Cutting steel wire, steel material for cutting steel wire and production method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for cutting steel wire and production method, applied in the field of steel for cutting steel wire and cutting steel wire, can solve the problems of large inclusion size, high number density of inclusions, low tensile strength and the like
Active Publication Date: 2020-05-22
INST OF RES OF IRON & STEEL JIANGSU PROVINCE +2
View PDF6 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In view of the fact that the steel for cutting steel wire prepared by the current production process in this technical field has problems such as large inclusion size, high number density of inclusions, and low tensile strength, the performance of the existing cutting steel wire cannot meet market demand.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0068] In this embodiment, five test examples with serial numbers A, B, C, D, and E are illustrated, and the specific details of this embodiment will be introduced below.
[0069] (1) Pretreatment
[0070] Take blast furnace molten iron for desulfurization in KR desulfurization device. The temperature, weight, Si content, S content of blast furnace molten iron and the S content in molten iron after desulfurization are shown in Table 1.
[0071] [Table 1]
[0072]
[0073] (2) Electric furnace blowing
[0074] Add steel scrap and pretreated molten iron into a 100t electric furnace, and mix the two into molten steel with a total weight of 110±2t; add the first batch of slagging agent to the molten steel and then perform desiliconization and dephosphorization; The second batch of slagging agent is added to the molten steel after silicon and dephosphorization; after that, the molten steel is subjected to oxygen blowing decarburization, and during the oxygen blowing decarburiz...
Embodiment 2
[0100] In this embodiment, five test examples with serial numbers H, I, J, K, and L are illustrated, and the specific details of this embodiment will be introduced below.
[0101] (1) Pretreatment
[0102] Take blast furnace molten iron for desulfurization in KR desulfurization device. The temperature, weight, Si content, S content of blast furnace molten iron and the S content in molten iron after desulfurization are shown in Table 8.
[0103] [Table 8]
[0104]
[0105] (2) Converter blowing
[0106] Add steel scrap and pretreated molten iron into a 120t converter, and mix the two into molten steel with a total weight of 130±2t; add the first batch of slagging agent to the molten steel and then perform desiliconization and dephosphorization; The second batch of slagging agent is added to the molten steel after silicon and dephosphorization; after that, the molten steel is subjected to oxygen blowing decarburization, and during the oxygen blowing decarburization process ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
diameter
aaaaa
aaaaa
diameter
aaaaa
aaaaa
diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a sawing wire, steel for the sawing wire, and a production method thereof. The production method comprises the steps of desulfurizing molten iron till S in the molten iron is no more than 0.002%; mixing the desulfurized molten iron and steel scrap into molten steel, and desiliconizing and dephosphorizing the molten steel at 1330 DEG C-1380 DEG C; then, decarburizing the molten steel by blowing oxygen, and obtaining the molten steel comprising no less than 0.3% of C, no more than 0.01% of P and no more than 0.01% of S, wherein the temperature of the molten steel is no lower than 1650 DEG C; adding desoxidants and slagging media to the molten steel for deoxidation alloying; then, refining the molten steel for regulating chemical components and inclusions, wherein thecomponents of the inclusions comprise no more than 10% of Al2O3 and no more than 30% of CaO; degassing the refined molten steel and removing the inclusions to obtain the molten steel, wherein the sizeof the inclusions of the molten steel is no more than 10 [mu]m, and the number density of the inclusions is no more than 0.5 g / m<3>; and casting the molten steel into steel billets. The steel, prepared with the production method, for the sawing wire can be used as base metal for producing the sawing wire with the diameter of no more than 100 <mu>m and the tensile strength of no lower than 4600 MPa; and the length of the continuous wire in the process of manufacturing the sawing wire is no less than 200 km.
Description
technical field [0001] The invention belongs to the technical field of iron and steel smelting, and relates to a production method of steel for cutting steel wire, and also relates to a steel for cutting steel wire prepared by the production method, and a cutting steel wire further processed from the steel for cutting steel wire . Background technique [0002] Cutting wire, also known as cutting wire, cutting steel wire, and cutting wire, is a special wire used for cutting, and it is also a special steel wire with a diameter of less than 0.20mm and a galvanized copper surface. It is widely used as a consumable material In the fields of energy, aviation, equipment and public facilities, such as cutting and forming of solar silicon wafers, quartz materials, monocrystalline silicon, and polycrystalline silicon. It is even possible to inlay tiny diamond particles on the cutting wire to make a diamond cutting wire, or diamond wire, diamond cutting wire, or diamond wire. [0003...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more