Oil-proof water-proof antiskid shoe sole material and preparing method thereof
A shoe sole material and oil-repellent technology, applied in shoe soles, applications, footwear, etc., can solve the problems of decreased wear resistance, poor combination of oil resistance and wear resistance, poor dispersion of carbon black, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0023] Embodiment one: the preparation method 1 of shoe material
[0024] Step 1: Weigh the following components: 80 parts of nitrile rubber, 10 parts of butyl rubber, 10 parts of butadiene rubber, 50 parts of white carbon black, 6 parts of phenolic resin, 3 parts of terpene resin, 6 parts of zinc oxide, stearin 1.5 parts of acid, 2 parts of antioxidant 4020, 5 parts of active agent, 3 parts of accelerator CBS, 2 parts of sulfur powder, 20 parts of plasticizer aliphatic dibasic acid fat; wherein the active agent comprises the following parts by weight: zinc oxide 3-5 1-2 parts of stearic acid.
[0025] Step 2: Knead the large material prepared in step 1 until uniform; the large material includes: 80 parts of nitrile rubber, 10 parts of butyl rubber, 10 parts of butadiene rubber, and 50 parts of white carbon black.
[0026] Step 3: Wait until the temperature of the internal mixer rises to 90°C, clean up the dust and put in small materials for mixing for 30 seconds; the small m...
Embodiment 2
[0030] Embodiment two: the preparation method 2 of shoe material
[0031] Step 1: Weigh the following components: 70 parts of nitrile rubber, 20 parts of butyl rubber, 10 parts of butadiene rubber, 40 parts of white carbon black, 6 parts of phenolic resin, 4 parts of terpene resin, 6 parts of zinc oxide, stearin 1.5 parts of acid, 2 parts of anti-aging agent 4010NA, 4 parts of active agent, 3 parts of accelerator TBBS, 2 parts of sulfur powder, 10 parts of plasticizer aliphatic dibasic acid fat; wherein the active agent contains the following parts by weight: zinc oxide 3-5 1-2 parts of stearic acid.
[0032] Step 2: Knead the large material prepared in step 1 until uniform; the large material includes: 20 parts of nitrile rubber, 20 parts of butyl rubber, 10 parts of butadiene rubber, and 40 parts of white carbon black.
[0033] Step 3: When the temperature of the internal mixer rises to 90°C, clean the dust and put in small materials for mixing for 30 seconds; the small mat...
Embodiment 3
[0037] Embodiment three: the preparation method 3 of shoe material
[0038] Step 1: Weigh the following components: 50 parts of nitrile rubber, 40 parts of butyl rubber, 10 parts of butadiene rubber, 35 parts of white carbon black, 6 parts of phenolic resin, 4 parts of terpene resin, 6 parts of zinc oxide, stearin 1.5 parts of acid, 2 parts of anti-aging agent RD, 3.5 parts of active agent, 3 parts of accelerator TBBS, 2 parts of sulfur powder, 5 parts of plasticizer aliphatic dibasic acid fat; wherein the active agent contains the following parts by weight: zinc oxide 3-5 1-2 parts of stearic acid.
[0039] Step 2: Knead the large material prepared in step 1 until uniform; the large material includes: 50 parts of nitrile rubber, 40 parts of butyl rubber, 10 parts of butadiene rubber, and 35 parts of white carbon black.
[0040] Step 3: Wait until the temperature of the internal mixer rises to 90°C, clean up the dust and put in small materials for mixing for 30 seconds; the s...