Automatic overheating process

An overheating and automatic technology, applied in the direction of instruments, manufacturing computing systems, data processing applications, etc., can solve problems such as waste of working hours, achieve the effects of avoiding abnormal accidents, shortening working hours for temperature stabilization, and improving competitiveness

Active Publication Date: 2019-10-22
内蒙古中环晶体材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the above problems, the problem to be solved by the present invention is to provide an automatic overheating process, which can automatically detect the phenomenon of diameter shrinkage when the seed crystal is overheated when it is applied in the temperature stabilization process. The degree of automation is high, and the working hours caused by insufficient manual experience Waste and Occurrence of Unusual Accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The present invention will be further described below in conjunction with specific examples.

[0026] The invention relates to an automatic overheating process, which is applied in the automatic temperature stabilization process of Czochralski single crystal. In the automatic temperature stabilization process, the automatic overheating process is adopted, and the artificial overheating operation can be simulated automatically, which can not only manually determine the overheating of the seed crystal The operation steps are automatic overheating operation, and the phenomenon of diameter shrinkage when the seed crystal is overheated can be automatically detected. Through automatic overheating parameters, automation is carried out. Compared with manual operation, it is more accurate, scientific and unified, and avoids problems caused by insufficient manual experience. The waste of working hours and the occurrence of abnormal accidents.

[0027] In the Czochralski single cr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an automatic overheating process, which is used for carrying out overheating welding within overheating welding time after seed crystal is automatically reduced in a temperaturestabilizing process, and comprises the following steps of: S1, measuring the diameter of the seed crystal, carrying out timing, and recording the maximum value of the diameter of the seed crystal inthe timing process; S2, carrying out automatic temperature adjustment according to the liquid level temperature of the silicon solution, and adjusting the liquid level temperature of the silicon solution to the welding temperature; S3, carrying out overheating welding and timing, and recording the minimum value of the seed crystal diameter in the timing process; and S4, calculating an overheatingdiameter reduction difference value of the seed crystal, and judging whether overheating is completed or not according to the overheating diameter reduction difference value. The method has the beneficial effects that automatic overheating is carried out according to the operation steps of manually judging overheating of the seed crystals, the phenomenon of diameter shrinkage during overheating ofthe seed crystals is automatically detected, labor hour waste and abnormal accidents caused by insufficient artificial experience are avoided, the temperature stabilizing labor hour is shortened, theyield is increased, and the competitiveness of enterprises is improved.

Description

technical field [0001] The invention belongs to the technical field of Czochralski single crystal, and in particular relates to an automatic overheating process. Background technique [0002] At present, the competition in the industry is becoming increasingly fierce, and cost reduction and efficiency increase have become a magic weapon for an enterprise to survive. At present, in the production process of solar photovoltaic material manufacturing, except for the equal-diameter process state (automatic has been realized), the operation is the most difficult and takes the longest time. The state of the art process is temperature stabilization. At present, the manual temperature stabilization method is generally used in the industry. The manual temperature stabilization method is very dependent on operating experience, and requires the continuous attention of the operator, which takes up a lot of manual energy and practice. [0003] The current industry average of manual temp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G06Q10/06G06Q50/04
CPCG06Q10/0633G06Q50/04Y02P90/30
Inventor 王鑫皇甫亚楠杨瑞峰周泽王建平王林徐强高润飞谷守伟
Owner 内蒙古中环晶体材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products