Particles and preparation method thereof

A particle and quantum dot technology, applied in the field of particles and their preparation, can solve problems such as large difference in coordination ability, limited selection of functional groups, and inability to finely adjust the degree of coordination, so as to enhance coordination ability and ensure sufficient passivation Enhance the effect of luminous performance

Inactive Publication Date: 2019-06-11
TCL CORPORATION
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the above-mentioned deficiencies in the prior art, the purpose of the present invention is to provide a particle and its preparation method, aiming to solve the problem that the existing functional groups that can coordinate with the surface of quantum dots are very limited, and the ability to coordinate with each other is limited. The difference is large, and it is impossible to fine-tune the degree of coordination

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Particles and preparation method thereof
  • Particles and preparation method thereof
  • Particles and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0109] The preparation of the present embodiment CdSe / ZnS quantum dots comprises the following steps:

[0110] 1) Add 0.8mmol cadmium oxide, 8mmol zinc acetate, 10mL oleylamine and 30mL octadecene into a 100mL three-necked flask, and exhaust at 170°C for 30 minutes to remove water and oxygen in the reaction system;

[0111] 2), after the reaction system is filled with argon, the temperature is raised to 300 degrees;

[0112] 3) Rapidly inject a mixed reaction solution of 0.2 mmol of elemental selenium, 8 mmol of elemental sulfur and 4 mL of trioctylphosphine into the reaction system, and react at 300 degrees for 10 minutes to obtain CdSe / ZnS quantum dots.

[0113] The luminescence wavelength of the obtained CdSe / ZnS quantum dots in n-hexane solvent is 525 nanometers, the peak width is 25 nanometers, and the yield of quantum dots is 53%.

Embodiment I

[0115] The preparation of InP / ZnSeS quantum dots in this embodiment comprises the following steps:

[0116] 1) Add 0.16mmol indium chloride, 1mL tetrahydrofuran, 0.5mL oleic acid and 8mL octadecene into a 50mL three-necked flask, and exhaust at 150 degrees for 30 minutes to remove water and oxygen in the reaction system;

[0117] 2), after the reaction system is filled with argon, the temperature is raised to 280 degrees;

[0118] 3) Quickly inject 0.06mmol P(TMS) into the reaction system 3 (Tri-trimethylsilylphosphorus), a mixed solution of 0.5mL octadecene, and react at 280 degrees for 20 seconds to obtain the InP quantum dot core;

[0119] 4), inject 0.04mmol Se-TOP precursor, 1.2mmol dodecyl mercaptan, 2mmol zinc oleate into the reaction system at a uniform speed within 30 minutes;

[0120] 5) After the reaction, the temperature is naturally lowered to obtain InP / ZnSeS quantum dots.

[0121] The luminescence wavelength of the obtained InP / ZnSeS quantum dots in n-hexane ...

Embodiment 3

[0123] This embodiment takes figure 1 Structural molecules are used as surface ligands, and the particles of this embodiment (the particles are composed of: CdSe / ZnS quantum dots and the CdSe / ZnS quantum dot surface combined figure 1 The preparation of structure molecule) comprises the following steps:

[0124] 1), weigh 400 mg of CdSe / ZnS quantum dots in the above-mentioned embodiment 1 and add them into 20 mL of octadecene to fully dissolve to obtain a CdSe / ZnS quantum dot solution;

[0125] 2), add 0.5mL surface ligand to the above CdSe / ZnS quantum dot solution at one time;

[0126] 3), the mixed system was heated up to 120 degrees Celsius, and reacted for 60 minutes under a nitrogen atmosphere;

[0127] 4) After cooling the reaction system to room temperature, the particles are obtained by centrifugal separation and washing.

[0128] The yield of the particles was 62%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
emission peakaaaaaaaaaa
widthaaaaaaaaaa
emission peakaaaaaaaaaa
Login to View More

Abstract

The invention discloses particles and a preparation method thereof. The particles comprise quantum dots and surface ligands combined with the surfaces of the quantum dots. A delocalized conjugated electron cloud is formed by an organic group P2 with a conjugated system, and then a delocalized conjugated electron cloud system is pushed towards a coordination group P1 by an electron-donating organicgroup P3, so that the coordination ability of coordination lone pair electrons of coordination atoms on the coordination group P1 to coordination atoms on the surfaces of the quantum dots is greatlyenhanced, the firmness of coordination bonds is enhanced, therefore, full passivation of the surfaces of the quantum dots can be ensured effectively, and the luminescence property of a quantum dot material is improved.

Description

technical field [0001] The invention relates to the technical field of quantum dots, in particular to a particle and a preparation method thereof. Background technique [0002] Quantum dots are a special material that is confined to the order of nanometers in three dimensions. This remarkable quantum confinement effect makes quantum dots have many unique nanometer properties: continuously adjustable emission wavelength, narrow emission wavelength, Broad absorption spectrum, high luminous intensity, long fluorescence lifetime and good biocompatibility, etc. These characteristics make quantum dots have broad application prospects in biomarkers, flat panel displays, solid-state lighting, photovoltaic solar energy and other fields. [0003] The size of quantum dots is usually below 20 nanometers, so the specific surface area of ​​quantum dot materials is very large, and the surface characteristics and properties of quantum dots have a significant impact on the performance of qu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K11/02C09K11/88B82Y20/00B82Y30/00B82Y40/00
Inventor 杨一行
Owner TCL CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com