihydrogen phosphate, 1.05 parts of ethylenediaminetetraacetic acid dipotassium salt dihydrate, 6.3 parts of water.

[0041] Preparation:

[0042] (1) Take magnesium oxide and potassium dihydrogen phosphate, and use a cement slurry mixer to stir at a slow speed for 1min to stir and mix it evenly to obtain a uniform powder;

[0043] (2) Dissolve ethylenediaminetetraacetic acid dipotassium salt dihydrate in water, and slowly add it to the above mixture, stir slowly for 1min, then stir rapidly for 2min and put it into a 40mm×40mm×40mm mold, to be tested After the block is hardened, it can be removed from the mold to obtain a quick repair material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel rapid repair material for magnesium phosphate cement and a preparation method thereof. The composite material is mainly made of the following raw materials in parts by weight: 25 parts of magnesium oxide, 15-20 parts of potassium dihydrogen phosphate, Diamine tetraacetic acid dipotassium salt dihydrate 0.5-1.5 parts, water 5-10 parts. The invention uses dipotassium ethylenediaminetetraacetic acid dihydrate as a setting retarder, replacing the borax used in traditional magnesium phosphate cement. The invention has excellent retarding effect. On the one hand, the setting time of the magnesium phosphate repair system is greatly prolonged; on the other hand, the system can not only ensure the early strength of the magnesium phosphate cement sample, but also improve its later strength to a certain extent.

Description

technical field [0001] The invention relates to a rapid repair material for magnesium phosphate cement and a preparation method thereof, belonging to the technical field of cement-based rapid repair materials. Background technique [0002] Magnesium phosphate cement (MPC), as a new type of cementitious material, is widely used in rapid repair fields such as roads, bridge decks, and airstrips because of its rapid hardening, early strength, and small drying shrinkage deformation. The hydration mechanism of magnesium phosphate cement is essentially an acid-base neutralization reaction, and its main active phase, magnesium oxide and phosphate, reacts very violently when it meets water. When it is short, the time from mixing to final setting of magnesium phosphate cement is extremely short, which is difficult to meet the construction operation and process requirements. Therefore, in view of this situation, the development of a retarder suitable for the magnesium phosphate system...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/12C04B103/22
Inventor 蒋金洋张傲宁冯滔滔王凤娟
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com