Microsphere yttrium barium copper oxygen high-temperature superconductor grinding method

A technology of yttrium barium copper oxide and superconductors, which is applied in the direction of spherical grinders, grinding workpiece supports, grinding drive devices, etc., can solve the problems of processing difficult micro superconducting materials into spherical structures, so as to expand commercial use and value, reduce Difficulties in processing, effects of expanded scope of application and commercial use

Inactive Publication Date: 2019-08-13
DALIAN UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In bulk superconducting materials, due to the unique advantages and applications of spherical superconducting materials compared with other polyhedral structures, it is difficult to process micro superconducting materials into spherical structures by using common mechanical processing methods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microsphere yttrium barium copper oxygen high-temperature superconductor grinding method
  • Microsphere yttrium barium copper oxygen high-temperature superconductor grinding method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The specific implementation manners of the present invention will be described in detail below in conjunction with the accompanying drawings and technical solutions.

[0017] The side length of the hexahedral yttrium barium copper oxide superconductor is about 2.0 mm. Put it into deionized water and ultrasonically clean it for 5 minutes to remove impurities and dust on its surface.

[0018] Select two cylinders with a diameter of 30mm and a length of 150mm as the fixture for this experiment, and engrave a groove on the cylinder with a length of 1.5mm, a width of 2.1mm, and a height of 1.8mm, and glue the sample to the groove with glue; The other is engraved with a semi-cylindrical hole with a diameter of 2.1mm and a depth of 2mm, and the fixture is installed on a 200D PCD&PCBN tool grinder.

[0019] Set the spindle speed of the grinding wheel. The spindle speed of the grinding wheel is 3000r / min.

[0020] Set the angle between the table and the grinding wheel spindle ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
radiusaaaaaaaaaa
Login to View More

Abstract

The invention provides a microsphere yttrium barium copper oxygen high-temperature superconductor grinding method, and belongs to the technical field of micro-machining. A grinding machine is adoptedto grind cubic yttrium barium copper oxygen superconductors to machine out sphere yttrium barium copper oxygen superconductors. Micro yttrium barium copper oxygen samples are fixed in a cylindrical fixture; and the fixture is fixed on a horizontal worktable. An included angle between the worktable and a grinding wheel main shaft is adjusted within 5-10%. The rotating speed of the grinding wheel main shaft is set within 2500-3500 r / min. The feeding quantity of the worktable in the horizontal direction is set within 0.2-0.5 mm / min. Then, the rotating speed of the worktable is adjusted within 200-300 t / min. The samples rotationally move along an X axle. The radius of the samples is about 0.9 mm after machining. The invention realizes a new microsphere yttrium barium copper oxygen superconductor machining method.

Description

technical field [0001] The invention belongs to the field of micro-machining of superconductor materials, and relates to a grinding method for processing a micro-sized regular polyhedron into a micro-sphere yttrium-barium-copper-oxygen superconductor. Background technique [0002] Superconducting technology is a new technology field with wide application and great potential. It has a profound impact on the national economy, national defense and military, medical and health care and various high-tech industries. In recent years, with the development of superconducting technology, especially the continuous development of high-temperature superconducting technology, people have continuously explored high-temperature superconducting materials of different materials and developed various superconducting devices. The most ideal application of superconductors is as cable materials in urban commercial power systems. In addition, it can also be used for connecting wires and ultra-mi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B24B11/02B24B41/06B24B47/12
CPCB24B11/02B24B41/06B24B47/12
Inventor 张振宇刘冬冬崔俊峰陈雷雷
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com