Lithium ion battery, and aluminum-plastic film

A lithium-ion battery and aluminum-plastic film technology, which is applied to secondary batteries, battery pack components, circuits, etc., can solve the problems of poor airtightness of packaging, corrosion of packaging, easy scratches, etc., and achieve strong heat resistance and safety High performance and long service life

Active Publication Date: 2019-07-09
CONTEMPORARY AMPEREX TECH CO
View PDF12 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the soft aluminum-plastic film packaging also has problems such as easy scratches, poor airtightness of the package, and corrosion of the package.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium ion battery, and aluminum-plastic film
  • Lithium ion battery, and aluminum-plastic film
  • Lithium ion battery, and aluminum-plastic film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 1) Preparation of negative electrode sheet

[0027] Negative electrode active material artificial graphite, carbon black conductive agent SP, binder styrene-butadiene rubber, thickener CMC (carboxymethyl cellulose) are mixed according to weight ratio 96.2:1.5:1.5:0.8, add solvent deionized water, Stir and mix evenly under vacuum conditions to obtain the negative electrode slurry; evenly coat the negative electrode slurry on the copper foil of the negative electrode current collector, and then dry it at 80-90°C for cold pressing, trimming, cutting, and stripping , and then dried at 110° C. under vacuum for 4 hours to obtain a negative electrode sheet.

[0028] 2) Preparation of positive electrode sheet

[0029] The cathode active material LiNi 1 / 3 mn 1 / 3 co 1 / 3 o 2 (NCM333), carbon black conductive agent SP, and binder polyvinylidene fluoride are mixed according to a weight ratio of 97:2:1, and solvent N-methyl pyrrolidone is added, stirred and mixed evenly under va...

Embodiment 2

[0036] The thickness of the nylon cast film protective layer is 20 μm, the material of the first bonding layer is epoxy resin, the thickness is 2 μm, the material of the high temperature resistant layer is borosilicate carbon, the thickness is 10 μm, and the material of the second bonding layer is epoxy resin , the thickness is 3 μm, the thickness of the aluminum foil layer is 25 μm, the material of the third bonding layer is epoxy resin, the thickness is 4 μm, the thickness of the polypropylene cast film heat seal layer is 25 μm, and the total thickness of the aluminum-plastic film is 89 μm.

Embodiment 3

[0038] The thickness of the protective layer of the nylon cast film is 25 μm, the material of the first adhesive layer is acrylic resin, the thickness is 2.5 μm, the material of the high temperature resistant layer is reinforced C-C composite material, the thickness is 15 μm, the material of the second adhesive layer is acrylic resin, the thickness is The thickness of the aluminum foil layer is 2.5 μm, the thickness of the third bonding layer is acrylic resin, the thickness is 2.5 μm, the thickness of the heat-sealing layer of the polypropylene cast film is 25 μm, and the total thickness of the aluminum-plastic film is 100.5 μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a lithium ion battery, and an aluminum-plastic film. The aluminum-plastic film comprises a protective layer, a first bonding layer, a high temperature resistant layer, a secondbonding layer, an aluminium foil layer, a third bonding layer, and a heat sealing layer; the first bonding layer is arranged between the protective layer and the high temperature resistant layer; thesecond bonding layer is arranged between the high temperature resistant layer and the aluminium foil layer; the third bonding layer is arranged between the aluminium foil layer and the heat sealing layer. Compared with the prior art, the advantages of the aluminum-plastic film are that: electrolyte corrosion resistance, water resistance, oxygen insulation performance, high temperature resistance,explosion-proof performance, and high packaging adhesive force are achieved, large scale popularization and applications in the field of flexible package lithium ion battery can be realized, the obtained lithium ion batteries are excellent in heat resistance, high in safety performance, and long in service life.

Description

technical field [0001] The invention belongs to the field of lithium-ion batteries, and more specifically, the invention relates to a lithium-ion battery and an aluminum-plastic film. Background technique [0002] Lithium-ion batteries are widely used in the fields of digital products and electric vehicles. The packaging forms of lithium-ion battery outer packaging shells mainly include cylindrical, square hard shells and soft aluminum-plastic films. Compared with other packaging materials, when the heat of the battery core is out of control, the aluminum-plastic film-packed battery will be broken first, which can release the gas generated during the use of the lithium-ion battery and prevent the battery from exploding. At the same time, the aluminum-plastic film-packed soft The space utilization rate of the battery pack is high, and the energy density is high. However, soft aluminum-plastic film packaging also has problems such as easy scratches, poor airtightness of the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B9/00B32B9/04B32B27/34B32B15/20B32B7/12B32B15/085B32B27/32H01M2/02H01M10/0525H01M50/124
CPCB32B5/02B32B9/00B32B9/045B32B9/041B32B27/34B32B15/20B32B7/12B32B15/085B32B27/32H01M10/0525B32B2262/106B32B2262/10B32B2307/73B32B2307/7242B32B2307/306B32B2307/752B32B2307/584B32B2457/10H01M50/124Y02E60/10
Inventor 马云建喻鸿钢张玮郭颍歌金海族
Owner CONTEMPORARY AMPEREX TECH CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap