A kind of PVC organic compound heat stabilizer and PVC product and preparation method thereof

A composite thermal stabilizer and organic technology, applied in the field of organic composite materials, can solve problems such as poor thermal stability, and achieve the effects of alleviating the phenomenon of zinc burning, improving stability and strong operability

Active Publication Date: 2021-04-23
GUANGDONG XINDA ADVANCED MATERIALS TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved in the present invention is to overcome the defects and deficiencies of the poor long-term thermal stability of existing PVC heat stabilizers, and provide a PVC organic composite heat stabilizer, which is based on tetrahydroxyalkyl glycoluril as a stabilizer. The synergistic effect of the composite components effectively improves the thermal stability, inhibits the zinc burning phenomenon of PVC, and provides a new idea for the research and development of PVC thermal stabilizers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of PVC organic compound heat stabilizer and PVC product and preparation method thereof
  • A kind of PVC organic compound heat stabilizer and PVC product and preparation method thereof
  • A kind of PVC organic compound heat stabilizer and PVC product and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A PVC product, including 100 parts of PVC, 1 part of tetramethylol glycoluril, 1 part of 1,3-dimethyl-6-aminouracil, 0.6 parts of zinc stearate, 2.4 parts of calcium stearate, 5 parts Part Dioctyl Phthalate, 0.5 Part Stearic Acid,

[0035] The preparation method is as follows: Weigh the raw materials of each component, stir and mix evenly through a high-speed agitator at a high speed, and the mixture is mixed and plasticized into sheets on a two-roll mill. In this embodiment, each part is 1 gram. The roller temperature of the two-roll mill is 170°C, roller distance 1mm, roller speed: 45r / min, mixing time 5min.

Embodiment 2

[0037] A PVC product, including 100 parts of PVC, 5 parts of tetramethylol glycoluril, 1 part of 1,3-dimethyl-6-aminouracil, 0.6 parts of zinc stearate, 2.4 parts of calcium stearate, 5 parts Part Dioctyl Phthalate, 0.5 Part Stearic Acid,

[0038] The preparation method is as follows: Weigh the raw materials of each component, stir and mix evenly through a high-speed agitator at a high speed, and the mixture is mixed and plasticized into sheets on a two-roll mill. In this embodiment, each part is 1 gram. The roller temperature of the two-roll mill is 170°C, roller distance 1mm, roller speed: 45r / min, mixing time 5min.

Embodiment 3

[0040] A PVC product, including 100 parts of PVC, 1 part of tetramethylol glycoluril, 5 parts of 1,3-dimethyl-6-aminouracil, 0.6 parts of zinc stearate, 2.4 parts of calcium stearate, 5 parts Part Dioctyl Phthalate, 0.5 Part Stearic Acid,

[0041] The preparation method is as follows: Weigh the raw materials of each component, stir and mix evenly through a high-speed agitator at a high speed, and the mixture is mixed and plasticized into sheets on a two-roll mill. In this embodiment, each part is 1 gram. The roller temperature of the two-roll mill is 170°C, roller distance 1mm, roller speed: 45r / min, mixing time 5min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a PVC organic composite heat stabilizer, a PVC product and a preparation method thereof. 1,3-dimethyl-6-aminouracil 1-5 parts, zinc stearate 0.5-1 part, calcium stearate 2-2.5 parts. The PVC organic composite heat stabilizer of the present invention uses tetrahydroxyalkyl glycoluril as the main stabilizer, and is compounded with other synergistic components, which effectively improves the stability of the PVC heat stabilizer, alleviates the "zinc burning phenomenon" of PVC, and improves The degradation and aging of PVC; the 1,3-dimethyl-6-aminouracil in the PVC organic composite heat stabilizer has the ability to replace the unstable chlorine atoms in PVC, and cooperate with tetrahydroxyalkyl glycoluril to eliminate or reduce PVC The discoloration phenomenon; the heat stabilizer system does not contain heavy metal substances, which is in line with the concept of non-toxic and environmental protection.

Description

technical field [0001] The invention relates to the technical field of organic composite materials, more specifically, to a PVC organic composite heat stabilizer, PVC products and a preparation method thereof. Background technique [0002] Polyvinyl chloride (PVC) is one of the five general-purpose plastics. Due to its excellent comprehensive performance and low price, it has been widely used in various fields, and its consumption is second only to polyethylene. However, the poor thermal stability of polyvinyl chloride makes it necessary to add appropriate heat stabilizers during processing to inhibit the degradation of polyvinyl chloride. Generally speaking, heat stabilizers can be divided into the following categories: lead salts, metal soaps, organotin and rare earth heat stabilizers. However, the common lead salts and organotin heat stabilizers in the market are toxic to a certain extent. Under the theme of global environmental protection, it is an urgent demand in the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K5/00C08K5/3445C08K5/3462C08K5/098C08L27/06B29B7/56
CPCB29B7/56C08K5/00C08K5/098C08K5/3445C08K5/3462C08K2201/014C08L27/06
Inventor 廖正福陈庆华
Owner GUANGDONG XINDA ADVANCED MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com