Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of application method of modified collagen polypeptide leather filler

A technology of collagen polypeptide and application method, applied in application, small raw hide/big raw hide/leather/fur treatment, small raw hide/large raw hide/leather skin/fur chemical treatment, etc., can solve problems such as difficulties and increase molecular weight , The leather has good mildew resistance and the effect of reducing pollution

Active Publication Date: 2022-07-08
宏兴汽车皮革(福建)发展有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Therefore, in view of the above-mentioned problems, the present invention proposes a method for preparing a modified collagen polypeptide tanning filler from chrome-free multi-metal tanned leather shavings. The method of tannery can reduce the environmental pollution of tanning, solve the problem of difficult leather shavings processing in enterprises, and can also save resources, save tanning costs, and improve the economic benefits of enterprises; the modified collagen polypeptide tannery prepared by the method The filler has a moderate molecular weight, high hydrolysis yield, positive electricity, antibacterial and antifungal properties, and can avoid leather discoloration when used in the tanning process. It can also promote the absorption of other anionic materials in the tanning process and endow the leather with mildew resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for preparing modified collagen polypeptide leather-making filler from chrome-free multi-metal tanned leather scraps, comprising the following steps in turn:

[0021] Step (1) Hydrolysis of leather scraps: take a certain amount of leather scraps and place them in a reactor, and based on the quality of leather scraps, add 1% surfactant, 0.5% degreaser, 10 times water to soak and stir the leather scraps for 2 hours, Drain the water and wash it twice with water; add 15% oxalic acid, 7.5 times water, stir and react at 90°C for 8h, filter and dry to obtain collagen polypeptide;

[0022] Step (2) Collagen polypeptide modification: add a certain amount of collagen polypeptide into the reactor, add 3 times of water to dissolve, add 100% absolute ethanol while stirring, add 20% triethylamine, add 40% tetrahydroxymethyl quaternary phosphorus salt, adjust the pH to 7, and stir for 6 hours at 30 °C; after the reaction is completed, let it stand for 24 hours to obtain a mod...

Embodiment 2

[0024] A method for preparing modified collagen polypeptide leather-making filler from chrome-free multi-metal tanned leather scraps, comprising the following steps in turn:

[0025] Step (1) Hydrolysis of leather scraps: take a certain amount of leather scraps and place them in a reactor. Based on the quality of leather scraps, add 2% surfactant, 0.2% degreaser, and 15 times water to soak and stir the leather scraps for 5 hours. Drain the water and wash it twice with water; add 20% oxalic acid, 10 times water, stir at 80°C for 5 hours, adjust the temperature, stir at 60°C for 5 hours, filter and dry to obtain collagen peptides;

[0026] Step (2) Collagen polypeptide modification: add a certain amount of collagen polypeptide into the reactor, add 5 times water to dissolve based on the quality of collagen polypeptide; take 100% vinyl-containing quaternary ammonium salt in the container, add vinyl-containing 100% water of the mass of quaternary ammonium salt, add ammonium persul...

Embodiment 3

[0028] A method for preparing modified collagen polypeptide leather-making filler from chrome-free multi-metal tanned leather scraps, comprising the following steps in turn:

[0029] Step (1) Hydrolysis of leather scraps: take a certain amount of leather scraps and place them in the reactor, and based on the quality of leather scraps, add 0.5% surfactant, 1% degreaser, and 8 times water to soak and stir the leather scraps for 1 hour, Drain the water and wash it twice with water; add 10% oxalic acid, 15 times water, stir at 70°C for 4 hours, 50°C for 6 hours, 30°C for 8 hours, filter and dry to obtain collagen peptides;

[0030] Step (2) Modification of collagen polypeptide: add a certain amount of collagen polypeptide into the reactor, add 5 times of water to dissolve based on the quality of collagen polypeptide; take 50% of vinyl-containing quaternary ammonium salt into the container, add vinyl-containing Water containing 100% of the mass of the quaternary ammonium salt, addi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical fields of leather making chemistry and engineering, and provides a method for preparing a modified collagen polypeptide leather-making filler from chrome-free multi-metal tanned leather shavings. The method of leather filler can reduce the environmental pollution caused by tanning, solve the problem of difficulty in handling leather scraps in enterprises, and at the same time can save resources, save the cost of tanning, and improve the economic benefits of enterprises; the modified collagen polypeptide prepared by the method The tanning filler has moderate molecular weight, high hydrolysis yield, positive electricity and antibacterial and mildew resistance. It can avoid the discoloration of leather when applied in the tanning process, and can promote the absorption of other anionic materials in the tanning process. Moldy.

Description

technical field [0001] The invention relates to the technical field of leather making chemistry and engineering, in particular to an application method of a modified collagen polypeptide leather filling agent. Background technique [0002] The disposal of tannery shavings is one of the major difficulties faced by tannery enterprises. According to the traditional tanning process, nearly 30% of the raw hide quality during the tanning process will be converted into leather shavings and other leather solid wastes, including chrome-containing solid waste. Waste and chrome-free solid waste, around 600,000 leather wastes are generated worldwide each year. These leather wastes are rich in collagen, but they are not well utilized, and are mostly disposed of by incineration and landfilling, which wastes resources and pollutes the environment. The leather shavings are prepared into a leather filler, which is taken from the leather and used for the leather, and the leather filler has l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C14C3/08C14C9/02
Inventor 孙辉永梁永贤姚庆达杨义清温会涛但卫华
Owner 宏兴汽车皮革(福建)发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com